Electroplating effect glaze
The invention is applicable to the technical field of metal glaze, and provides electroplating effect glaze which is prepared by the following steps: the electroplating effect glaze consists of ground glaze and cover glaze; the ground glaze comprises lead frit, calcite, manganese carbonate, strontium carbonate, copper oxide, zinc oxide, quartz and lithium carbonate; the cover glaze comprises boron frit, lithium carbonate, quartz, ferric oxide, zinc oxide, vanadium pentoxide, copper oxide, sodium pyrophosphate, titanium dioxide, chromic oxide, nickel protoxide, cobalt oxide, strontium carbonate, calcite and manganese dioxide. Preferably, the ground glaze is prepared from the following components in parts by mass: 25 to 35 parts of lead frit, 15 to 25 parts of calcite, 2 to 3 parts of manganese carbonate, 3 to 6 parts of strontium carbonate, 6 to 10 parts of copper oxide, 10 to 20 parts of zinc oxide, 13 to 16 parts of quartz and 3 to 6 parts of lithium carbonate. The surface layer of the glaze can present a metal electroplating effect, the texture hand feeling with obvious wrinkles can be obtained by adjusting the bottom glaze, the quality and stability of the obtained metal glaze are high, and the metal glaze can be produced at low temperature in batches in a roller kiln.
本发明适用于金属釉技术领域，提供了一种电镀效果釉，包括以下步骤：所述电镀效果釉由底釉和面釉组成；所述底釉包括铅熔块、方解石、碳酸锰、碳酸锶、氧化铜、氧化锌、石英和碳酸锂；所述面釉包括硼熔块、碳酸锂、石英、三氧化二铁、氧化锌、五氧化二钒、氧化铜、焦磷酸钠、二氧化钛、氧化铬、氧化亚镍、氧化钴、碳酸锶、方解石和二氧化锰。优选的，以质量份数计，所述底釉各组分的含量如下：铅熔块25～35份、方解石15～25份、碳酸锰2～3份、碳酸锶3～6份、氧化铜6～10份、氧化锌10～20份、石英13～16份和碳酸锂3～6份。本发明釉面表层能呈现金属电镀效果，而且通过底面釉调整可以得到褶皱明显的肌理手感，所得金属釉的质量和稳定性高，可批量在辊道窑炉中低温量产。
Electroplating effect glaze
The invention is applicable to the technical field of metal glaze, and provides electroplating effect glaze which is prepared by the following steps: the electroplating effect glaze consists of ground glaze and cover glaze; the ground glaze comprises lead frit, calcite, manganese carbonate, strontium carbonate, copper oxide, zinc oxide, quartz and lithium carbonate; the cover glaze comprises boron frit, lithium carbonate, quartz, ferric oxide, zinc oxide, vanadium pentoxide, copper oxide, sodium pyrophosphate, titanium dioxide, chromic oxide, nickel protoxide, cobalt oxide, strontium carbonate, calcite and manganese dioxide. Preferably, the ground glaze is prepared from the following components in parts by mass: 25 to 35 parts of lead frit, 15 to 25 parts of calcite, 2 to 3 parts of manganese carbonate, 3 to 6 parts of strontium carbonate, 6 to 10 parts of copper oxide, 10 to 20 parts of zinc oxide, 13 to 16 parts of quartz and 3 to 6 parts of lithium carbonate. The surface layer of the glaze can present a metal electroplating effect, the texture hand feeling with obvious wrinkles can be obtained by adjusting the bottom glaze, the quality and stability of the obtained metal glaze are high, and the metal glaze can be produced at low temperature in batches in a roller kiln.
本发明适用于金属釉技术领域，提供了一种电镀效果釉，包括以下步骤：所述电镀效果釉由底釉和面釉组成；所述底釉包括铅熔块、方解石、碳酸锰、碳酸锶、氧化铜、氧化锌、石英和碳酸锂；所述面釉包括硼熔块、碳酸锂、石英、三氧化二铁、氧化锌、五氧化二钒、氧化铜、焦磷酸钠、二氧化钛、氧化铬、氧化亚镍、氧化钴、碳酸锶、方解石和二氧化锰。优选的，以质量份数计，所述底釉各组分的含量如下：铅熔块25～35份、方解石15～25份、碳酸锰2～3份、碳酸锶3～6份、氧化铜6～10份、氧化锌10～20份、石英13～16份和碳酸锂3～6份。本发明釉面表层能呈现金属电镀效果，而且通过底面釉调整可以得到褶皱明显的肌理手感，所得金属釉的质量和稳定性高，可批量在辊道窑炉中低温量产。
Electroplating effect glaze
一种电镀效果釉
CHEN JINLONG (Autor:in) / CHEN DIQING (Autor:in) / CHEN DIXI (Autor:in) / WU ZHIQUAN (Autor:in)