The invention provides temmoku green glaze and a preparation method thereof, and relates to the technical field of temmoku glaze preparation. The glaze slip of the temmoku glaze comprises an inorganic raw material and an auxiliary agent; the inorganic raw materials comprise the following components in parts by mass: 10 parts of frit, 10 to 18 parts of SiO2, 7 to 14 parts of P2O5, 5 to 9 parts of Li2O, 8 to 13 parts of Al2O3, 3 to 5 parts of TiO2, 2 to 4 parts of hematite and 1 to 3 parts of magnetite; the auxiliary agent is prepared from the following components in parts by mass: 10 parts of polyacrylamide, 10 to 15 parts of sodium tripolyphosphate, 5 to 9 parts of sodium carboxymethyl cellulose and 2 to 5 parts of phenylmethyldiethoxysilane. The method for preparing the temmoku green glaze comprises the following steps: S1, preparing glaze slip; S2, spraying the glaze; and S3, firing in a reducing atmosphere. The temmoku green glaze prepared by the invention is cyan blue or turquoise green, and is beautiful and elegant in appearance.
本发明提供一种天目青釉及其制备方法，涉及天目釉制备技术领域。天目釉的釉浆包括无机原料和助剂；按质量份计，所述无机原料包括10份熔块、10～18份SiO2、7～14份P2O5、5～9份Li2O、8～13份Al2O3、3～5份TiO2、2～4份赤铁矿、1～3份磁铁矿；按质量份计，所述助剂包括10份聚丙烯酰胺、10～15份三聚磷酸钠、5～9份羧甲基纤维素钠和2～5份苯基甲基二乙氧基硅烷。制备天目青釉的方法包括以下步骤：S1.制备釉浆，S2.喷釉，S3.在还原气氛中烧制。本发明制备的天目青釉呈现青蓝色或青绿色，表观美而大气。
Tangku green glaze and preparation method thereof
The invention provides temmoku green glaze and a preparation method thereof, and relates to the technical field of temmoku glaze preparation. The glaze slip of the temmoku glaze comprises an inorganic raw material and an auxiliary agent; the inorganic raw materials comprise the following components in parts by mass: 10 parts of frit, 10 to 18 parts of SiO2, 7 to 14 parts of P2O5, 5 to 9 parts of Li2O, 8 to 13 parts of Al2O3, 3 to 5 parts of TiO2, 2 to 4 parts of hematite and 1 to 3 parts of magnetite; the auxiliary agent is prepared from the following components in parts by mass: 10 parts of polyacrylamide, 10 to 15 parts of sodium tripolyphosphate, 5 to 9 parts of sodium carboxymethyl cellulose and 2 to 5 parts of phenylmethyldiethoxysilane. The method for preparing the temmoku green glaze comprises the following steps: S1, preparing glaze slip; S2, spraying the glaze; and S3, firing in a reducing atmosphere. The temmoku green glaze prepared by the invention is cyan blue or turquoise green, and is beautiful and elegant in appearance.
本发明提供一种天目青釉及其制备方法，涉及天目釉制备技术领域。天目釉的釉浆包括无机原料和助剂；按质量份计，所述无机原料包括10份熔块、10～18份SiO2、7～14份P2O5、5～9份Li2O、8～13份Al2O3、3～5份TiO2、2～4份赤铁矿、1～3份磁铁矿；按质量份计，所述助剂包括10份聚丙烯酰胺、10～15份三聚磷酸钠、5～9份羧甲基纤维素钠和2～5份苯基甲基二乙氧基硅烷。制备天目青釉的方法包括以下步骤：S1.制备釉浆，S2.喷釉，S3.在还原气氛中烧制。本发明制备的天目青釉呈现青蓝色或青绿色，表观美而大气。
Tangku green glaze and preparation method thereof
一种天目青釉及其制备方法
PAN JUNYUN (Autor:in) / DENG JINGHUA (Autor:in)
01.11.2024
Patent
Elektronische Ressource
Chinesisch
Green background crystal glaze and preparation method thereof
| Europäisches Patentamt | 2020
Pea-green glaze porcelain and preparation method thereof
| Europäisches Patentamt | 2024
Smoke rain green glaze and preparation method thereof
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2021