Water-based transmutation artistic digital glaze as well as preparation method and application thereof
The invention discloses a water-based transmutation art digital glaze, which comprises an auxiliary agent, a conditioning agent and a basic glaze, and is characterized in that the basic glaze comprises the following components in parts by mass: 40 to 50 parts of high-boron frit, 25 to 35 parts of albite, 15 to 25 parts of wollastonite, 4.5 to 5.5 parts of silicon carbide and 0.3 to 0.7 part of copper oxide; wherein the high-boron frit comprises the following components in parts by mass: 31-35 parts of boron oxide, 6-10 parts of sodium oxide, 4-8 parts of aluminum oxide, 40-44 parts of silicon oxide, 7-11 parts of calcium oxide and 1.5-2.5 parts of strontium oxide. A glaze surface prepared from the digital glaze has a natural aesthetic effect and can be applied to ceramic large plates.
本发明公开了一种水性窑变艺术数码釉料，该数码釉料包括助剂、调节剂以及基础釉料，其特征在于，所述基础釉料包括以下按质量份计各组分：高硼熔块40～50份，钠长石25～35份，硅灰石15～25份，碳化硅4.5～5.5份，氧化铜0.3～0.7份；其中，所述高硼熔块包括以下按质量份计各组分：氧化硼31～35份，氧化钠6～10份，氧化铝4～8份，氧化硅40～44份，氧化钙7～11份，氧化锶1.5～2.5份。由上述数码釉料制备得到的釉面，具有自然美学效果，可应用于陶瓷大板。
Water-based transmutation artistic digital glaze as well as preparation method and application thereof
The invention discloses a water-based transmutation art digital glaze, which comprises an auxiliary agent, a conditioning agent and a basic glaze, and is characterized in that the basic glaze comprises the following components in parts by mass: 40 to 50 parts of high-boron frit, 25 to 35 parts of albite, 15 to 25 parts of wollastonite, 4.5 to 5.5 parts of silicon carbide and 0.3 to 0.7 part of copper oxide; wherein the high-boron frit comprises the following components in parts by mass: 31-35 parts of boron oxide, 6-10 parts of sodium oxide, 4-8 parts of aluminum oxide, 40-44 parts of silicon oxide, 7-11 parts of calcium oxide and 1.5-2.5 parts of strontium oxide. A glaze surface prepared from the digital glaze has a natural aesthetic effect and can be applied to ceramic large plates.
本发明公开了一种水性窑变艺术数码釉料，该数码釉料包括助剂、调节剂以及基础釉料，其特征在于，所述基础釉料包括以下按质量份计各组分：高硼熔块40～50份，钠长石25～35份，硅灰石15～25份，碳化硅4.5～5.5份，氧化铜0.3～0.7份；其中，所述高硼熔块包括以下按质量份计各组分：氧化硼31～35份，氧化钠6～10份，氧化铝4～8份，氧化硅40～44份，氧化钙7～11份，氧化锶1.5～2.5份。由上述数码釉料制备得到的釉面，具有自然美学效果，可应用于陶瓷大板。
Water-based transmutation artistic digital glaze as well as preparation method and application thereof
一种水性窑变艺术数码釉料及其制备方法与应用
LUO JINYUAN (Autor:in) / LI XINGBING (Autor:in)
01.08.2023
Patent
Elektronische Ressource
Chinesisch
Transmutation glaze, transmutation glaze laterite ceramic product and preparation method thereof
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2024
Glaze slip for preparing transmutation glaze and preparation method of transmutation glaze
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2022