A HIGH EARLY STRENGTH CEMENT CONCRETE COMPOSITION HAVING THE SELF-HEALING FOR ROAD PAVEMENT AND A REPAIRING METHOD OF ROAD PAVEMENT USING THE SAME
The present invention relates to a high early strength cement concrete structure having self-repairing properties and a road repair and maintenance method using the same including 3 to 45 wt% of early strength inorganic binding material, 20 to 80 wt% of fine aggregate, 15 to 75 wt% of coarse aggregate, 0.1 to 20 wt% of water, and 0.01 to 20 wt% of functional admixture. The early strength inorganic binding material includes 15 to 80 wt% of early strength Portland cement, 3 to 50 wt% of amorphous calcium aluminate, 1 to 40 wt% of alumina cement, 1 to 40 wt% of gelrite having a fineness of 3,000 to 8,500 square centimeters per gram, 0.1 to 20 wt% of quartz, 0.1 to 15 wt% of desulfurized gypsum, 0.01 to 10 wt% of zinc stearate, 0.01 to 10 wt% of zircoaluminate, and 0.01 to 10 wt% of zirconia. The high early strength cement concrete composition according to the present invention is capable of improving concrete workability, improving the strength of the concrete, its tensile strength and adhesive strength in particular, significantly improving durability, preventing expansion breakdown and surface cracking of the concrete, and exhibiting self-healing properties.
본 발명은 속경성 무기 결합재 3∼45중량%, 잔골재 20∼80중량%, 굵은골재 15∼75중량%, 물 0.1∼20중량% 및 기능성 혼화제 0.01∼20중량% 포함하며, 상기 속경성 무기 결합재는 조강 포틀랜드 시멘트 15∼80중량%, 비정질칼슘알루미네이트 3∼50중량%, 알루미나 시멘트 1∼40중량%, 분말도가 3,000∼8,500㎠/g인 겔라이트 1∼40중량%, 쿼츠 0.1∼20중량%, 탈황석고 0.1∼15중량%, 스테아린산아연 0.01∼10중량%, 지르코알루미네이트 0.01∼10중량% 및 지르코니아 0.01∼10중량%를 포함하는 것을 특징으로 하는 자기보수성을 가지는 초속경 시멘트 콘크리트 구조물 및 이를 이용한 도로 유지 보수 공법에 관한 것이다. 본 발명에 따른 초속경 시멘트 콘크리트 조성물은 콘크리트의 작업성을 향상시킬 수 있고, 콘크리트의 강도, 특히 인장강도 및 부착강도를 개선하며 내구성을 크게 향상시킬 수 있고, 콘크리트의 표면균열 및 팽창파괴현상을 방지하는 효과 및 자기 치유성능을 발휘할 수 있다.
A HIGH EARLY STRENGTH CEMENT CONCRETE COMPOSITION HAVING THE SELF-HEALING FOR ROAD PAVEMENT AND A REPAIRING METHOD OF ROAD PAVEMENT USING THE SAME
The present invention relates to a high early strength cement concrete structure having self-repairing properties and a road repair and maintenance method using the same including 3 to 45 wt% of early strength inorganic binding material, 20 to 80 wt% of fine aggregate, 15 to 75 wt% of coarse aggregate, 0.1 to 20 wt% of water, and 0.01 to 20 wt% of functional admixture. The early strength inorganic binding material includes 15 to 80 wt% of early strength Portland cement, 3 to 50 wt% of amorphous calcium aluminate, 1 to 40 wt% of alumina cement, 1 to 40 wt% of gelrite having a fineness of 3,000 to 8,500 square centimeters per gram, 0.1 to 20 wt% of quartz, 0.1 to 15 wt% of desulfurized gypsum, 0.01 to 10 wt% of zinc stearate, 0.01 to 10 wt% of zircoaluminate, and 0.01 to 10 wt% of zirconia. The high early strength cement concrete composition according to the present invention is capable of improving concrete workability, improving the strength of the concrete, its tensile strength and adhesive strength in particular, significantly improving durability, preventing expansion breakdown and surface cracking of the concrete, and exhibiting self-healing properties.
본 발명은 속경성 무기 결합재 3∼45중량%, 잔골재 20∼80중량%, 굵은골재 15∼75중량%, 물 0.1∼20중량% 및 기능성 혼화제 0.01∼20중량% 포함하며, 상기 속경성 무기 결합재는 조강 포틀랜드 시멘트 15∼80중량%, 비정질칼슘알루미네이트 3∼50중량%, 알루미나 시멘트 1∼40중량%, 분말도가 3,000∼8,500㎠/g인 겔라이트 1∼40중량%, 쿼츠 0.1∼20중량%, 탈황석고 0.1∼15중량%, 스테아린산아연 0.01∼10중량%, 지르코알루미네이트 0.01∼10중량% 및 지르코니아 0.01∼10중량%를 포함하는 것을 특징으로 하는 자기보수성을 가지는 초속경 시멘트 콘크리트 구조물 및 이를 이용한 도로 유지 보수 공법에 관한 것이다. 본 발명에 따른 초속경 시멘트 콘크리트 조성물은 콘크리트의 작업성을 향상시킬 수 있고, 콘크리트의 강도, 특히 인장강도 및 부착강도를 개선하며 내구성을 크게 향상시킬 수 있고, 콘크리트의 표면균열 및 팽창파괴현상을 방지하는 효과 및 자기 치유성능을 발휘할 수 있다.
A HIGH EARLY STRENGTH CEMENT CONCRETE COMPOSITION HAVING THE SELF-HEALING FOR ROAD PAVEMENT AND A REPAIRING METHOD OF ROAD PAVEMENT USING THE SAME
자기보수성을 가지는 초속경 시멘트 콘크리트 조성물 및 이를 이용한 도로 유지 보수 공법
CHOI JONG YUN (Autor:in) / SHIN MIN JI (Autor:in)
27.03.2017
Patent
Elektronische Ressource
Koreanisch
| Europäisches Patentamt | 2016
| Europäisches Patentamt | 2017
| Europäisches Patentamt | 2017
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2016