SILICA FUME-CONTAINING HIGH FLUIDITY CEMENT COMPOSITION AND PRODUCTION METHOD THEREOF
To provide a silica fume-containing cement composition with high fluidity, capable of solving conventional problems with the occurrence of degradation in fluidity even if the amount of CA is restricted.SOLUTION: This invention relates to a silica fume-containing cement composition using a low-heat Portland cement as a base cement, and to a production method thereof. A substitutional rate of the silica fume is 7.5 to 15 mass%, the amount of CA in a base cement is 3.6 mass% or lower and the total amount of alkali in the base cement is 0.35 mass% or lower. The silica fume-containing cement composition exhibits a flow area ratio of 5.0 or more when a water-cement ratio is 15% or lower.SELECTED DRAWING: Figure 4
【課題】シリカフューム含有セメント組成物について、Ｃ３Ａ量を制限しても流動性が低下すると云う従来の問題を解決し、高い流動性を有するシリカフューム含有セメント組成物を提供する。【解決手段】低熱ポルトランドセメントをベースセメントとしてシリカフュームを含有するセメント組成物であって、シリカフュームの置換率が７.５〜１５質量％、ベースセメント中のＣ３Ａ量が３.６質量％以下、およびベースセメント中の全アルカリ量が０.３５質量％以下であり、水セメント比１５％以下において５.０以上のフロー面積比を示すことを特徴とするシリカフューム含有高流動性セメント組成物、およびその製造方法。【選択図】図４
SILICA FUME-CONTAINING HIGH FLUIDITY CEMENT COMPOSITION AND PRODUCTION METHOD THEREOF
To provide a silica fume-containing cement composition with high fluidity, capable of solving conventional problems with the occurrence of degradation in fluidity even if the amount of CA is restricted.SOLUTION: This invention relates to a silica fume-containing cement composition using a low-heat Portland cement as a base cement, and to a production method thereof. A substitutional rate of the silica fume is 7.5 to 15 mass%, the amount of CA in a base cement is 3.6 mass% or lower and the total amount of alkali in the base cement is 0.35 mass% or lower. The silica fume-containing cement composition exhibits a flow area ratio of 5.0 or more when a water-cement ratio is 15% or lower.SELECTED DRAWING: Figure 4
【課題】シリカフューム含有セメント組成物について、Ｃ３Ａ量を制限しても流動性が低下すると云う従来の問題を解決し、高い流動性を有するシリカフューム含有セメント組成物を提供する。【解決手段】低熱ポルトランドセメントをベースセメントとしてシリカフュームを含有するセメント組成物であって、シリカフュームの置換率が７.５〜１５質量％、ベースセメント中のＣ３Ａ量が３.６質量％以下、およびベースセメント中の全アルカリ量が０.３５質量％以下であり、水セメント比１５％以下において５.０以上のフロー面積比を示すことを特徴とするシリカフューム含有高流動性セメント組成物、およびその製造方法。【選択図】図４
SILICA FUME-CONTAINING HIGH FLUIDITY CEMENT COMPOSITION AND PRODUCTION METHOD THEREOF
シリカフューム含有高流動性セメント組成物およびその製造方法
KIMURA SHOHEI (Autor:in) / KUROIWA YOSHIHITO (Autor:in) / SHIRAHAMA NORIE (Autor:in)
01.11.2018
Patent
Elektronische Ressource
Japanisch
| Europäisches Patentamt | 2019
Phosphate Cement-Based Concretes Containing Silica Fume
| Online Contents | 2014
| British Library Conference Proceedings | 1993
Comparison of Fluidity between Metakaolin and Silica Fume Concretes
| Trans Tech Publications | 2011