Light-transmitting concrete and preparation method thereof
The invention relates to light-transmitting concrete and a preparation method thereof, and relates to the technical field of light-transmitting concrete.The light-transmitting concrete is prepared from, by weight, 90-110 parts of white cement, 200-280 parts of quartz sand, 45-60 parts of water, 1-3 parts of polycarboxylate superplasticizer, 0.5-1.5 parts of defoaming agent, 0.5-1.5 parts of stabilizer, 7-9 parts of redispersible rubber powder, 0.7-1.6 parts of carbon fiber and 6-15 parts of epoxy resin. The light-transmitting concrete further comprises a light-transmitting material, and the light-transmitting material is selected from at least one of light-guide fibers and acrylic rods. According to the prepared light-transmitting concrete, on the basis of high light transmittance, the strength is further improved, the light-transmitting concrete is not prone to cracking, the water seepage prevention effect is better, after the epoxy resin is used for sealing the surface of the light-transmitting concrete, the surface energy of the light-transmitting concrete is effectively improved, and the surface of the light-transmitting concrete is smooth, flat, more resistant to dirt, not prone to pollution and convenient to clean.
本申请涉及一种透光混凝土及其制备方法，涉及透光混凝土技术领域，透光混凝土由以下重量份的原料组成：90‑110份白水泥、200‑280份石英砂、45‑60份水、1‑3份聚羧酸减水剂、0.5‑1.5份消泡剂、0.5‑1.5份稳定剂、7‑9份可再分散性胶粉、0.7‑1.6份碳纤维和6‑15份环氧树脂；透光混凝土中还包括透光材料，透光材料选自光导纤维和亚克力棒中的至少一种。本申请制备的透光混凝土，在具备高透光性的基础上，强度进一步得到提高且不容易开裂，防渗水效果更佳，再利用环氧树脂对透光混凝土的表面进行封层后，有效提高透光混凝土的表面能，使其表面光滑平整，更耐脏，不容易受污染，便于清洁。
Light-transmitting concrete and preparation method thereof
The invention relates to light-transmitting concrete and a preparation method thereof, and relates to the technical field of light-transmitting concrete.The light-transmitting concrete is prepared from, by weight, 90-110 parts of white cement, 200-280 parts of quartz sand, 45-60 parts of water, 1-3 parts of polycarboxylate superplasticizer, 0.5-1.5 parts of defoaming agent, 0.5-1.5 parts of stabilizer, 7-9 parts of redispersible rubber powder, 0.7-1.6 parts of carbon fiber and 6-15 parts of epoxy resin. The light-transmitting concrete further comprises a light-transmitting material, and the light-transmitting material is selected from at least one of light-guide fibers and acrylic rods. According to the prepared light-transmitting concrete, on the basis of high light transmittance, the strength is further improved, the light-transmitting concrete is not prone to cracking, the water seepage prevention effect is better, after the epoxy resin is used for sealing the surface of the light-transmitting concrete, the surface energy of the light-transmitting concrete is effectively improved, and the surface of the light-transmitting concrete is smooth, flat, more resistant to dirt, not prone to pollution and convenient to clean.
本申请涉及一种透光混凝土及其制备方法，涉及透光混凝土技术领域，透光混凝土由以下重量份的原料组成：90‑110份白水泥、200‑280份石英砂、45‑60份水、1‑3份聚羧酸减水剂、0.5‑1.5份消泡剂、0.5‑1.5份稳定剂、7‑9份可再分散性胶粉、0.7‑1.6份碳纤维和6‑15份环氧树脂；透光混凝土中还包括透光材料，透光材料选自光导纤维和亚克力棒中的至少一种。本申请制备的透光混凝土，在具备高透光性的基础上，强度进一步得到提高且不容易开裂，防渗水效果更佳，再利用环氧树脂对透光混凝土的表面进行封层后，有效提高透光混凝土的表面能，使其表面光滑平整，更耐脏，不容易受污染，便于清洁。
Light-transmitting concrete and preparation method thereof
一种透光混凝土及其制备方法
QIN LING (Autor:in) / WANG HAIJIANG (Autor:in) / DING JIXIANG (Autor:in)
12.01.2024
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Light-transmitting concrete and preparation method thereof
| Europäisches Patentamt | 2023
Light-transmitting concrete aggregate and preparation method thereof
| Europäisches Patentamt | 2023
Light-transmitting concrete and preparation process thereof
| Europäisches Patentamt | 2023
High-strength light-transmitting concrete and preparation method thereof
| Europäisches Patentamt | 2021
3D printing light-transmitting concrete structure and preparation method thereof
| Europäisches Patentamt | 2023