METHOD FOR MANUFACTURING PRECAST RESIDUAL FRAME MOLD PANEL
To provide a method for manufacturing a precast residual frame mold panel, capable of preventing a permeable fine powder layer, such as calcium carbonate, from being formed on a back side of a panel body, without causing any work effort.SOLUTION: A method for manufacturing a precast residual frame mold panel includes feeding a concrete raw material containing a cement, gravel and sand, and a fluidized cement composition, etc., obtained by mixing 5 wt.% to 40 wt.% of a limestone fine powder with respect to the cement in the concrete raw material with kneading water, into a frame for molding, thereby rapidly reacting dissolved calcium hydroxide with the limestone fine powder to form a dense hydration product that is insoluble in water. Accordingly, a waterproof layer 4 containing the hydration product is formed over an entire area of a back surface 2a of the panel body 2, thereby preventing a chemical reaction between carbon dioxide in the outside air and the calcium hydroxide, preventing the formation of a permeable fine powder layer L on the back surface, and naturally sealing a capillary void 9A and a void 9B formed between a buried part 7 of a connecting fitting 3 and the panel body 2 by the waterproof layer 4.SELECTED DRAWING: Figure 1
【課題】作業の手間が生じずに、パネル本体の背面に炭酸カルシウム等の透水性微紛末層が形成されることを防止できるプレキャスト製残存型枠パネルの製造方法を提供する。【解決手段】プレキャスト製残存型枠パネルの製造方法は、セメント、砂利及び砂を含むコンクリート原材料と、このコンクリート原材料中のセメントに対して５重量％から４０重量％の石灰石微粉末と、練り水とをミキシングした流動化セメント組成物等を成形用型枠に投入し、溶出する水酸化カルシウムと、石灰石微粉末とが急速に水和反応し、水に不溶な水和生成物が緻密に形成されることで、パネル本体２の背面２ａ全域に水和生成物を含む防水層４が形成され、外気中の二酸化炭素と水酸化カルシウムが化学反応し、背面に透水性微粉末層Ｌが形成されることを防止し、毛細管空隙９Ａや被連結金具３の埋設部７とパネル本体２との間に形成された空隙９Ｂが防水層４により自然に塞がれる。【選択図】図１
METHOD FOR MANUFACTURING PRECAST RESIDUAL FRAME MOLD PANEL
To provide a method for manufacturing a precast residual frame mold panel, capable of preventing a permeable fine powder layer, such as calcium carbonate, from being formed on a back side of a panel body, without causing any work effort.SOLUTION: A method for manufacturing a precast residual frame mold panel includes feeding a concrete raw material containing a cement, gravel and sand, and a fluidized cement composition, etc., obtained by mixing 5 wt.% to 40 wt.% of a limestone fine powder with respect to the cement in the concrete raw material with kneading water, into a frame for molding, thereby rapidly reacting dissolved calcium hydroxide with the limestone fine powder to form a dense hydration product that is insoluble in water. Accordingly, a waterproof layer 4 containing the hydration product is formed over an entire area of a back surface 2a of the panel body 2, thereby preventing a chemical reaction between carbon dioxide in the outside air and the calcium hydroxide, preventing the formation of a permeable fine powder layer L on the back surface, and naturally sealing a capillary void 9A and a void 9B formed between a buried part 7 of a connecting fitting 3 and the panel body 2 by the waterproof layer 4.SELECTED DRAWING: Figure 1
【課題】作業の手間が生じずに、パネル本体の背面に炭酸カルシウム等の透水性微紛末層が形成されることを防止できるプレキャスト製残存型枠パネルの製造方法を提供する。【解決手段】プレキャスト製残存型枠パネルの製造方法は、セメント、砂利及び砂を含むコンクリート原材料と、このコンクリート原材料中のセメントに対して５重量％から４０重量％の石灰石微粉末と、練り水とをミキシングした流動化セメント組成物等を成形用型枠に投入し、溶出する水酸化カルシウムと、石灰石微粉末とが急速に水和反応し、水に不溶な水和生成物が緻密に形成されることで、パネル本体２の背面２ａ全域に水和生成物を含む防水層４が形成され、外気中の二酸化炭素と水酸化カルシウムが化学反応し、背面に透水性微粉末層Ｌが形成されることを防止し、毛細管空隙９Ａや被連結金具３の埋設部７とパネル本体２との間に形成された空隙９Ｂが防水層４により自然に塞がれる。【選択図】図１
METHOD FOR MANUFACTURING PRECAST RESIDUAL FRAME MOLD PANEL
プレキャスト製残存型枠パネルの製造方法
YAMASHITA JOJI (Autor:in)
14.08.2024
Patent
Elektronische Ressource
Japanisch