SLURRY COMPOSITION
To provide a slurry composition capable of preventing defects from occurring on a sheet and thereby advancing a sintering step in a ceramic molding process, and capable of producing a ceramic molded body excellent in smoothness and compactness.SOLUTION: A slurry composition comprises a resin component (A) and a resin component (B) as binders. A content ratio ((A)/(B)) of (A) and (B) is 20/80 to 80 to 20 by mass ratio. The resin component (A) contains: 60 to 95 mass% of a polyethylene glycol-containing (meth)acrylic monomer (a1); and 5 to 40 mass% of a hydroxyl group-containing (meth)acrylic monomer (a2). A mass ratio of a polyethylene glycol moiety contained in the resin component (A) is 40 to 80 mass% based on the whole component (A), and a mass average molecular weight of the resin component (A) is 40,000 to 300,000. The resin component (B) is one or more resin selected from the group consisting of an acrylic resin, a cellulose-based resin, a polyvinyl alcohol, and polyvinyl pyrrolidone.SELECTED DRAWING: None
【課題】セラミックス成形において焼結工程が良好に進行するためシートに欠陥が発生することを抑え、平滑性と緻密性に優れるセラミックス成形体を作製可能なスラリー組成物の提供。【解決手段】スラリー組成物は、樹脂成分（Ａ）および樹脂成分（Ｂ）をバインダーとして含んでなる。（Ａ）と（Ｂ）との含有割合（（Ａ）／（Ｂ））が質量比で２０／８０〜８０／２０である。（Ａ）が、ポリエチレングリコール含有（メタ）アクリルモノマー（ａ１）を６０〜９５質量％、水酸基含有（メタ）アクリルモノマー（ａ２）を５〜４０質量％含有する。（Ａ）中に含まれるポリエチレングリコール部分の質量比が（Ａ）全体に対して４０〜８０質量％であり、（Ａ）の質量平均分子量が４０，０００〜３００，０００である。（Ｂ）が、アクリル系樹脂、セルロース系樹脂、ポリビニルアルコールおよびポリビニルピロリドンからなる群より選ばれた１種以上の樹脂である。【選択図】なし
SLURRY COMPOSITION
To provide a slurry composition capable of preventing defects from occurring on a sheet and thereby advancing a sintering step in a ceramic molding process, and capable of producing a ceramic molded body excellent in smoothness and compactness.SOLUTION: A slurry composition comprises a resin component (A) and a resin component (B) as binders. A content ratio ((A)/(B)) of (A) and (B) is 20/80 to 80 to 20 by mass ratio. The resin component (A) contains: 60 to 95 mass% of a polyethylene glycol-containing (meth)acrylic monomer (a1); and 5 to 40 mass% of a hydroxyl group-containing (meth)acrylic monomer (a2). A mass ratio of a polyethylene glycol moiety contained in the resin component (A) is 40 to 80 mass% based on the whole component (A), and a mass average molecular weight of the resin component (A) is 40,000 to 300,000. The resin component (B) is one or more resin selected from the group consisting of an acrylic resin, a cellulose-based resin, a polyvinyl alcohol, and polyvinyl pyrrolidone.SELECTED DRAWING: None
【課題】セラミックス成形において焼結工程が良好に進行するためシートに欠陥が発生することを抑え、平滑性と緻密性に優れるセラミックス成形体を作製可能なスラリー組成物の提供。【解決手段】スラリー組成物は、樹脂成分（Ａ）および樹脂成分（Ｂ）をバインダーとして含んでなる。（Ａ）と（Ｂ）との含有割合（（Ａ）／（Ｂ））が質量比で２０／８０〜８０／２０である。（Ａ）が、ポリエチレングリコール含有（メタ）アクリルモノマー（ａ１）を６０〜９５質量％、水酸基含有（メタ）アクリルモノマー（ａ２）を５〜４０質量％含有する。（Ａ）中に含まれるポリエチレングリコール部分の質量比が（Ａ）全体に対して４０〜８０質量％であり、（Ａ）の質量平均分子量が４０，０００〜３００，０００である。（Ｂ）が、アクリル系樹脂、セルロース系樹脂、ポリビニルアルコールおよびポリビニルピロリドンからなる群より選ばれた１種以上の樹脂である。【選択図】なし
SLURRY COMPOSITION
スラリー組成物
TANAKA MASAHIRO (Autor:in) / YAMADA AKIHIRO (Autor:in)
15.04.2021
Patent
Elektronische Ressource
Japanisch
IPC:
C08L
COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
,
Massen auf Basis makromolekularer Verbindungen
/
C04B
Kalk
,
LIME
/
C08F
MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
,
Makromolekulare Verbindungen, erhalten durch Reaktionen, an denen nur ungesättigte Kohlenstoff-Kohlenstoff-Bindungen beteiligt sind
/
C08K
Verwendung von anorganischen oder nichtmakromolekularen organischen Stoffen als Zusatzstoffe
,
USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS
CERIA SLURRY ADDITIVE COMPOSITION AND SLURRY COMPOSITION COMPRISING THE SAME
| Europäisches Patentamt | 2016
CERIA SLURRY ADDITIVE COMPOSITION AND SLURRY COMPOSITION COMPRISING THE SAME
Europäisches Patentamt | 2016