Ion-erosion-resistant self-repairing marine concrete and preparation method thereof
The invention discloses an anti-ion erosion self-repairing marine concrete and a preparation method thereof, the concrete comprises the following components in parts by weight: 100 parts of cement, 120-280 parts of fine aggregate, 220-350 parts of coarse aggregate, 30-40 parts of water, 2-4 parts of ZnAl-NO3 layered double hydroxide, 0.5-1 part of disodium fumarate, 0-10 parts of metakaolin, and 0.5-1 part of a water reducing agent. By using the ZnAl-NO3 layered double hydroxide, corrosive anions such as Cl <-> and SO4 < 2-> entering concrete can be effectively adsorbed, further damage of the ions to the concrete is prevented, on the other hand, the concrete crack self-repairing capability can be endowed by using the disodium fumarate, the corrosive cations such as Mg < 2 + > are converted into precipitates to repair the cracks, and the concrete crack self-repairing effect is improved. And a dual defense effect on corrosive ions is achieved.
本发明公开了一种抗离子侵蚀自修复海工混凝土及其制备方法，按照重量份数计算，所述混凝土包括如下组分：水泥为100份，细骨料为120～280份，粗骨料为220～350份，水为30～40份，ZnAl‑NO3层状双氢氧化物为2～4份，富马酸二钠盐为0.5～1份，偏高岭土为0～10份，减水剂为0.5～1份。本发明中ZnAl‑NO3层状双氢氧化物的使用可有效吸附进入混凝土中的侵蚀性阴离子如Cl‑和SO42‑等，防止这些离子对混凝土的进一步破坏，另一方面使用富马酸二钠盐可赋予混凝土裂缝自修复能力，通过将侵蚀性阳离子如Mg2+转化为沉淀修复裂缝，达到对侵蚀性离子的双重防御作用。
Ion-erosion-resistant self-repairing marine concrete and preparation method thereof
The invention discloses an anti-ion erosion self-repairing marine concrete and a preparation method thereof, the concrete comprises the following components in parts by weight: 100 parts of cement, 120-280 parts of fine aggregate, 220-350 parts of coarse aggregate, 30-40 parts of water, 2-4 parts of ZnAl-NO3 layered double hydroxide, 0.5-1 part of disodium fumarate, 0-10 parts of metakaolin, and 0.5-1 part of a water reducing agent. By using the ZnAl-NO3 layered double hydroxide, corrosive anions such as Cl <-> and SO4 < 2-> entering concrete can be effectively adsorbed, further damage of the ions to the concrete is prevented, on the other hand, the concrete crack self-repairing capability can be endowed by using the disodium fumarate, the corrosive cations such as Mg < 2 + > are converted into precipitates to repair the cracks, and the concrete crack self-repairing effect is improved. And a dual defense effect on corrosive ions is achieved.
本发明公开了一种抗离子侵蚀自修复海工混凝土及其制备方法，按照重量份数计算，所述混凝土包括如下组分：水泥为100份，细骨料为120～280份，粗骨料为220～350份，水为30～40份，ZnAl‑NO3层状双氢氧化物为2～4份，富马酸二钠盐为0.5～1份，偏高岭土为0～10份，减水剂为0.5～1份。本发明中ZnAl‑NO3层状双氢氧化物的使用可有效吸附进入混凝土中的侵蚀性阴离子如Cl‑和SO42‑等，防止这些离子对混凝土的进一步破坏，另一方面使用富马酸二钠盐可赋予混凝土裂缝自修复能力，通过将侵蚀性阳离子如Mg2+转化为沉淀修复裂缝，达到对侵蚀性离子的双重防御作用。
Ion-erosion-resistant self-repairing marine concrete and preparation method thereof
一种抗离子侵蚀自修复海工混凝土及其制备方法
WANG RUIYANG (Autor:in) / CHEN HUAXIN (Autor:in) / KUANG DONGLIANG (Autor:in) / YU JINCHENG (Autor:in) / WU YONGCHANG (Autor:in) / MA XIAOYAN (Autor:in)
23.07.2024
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
High-strength heat-resistant self-repairing concrete and preparation method thereof
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2021
Self-repairing concrete and preparation method thereof
| Europäisches Patentamt | 2024
Seawater-resistant concrete repairing material and preparation method thereof
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2022