Thermal-state repairing material for torpedo ladle
The invention discloses a hot-state repairing material for a torpedo ladle. The hot-state repairing material is prepared from the following raw materials in percentage by weight: 55 to 65 percent of reclaimed material, 20 to 30 percent of alumina powder, 8 to 12 percent of Guangxi white mud, 3 to 7 percent of silica powder, 0.1 to 0.5 percent of plasticizer, 0.1 to 0.5 percent of anti-rebound agent and 0.5 to 2 percent of fiber. The hot-state repairing material for the torpedo ladle has the advantages of high adhesion rate, good slag corrosion resistance, high high-temperature strength and long service life, the service life reaches 35 times or above, and the production cost is effectively reduced; and the thermal-state repairing material for the torpedo ladle is convenient to construct and suitable for industrial popularization and application.
本发明公开一种鱼雷罐用热态修补料，所述热态修补料按重量百分比包括以下原料：55～65％的再生料、20～30％的矾土粉、8～12％的广西白泥、3～7％的硅微粉、0.1～0.5％增塑剂、0.1～0.5％防反弹剂及0.5～2％纤维。本发明鱼雷罐用热态修补料，具有附着率高、抗渣侵蚀好、高温强度高以及使用寿命长的优点，使用寿命达35次以上，有效地降低生产成本；且本发明鱼雷罐用热态修补料施工方便，适合工业化推广应用。
Thermal-state repairing material for torpedo ladle
The invention discloses a hot-state repairing material for a torpedo ladle. The hot-state repairing material is prepared from the following raw materials in percentage by weight: 55 to 65 percent of reclaimed material, 20 to 30 percent of alumina powder, 8 to 12 percent of Guangxi white mud, 3 to 7 percent of silica powder, 0.1 to 0.5 percent of plasticizer, 0.1 to 0.5 percent of anti-rebound agent and 0.5 to 2 percent of fiber. The hot-state repairing material for the torpedo ladle has the advantages of high adhesion rate, good slag corrosion resistance, high high-temperature strength and long service life, the service life reaches 35 times or above, and the production cost is effectively reduced; and the thermal-state repairing material for the torpedo ladle is convenient to construct and suitable for industrial popularization and application.
本发明公开一种鱼雷罐用热态修补料，所述热态修补料按重量百分比包括以下原料：55～65％的再生料、20～30％的矾土粉、8～12％的广西白泥、3～7％的硅微粉、0.1～0.5％增塑剂、0.1～0.5％防反弹剂及0.5～2％纤维。本发明鱼雷罐用热态修补料，具有附着率高、抗渣侵蚀好、高温强度高以及使用寿命长的优点，使用寿命达35次以上，有效地降低生产成本；且本发明鱼雷罐用热态修补料施工方便，适合工业化推广应用。
Thermal-state repairing material for torpedo ladle
鱼雷罐用热态修补料
CAI CHANGXIU (Autor:in) / XU ZHIHUA (Autor:in) / ZHENG JIHONG (Autor:in) / TAN XIYANG (Autor:in)
27.12.2024
Patent
Elektronische Ressource
Chinesisch
Improvement of shotcast material for torpedo ladle
| Tema Archiv | 2013
Torpedo ladle material distribution system and method
| Europäisches Patentamt | 2024
Torpedo ladle lining repairing sprayed material as well as preparation method and use method thereof
| Europäisches Patentamt | 2015
Coating material for iron ladle and torpedo ladle and preparation method of coating material
| Europäisches Patentamt | 2022