METHOD FOR PRODUCTION OF MORTAR OR CONCRETE, STRENGTH INCREASING METHOD, AND ADDITIVE FOR STRENGTH INCREASE
PROBLEM TO BE SOLVED: To increase the strength of a cement-based hardened body while comparatively suppressing an expense.SOLUTION: Samples 2, 3, 4, 5, and 6 are prepared by adding by weight, 0.025%, 0.050%, 0.075%, 0.10% and 0.20% of sodium erythorbate to a cement-based hardened body. Further, samples 7, 8 are prepared by adding by weight, 0.10% and 0.20% of sodium gluconate to the cement, and a sample 1 is prepared as an additive-unused sample. In the result of a compressive strength test, all of the samples 2 to 8 exceed the sample 1 and thus, there is no sample evaluated to be unacceptable. In the comparison of magnitude in strength due to the type of additives, it is found out that the erythorbate contributes to strength increase higher by about 1.1 times than the gluconate.SELECTED DRAWING: Figure 1
【課題】比較的費用を抑制しつつセメント系硬化体の強度を増加させる。【解決手段】セメント系硬化体に対するエリソルビン酸ナトリウムの添加率を、セメントに対する重量パーセントで０．０２５％、０．０５０％、０．０７５％、０．１０％、０．２０％とし、これらを試料２、３、４、５、６とした。グルコン酸ナトリウムの添加量はセメントに対する重量パーセントで０．１０％、０．２０％とし、これらを試料７、８とした。また、比較のため添加剤を添加しない試料を作成し、試料１とした。試料２〜８のうち圧縮強度試験結果が添加剤を使用していない試料１を超えなかったものはなかったため、この試験により「不可」と評価されたものはなかった。添加剤の種類による強度を比較すると、エリソルビン酸塩の方がグルコン酸塩より１．１倍程度も強度増加への寄与が高いことがわかった。【選択図】図１
METHOD FOR PRODUCTION OF MORTAR OR CONCRETE, STRENGTH INCREASING METHOD, AND ADDITIVE FOR STRENGTH INCREASE
PROBLEM TO BE SOLVED: To increase the strength of a cement-based hardened body while comparatively suppressing an expense.SOLUTION: Samples 2, 3, 4, 5, and 6 are prepared by adding by weight, 0.025%, 0.050%, 0.075%, 0.10% and 0.20% of sodium erythorbate to a cement-based hardened body. Further, samples 7, 8 are prepared by adding by weight, 0.10% and 0.20% of sodium gluconate to the cement, and a sample 1 is prepared as an additive-unused sample. In the result of a compressive strength test, all of the samples 2 to 8 exceed the sample 1 and thus, there is no sample evaluated to be unacceptable. In the comparison of magnitude in strength due to the type of additives, it is found out that the erythorbate contributes to strength increase higher by about 1.1 times than the gluconate.SELECTED DRAWING: Figure 1
【課題】比較的費用を抑制しつつセメント系硬化体の強度を増加させる。【解決手段】セメント系硬化体に対するエリソルビン酸ナトリウムの添加率を、セメントに対する重量パーセントで０．０２５％、０．０５０％、０．０７５％、０．１０％、０．２０％とし、これらを試料２、３、４、５、６とした。グルコン酸ナトリウムの添加量はセメントに対する重量パーセントで０．１０％、０．２０％とし、これらを試料７、８とした。また、比較のため添加剤を添加しない試料を作成し、試料１とした。試料２〜８のうち圧縮強度試験結果が添加剤を使用していない試料１を超えなかったものはなかったため、この試験により「不可」と評価されたものはなかった。添加剤の種類による強度を比較すると、エリソルビン酸塩の方がグルコン酸塩より１．１倍程度も強度増加への寄与が高いことがわかった。【選択図】図１
METHOD FOR PRODUCTION OF MORTAR OR CONCRETE, STRENGTH INCREASING METHOD, AND ADDITIVE FOR STRENGTH INCREASE
モルタル又はコンクリートの製造方法、強度増加方法、及び強度増加用添加剤
TANIGUCHI OSAMU (Autor:in) / MIZUNO KENICHI (Autor:in)
02.03.2017
Patent
Elektronische Ressource
Japanisch
IPC:
C04B
Kalk
,
LIME
Manufacturing method of high-strength mortar concrete