CASTABLE REFRACTORY FOR BLAST FURNACE TROUGH
To provide castable refractory for a blast furnace trough, free from generating gas during its curing and free from powdering resulting from hydration, even if a silica-sol based binder is used.SOLUTION: Prevention of cracking and peeling, and improvement of corrosion resistance are required for castable refractory for use in lining a blast furnace trough. Castable refractory free from hydrogen gas generation resulting from a reaction of silicon and silica sol during its curing and free from powdering resulting from hydration, can be obtained by using a silica-sol based binder to improve thermal spalling resistance and by adding therein not more than 10 mass% in an external percentage (excluding zero) of an aluminum silicon alloy containing 20 to 50 mass% of silicon relative to the refractory raw material to improve hot strength. As a result, castable refractory for a blast furnace trough having improved hot strength, generating fewer cracks vertical to the working surface thereof, and having improved corrosion resistance, can be obtained.SELECTED DRAWING: Figure 1
【課題】シリカゾル系バインダーを使用しても、養生中のガス発生がなく、水和による粉化のない高炉樋用キャスタブル耐火物の提供。【解決手段】高炉樋の内張りに使用するキャスタブル耐火物には、亀裂、剥離の抑制と耐食性の向上が求められている。熱スポーリング性の向上のためにシリカゾル系バインダーを使用し、熱間強度を向上させるためにシリコンを２０〜５０質量％含むアルミニウムシリコン合金を前記耐火原料に対し外掛１０質量％以下（ゼロを除く）添加することにより、養生中にシリコンとシリカゾルの反応による水素ガスが発生せず、水和による粉化も発生しないキャスタブル耐火物が得られる。その結果、熱間強度が向上し、稼働面に垂直な亀裂が低減するとともに耐食性も向上した高炉樋用キャスタブル耐火物が得られる。【選択図】図１
CASTABLE REFRACTORY FOR BLAST FURNACE TROUGH
To provide castable refractory for a blast furnace trough, free from generating gas during its curing and free from powdering resulting from hydration, even if a silica-sol based binder is used.SOLUTION: Prevention of cracking and peeling, and improvement of corrosion resistance are required for castable refractory for use in lining a blast furnace trough. Castable refractory free from hydrogen gas generation resulting from a reaction of silicon and silica sol during its curing and free from powdering resulting from hydration, can be obtained by using a silica-sol based binder to improve thermal spalling resistance and by adding therein not more than 10 mass% in an external percentage (excluding zero) of an aluminum silicon alloy containing 20 to 50 mass% of silicon relative to the refractory raw material to improve hot strength. As a result, castable refractory for a blast furnace trough having improved hot strength, generating fewer cracks vertical to the working surface thereof, and having improved corrosion resistance, can be obtained.SELECTED DRAWING: Figure 1
【課題】シリカゾル系バインダーを使用しても、養生中のガス発生がなく、水和による粉化のない高炉樋用キャスタブル耐火物の提供。【解決手段】高炉樋の内張りに使用するキャスタブル耐火物には、亀裂、剥離の抑制と耐食性の向上が求められている。熱スポーリング性の向上のためにシリカゾル系バインダーを使用し、熱間強度を向上させるためにシリコンを２０〜５０質量％含むアルミニウムシリコン合金を前記耐火原料に対し外掛１０質量％以下（ゼロを除く）添加することにより、養生中にシリコンとシリカゾルの反応による水素ガスが発生せず、水和による粉化も発生しないキャスタブル耐火物が得られる。その結果、熱間強度が向上し、稼働面に垂直な亀裂が低減するとともに耐食性も向上した高炉樋用キャスタブル耐火物が得られる。【選択図】図１
CASTABLE REFRACTORY FOR BLAST FURNACE TROUGH
高炉樋用キャスタブル耐火物
WAKIMOTO MIKIYA (Autor:in) / MORIMOTO YOSHIHISA (Autor:in)
29.08.2019
Patent
Elektronische Ressource
Japanisch
IPC:
C04B
Kalk
,
LIME
/
C21B
Gewinnung von Eisen oder Stahl
,
MANUFACTURE OF IRON OR STEEL
/
F27D
Einzelheiten oder Zubehör für Industrieöfen, Schachtöfen, Brennöfen oder Retorten, soweit sie nicht auf eine Ofenart eingeschränkt sind
,
DETAILS OR ACCESSORIES OF FURNACES, KILNS, OVENS, OR RETORTS, IN SO FAR AS THEY ARE OF KINDS OCCURRING IN MORE THAN ONE KIND OF FURNACE
CASTABLE REFRACTORY FOR BLAST FURNACE TROUGH METAL PART
| Europäisches Patentamt | 2021
Castable for main trough of middle-sized blast furnace
| Europäisches Patentamt | 2016