MODIFIED ASPHALT BINDER MANUFACTURE AND ASPHALT CONCRETE COMPOSITION
The present invention relates to a method for manufacturing a modified asphalt binder using in-situ polymerization, and to an asphalt concrete composition using the same. The method for manufacturing a modified asphalt binder improves the durability of vehicle roads by improving binding force and resistance of the asphalt binder, thereby reducing maintenance costs, and human and physical loss caused by traffic congestion occurred when road maintenance is performed. To this end, the manufacturing method of the present invention comprises: a dilution step of mixing 2,6-dimethylphenol (DMP) with a diluent at a ratio of 1:1 based on wt% in a reactor, which maintains the temperature thereof at 120-140°C; a dissolution step of mixing 5-10 wt% of the DMP diluted solution with 90-95 wt% of AP-5 asphalt (penetration grade 60-70) to dissolve the mixture; a mixing step of mixing the DMP, which is a monomer, with styrene- butadiene-styrene (SBS), wherein 10-15 wt% of the DMP is mixed with respect to 100 wt% of the SBS; and a stirring step of mixing 80-90 wt% of the asphalt solution with 10-20 wt% of the SBS mixture, and implementing the agitation of the resultant product at 3000 rpm for 2 hours by using a homogeneous blender. In the dilution step, one of toluene or ethylene glycol is selectively used as the diluent.
본 발명은 내부중합을 이용한 개질아스팔트 바인더 제조방법 및 이를 이용한 아스팔트 콘크리트 조성물에 관한 것으로서, 아스팔트 바인더의 점결력 및 저항성의 개선을 통해 도로 포장층의 내구성이 향상되어 유지보수 비용의 절감 및 도로유지 보수시 발생하는 차량 정체로 인한 인적, 물적 손실을 감소시키기 위한 것이다. 이를 실현하기 위한 본 발명의 개질아스팔트 바인더 제조방법은, 120~140℃로 유지되는 반응기에 2,6-디메틸페놀(DMP)과 희석제를 중량% 기준 1:1의 비율로 혼합하되, 상기 희석제는 톨루엔 또는 에틸렌글리콜 중 하나가 선택적으로 사용되는 희석단계와; 상기 DMP희석액 5~10중량%를 AP-5아스팔트(침입도 60~70) 90~95중량%와 혼합하여 용해시키는 용해단계와; 단량체인 DMP와 SBS(Styrene- Butadiene-Styrene)를 혼합하되, SBS 100중량%를 기준으로 DMP는 10~15중량%로 혼합이 이루어지는 혼합단계와; 상기 아스팔트 용해액 80~90중량%와 SBS혼합물 10~20중량%를 혼합 후, 균질혼합기를 이용하여 3,000 rpm으로 2시간 동안 교반을 실시하는 교반단계를 포함하는 것을 특징으로 한다.
MODIFIED ASPHALT BINDER MANUFACTURE AND ASPHALT CONCRETE COMPOSITION
The present invention relates to a method for manufacturing a modified asphalt binder using in-situ polymerization, and to an asphalt concrete composition using the same. The method for manufacturing a modified asphalt binder improves the durability of vehicle roads by improving binding force and resistance of the asphalt binder, thereby reducing maintenance costs, and human and physical loss caused by traffic congestion occurred when road maintenance is performed. To this end, the manufacturing method of the present invention comprises: a dilution step of mixing 2,6-dimethylphenol (DMP) with a diluent at a ratio of 1:1 based on wt% in a reactor, which maintains the temperature thereof at 120-140°C; a dissolution step of mixing 5-10 wt% of the DMP diluted solution with 90-95 wt% of AP-5 asphalt (penetration grade 60-70) to dissolve the mixture; a mixing step of mixing the DMP, which is a monomer, with styrene- butadiene-styrene (SBS), wherein 10-15 wt% of the DMP is mixed with respect to 100 wt% of the SBS; and a stirring step of mixing 80-90 wt% of the asphalt solution with 10-20 wt% of the SBS mixture, and implementing the agitation of the resultant product at 3000 rpm for 2 hours by using a homogeneous blender. In the dilution step, one of toluene or ethylene glycol is selectively used as the diluent.
본 발명은 내부중합을 이용한 개질아스팔트 바인더 제조방법 및 이를 이용한 아스팔트 콘크리트 조성물에 관한 것으로서, 아스팔트 바인더의 점결력 및 저항성의 개선을 통해 도로 포장층의 내구성이 향상되어 유지보수 비용의 절감 및 도로유지 보수시 발생하는 차량 정체로 인한 인적, 물적 손실을 감소시키기 위한 것이다. 이를 실현하기 위한 본 발명의 개질아스팔트 바인더 제조방법은, 120~140℃로 유지되는 반응기에 2,6-디메틸페놀(DMP)과 희석제를 중량% 기준 1:1의 비율로 혼합하되, 상기 희석제는 톨루엔 또는 에틸렌글리콜 중 하나가 선택적으로 사용되는 희석단계와; 상기 DMP희석액 5~10중량%를 AP-5아스팔트(침입도 60~70) 90~95중량%와 혼합하여 용해시키는 용해단계와; 단량체인 DMP와 SBS(Styrene- Butadiene-Styrene)를 혼합하되, SBS 100중량%를 기준으로 DMP는 10~15중량%로 혼합이 이루어지는 혼합단계와; 상기 아스팔트 용해액 80~90중량%와 SBS혼합물 10~20중량%를 혼합 후, 균질혼합기를 이용하여 3,000 rpm으로 2시간 동안 교반을 실시하는 교반단계를 포함하는 것을 특징으로 한다.
MODIFIED ASPHALT BINDER MANUFACTURE AND ASPHALT CONCRETE COMPOSITION
내부중합을 이용한 개질아스팔트 바인더 제조방법 및 이를 이용한 아스팔트 콘크리트 조성물
YOON PIL YONG (Autor:in)
16.06.2016
Patent
Elektronische Ressource
Koreanisch
MODIFIED ASPHALT BINDER COMPOSITION AND MODIFIED ASPHALT MIXTURE COMPRISING THE SAME
| Europäisches Patentamt | 2023
BASE ASPHALT COMPOSITION AND MODIFIED ASPHALT BINDER COMPOSITION USING THE SAME
Europäisches Patentamt | 2024
BASE ASPHALT COMPOSITION AND MODIFIED ASPHALT BINDER COMPOSITION USING THE SAME
| Europäisches Patentamt | 2024