High-gloss opaque glaze for sanitary ware ceramic as well as preparation method and application of high-gloss opaque glaze
The invention discloses high-gloss opaque glaze for sanitary ware ceramic as well as a preparation method and application of the high-gloss opaque glaze. The glaze slip is prepared from the following raw materials in parts by mass: 25 to 32 parts of quartz, 10 to 23 parts of potassium feldspar, 8 to 15 parts of calcite, 0 to 4 parts of dolomite, 1 to 6 parts of aluminum oxide, 2 to 5 parts of kaolin, 8 to 10 parts of zirconium silicate, 6 to 8 parts of wollastonite, 5 to 18 parts of albite and 5 to 23 parts of barium frit. According to the preparation method disclosed by the invention, the formula is introduced in the form of the barium frit, and the barium frit is combined with the albite, so that the problems that the fluxing effect of barium is relatively insufficient, the vitrification of the glaze surface is insufficient, and the glaze surface gloss improvement effect is insufficient can be solved.
本发明公开了一种卫生洁具陶瓷高光泽乳浊釉及其制备方法和应用。釉浆原料按质量份组成包括：石英25‑32份、钾长石10‑23份、方解石8‑15份、白云石0‑4份、氧化铝1‑6份、高岭土2‑5份、硅酸锆8‑10份、硅灰石6‑8份、钠长石5‑18份、钡熔块5‑23份。本发明制备方法中采用钡熔块的形式引入配方，通过与钠长石的组合，能够克服钡自身助熔效果相对不足、釉面玻化不充分、釉面光泽提升作用发挥不足的问题。
High-gloss opaque glaze for sanitary ware ceramic as well as preparation method and application of high-gloss opaque glaze
The invention discloses high-gloss opaque glaze for sanitary ware ceramic as well as a preparation method and application of the high-gloss opaque glaze. The glaze slip is prepared from the following raw materials in parts by mass: 25 to 32 parts of quartz, 10 to 23 parts of potassium feldspar, 8 to 15 parts of calcite, 0 to 4 parts of dolomite, 1 to 6 parts of aluminum oxide, 2 to 5 parts of kaolin, 8 to 10 parts of zirconium silicate, 6 to 8 parts of wollastonite, 5 to 18 parts of albite and 5 to 23 parts of barium frit. According to the preparation method disclosed by the invention, the formula is introduced in the form of the barium frit, and the barium frit is combined with the albite, so that the problems that the fluxing effect of barium is relatively insufficient, the vitrification of the glaze surface is insufficient, and the glaze surface gloss improvement effect is insufficient can be solved.
本发明公开了一种卫生洁具陶瓷高光泽乳浊釉及其制备方法和应用。釉浆原料按质量份组成包括：石英25‑32份、钾长石10‑23份、方解石8‑15份、白云石0‑4份、氧化铝1‑6份、高岭土2‑5份、硅酸锆8‑10份、硅灰石6‑8份、钠长石5‑18份、钡熔块5‑23份。本发明制备方法中采用钡熔块的形式引入配方，通过与钠长石的组合，能够克服钡自身助熔效果相对不足、釉面玻化不充分、釉面光泽提升作用发挥不足的问题。
High-gloss opaque glaze for sanitary ware ceramic as well as preparation method and application of high-gloss opaque glaze
一种卫生洁具陶瓷高光泽乳浊釉及其制备方法和应用
LIN XIAOFA (Autor:in) / LIN XIAOSHAN (Autor:in) / YIN PING (Autor:in) / KUANG YONGJI (Autor:in) / MIN WEI (Autor:in) / ZHANG ZHIWEI (Autor:in)
08.11.2024
Patent
Elektronische Ressource
Chinesisch
| Europäisches Patentamt | 2021
High-gloss domestic ceramic glaze and preparation method thereof
| Europäisches Patentamt | 2020
Antibacterial glaze for ceramic sanitary ware, ceramic sanitary ware and preparation method thereof
| Europäisches Patentamt | 2020