COVERING MATERIAL, MANUFACTURING METHOD OF COVERING MATERIAL, CONCRETE MOLDED BODY, TUBULAR MOLDED BODY, MANUFACTURING METHOD OF TUBULAR MOLDED BODY, AND, SLURRY
To provide a covering material or the like capable of imparting sulfuric acid resistance to a concrete molded body.SOLUTION: The covering material comprises a cement-based hydraulic material, the cement-based hydraulic material contains a blast furnace slag fine powder and a fly ash, the content ratio of the blast furnace slag fine powder in the cement-based hydraulic material is over 50 mass% and 90 mass% or less, the content ratio of the fly ash in the cement-based hydraulic material is over 5 mass% to 25% or less, and the total content ratio of the blast furnace slag fine powder and the fly ash in the cement-based hydraulic material exceeds 65 mass%.SELECTED DRAWING: None
【課題】本発明は、コンクリート成形体に耐硫酸性を付与し得る被覆材等を提供する。【解決手段】本発明は、セメント系水硬性材料を備え、前記セメント系水硬性材料は、高炉スラグ微粉末、及び、フライアッシュを含有し、前記セメント系水硬性材料における前記高炉スラグ微粉末の含有割合は、５０質量％を超え９０質量％以下であり、前記セメント系水硬性材料における前記フライアッシュの含有割合は、５質量％を超え２５質量％以下であり、前記セメント系水硬性材料における前記高炉スラグ微粉末及び前記フライアッシュの合計の含有割合は、６５質量％を超える、被覆材等である。【選択図】 なし
COVERING MATERIAL, MANUFACTURING METHOD OF COVERING MATERIAL, CONCRETE MOLDED BODY, TUBULAR MOLDED BODY, MANUFACTURING METHOD OF TUBULAR MOLDED BODY, AND, SLURRY
To provide a covering material or the like capable of imparting sulfuric acid resistance to a concrete molded body.SOLUTION: The covering material comprises a cement-based hydraulic material, the cement-based hydraulic material contains a blast furnace slag fine powder and a fly ash, the content ratio of the blast furnace slag fine powder in the cement-based hydraulic material is over 50 mass% and 90 mass% or less, the content ratio of the fly ash in the cement-based hydraulic material is over 5 mass% to 25% or less, and the total content ratio of the blast furnace slag fine powder and the fly ash in the cement-based hydraulic material exceeds 65 mass%.SELECTED DRAWING: None
【課題】本発明は、コンクリート成形体に耐硫酸性を付与し得る被覆材等を提供する。【解決手段】本発明は、セメント系水硬性材料を備え、前記セメント系水硬性材料は、高炉スラグ微粉末、及び、フライアッシュを含有し、前記セメント系水硬性材料における前記高炉スラグ微粉末の含有割合は、５０質量％を超え９０質量％以下であり、前記セメント系水硬性材料における前記フライアッシュの含有割合は、５質量％を超え２５質量％以下であり、前記セメント系水硬性材料における前記高炉スラグ微粉末及び前記フライアッシュの合計の含有割合は、６５質量％を超える、被覆材等である。【選択図】 なし
COVERING MATERIAL, MANUFACTURING METHOD OF COVERING MATERIAL, CONCRETE MOLDED BODY, TUBULAR MOLDED BODY, MANUFACTURING METHOD OF TUBULAR MOLDED BODY, AND, SLURRY
被覆材、被覆材の製造方法、コンクリート成形体、管状成形体、管状成形体の製造方法、及び、スラリー
SAITO HISASHI (Autor:in)
07.10.2021
Patent
Elektronische Ressource
Japanisch
| Europäisches Patentamt | 2021
MOLDED BODY MANUFACTURING FACILITY, MOLDED BODY MANUFACTURING METHOD, AND MOLDED BODY
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2020
METHOD FOR MANUFACTURING CONCRETE MOLDED BODY, AND CONCRETE MOLDED BODY
| Europäisches Patentamt | 2024