A HIGH EARLY STRENGTH CEMENT CONCRETE COMPOSITION HAVING THE IMPROVED DURABILITY FOR ROAD PAVEMENT AND A REPAIRING METHOD OF ROAD PAVEMENT USING THE SAME
The present invention relates to a durability-improved high early strength cement concrete composition and a road repair and maintenance method using the same, including 5 to 40 wt% of high early strength cement binding material, 15 to 75 wt% of fine aggregate, 15 to 70 wt% of coarse aggregate, 0.1 to 20 wt% of water, and 0.01 to 20 wt% of polymer modifier. The high early strength cement binding material includes 15 to 75 wt% of high early strength Portland cement, 3 to 45 wt% of calcium sulfoaluminate, 1 to 35 wt% of alumina cement, 1 to 30 wt% of silicate white clay, 1 to 40 wt% of blast furnace slag powder having a fineness of 3,500 to 8,000 square centimeters per gram, 1 to 20 wt% of gypsum, 0.01 to 15 wt% of calcium oxide, 0.01 to 10 wt% of nickel aluminate, and 0.01 to 10 wt% of zirconium. The polymer modifier includes 40 to 99 wt% of styrene-butadiene rubber, 0.1 to 30 wt% of urethane emulsion, 0.01 to 15 wt% of polyparaphenylene vinylene, 0.01 to 15 wt% of polyphenyl ether, and 0.01 to 10 wt% of polymethacrylic acid aminoalkyl ester. The high early strength cement concrete composition according to the present invention is capable of improving concrete workability, improving the strength of the concrete, its tensile strength and adhesive strength in particular, significantly improving durability, and preventing expansion breakdown and surface cracking of the concrete.
본 발명은 내구성능이 개선된 초속경 시멘트 콘크리트 조성물 및 이를 이용한 도로 유지 보수 공법에 관한 것으로, 초속경 시멘트 결합재 5∼40중량%, 잔골재 15∼75중량%, 굵은골재 15∼70중량%, 물 0.1∼20중량% 및 폴리머 개질제 0.01∼20중량% 포함하며, 상기 초속경 시멘트 결합재는 조강 포틀랜드 시멘트 15∼75중량%, 칼슘설포알루미네이트 3∼45중량%, 알루미나 시멘트 1∼35중량%, 규산 백토 1∼30중량%, 분말도가 3,500∼8,000㎠/g인 고로슬래그 분말 1∼40중량%, 석고 1∼20중량%, 산화칼슘 0.01∼15중량%, 니켈알루미네이트 0.01∼10중량% 및 지르코늄 0.01∼10중량%를 포함하고, 상기 폴리머 개질제는 스티렌-부타디엔 고무 40∼99중량%, 우레탄 에멀젼 0.1∼30중량%, 폴리파라페닐렌 비닐렌 0.01∼15중량%, 폴리페닐에테르 0.01∼15중량% 및 폴리메타크릴산아미노알킬에스테르 0.01∼10중량%를 포함하는 것을 특징으로 하는 것이다. 본 발명에 따른 초속경 시멘트 콘크리트 조성물은 콘크리트의 작업성을 향상시킬 수 있고, 콘크리트의 강도, 특히 인장강도 및 부착강도를 개선하며 내구성을 크게 향상시킬 수 있고, 콘크리트의 표면균열 및 팽창파괴현상을 방지하는 효과를 발휘할 수 있다.
A HIGH EARLY STRENGTH CEMENT CONCRETE COMPOSITION HAVING THE IMPROVED DURABILITY FOR ROAD PAVEMENT AND A REPAIRING METHOD OF ROAD PAVEMENT USING THE SAME
The present invention relates to a durability-improved high early strength cement concrete composition and a road repair and maintenance method using the same, including 5 to 40 wt% of high early strength cement binding material, 15 to 75 wt% of fine aggregate, 15 to 70 wt% of coarse aggregate, 0.1 to 20 wt% of water, and 0.01 to 20 wt% of polymer modifier. The high early strength cement binding material includes 15 to 75 wt% of high early strength Portland cement, 3 to 45 wt% of calcium sulfoaluminate, 1 to 35 wt% of alumina cement, 1 to 30 wt% of silicate white clay, 1 to 40 wt% of blast furnace slag powder having a fineness of 3,500 to 8,000 square centimeters per gram, 1 to 20 wt% of gypsum, 0.01 to 15 wt% of calcium oxide, 0.01 to 10 wt% of nickel aluminate, and 0.01 to 10 wt% of zirconium. The polymer modifier includes 40 to 99 wt% of styrene-butadiene rubber, 0.1 to 30 wt% of urethane emulsion, 0.01 to 15 wt% of polyparaphenylene vinylene, 0.01 to 15 wt% of polyphenyl ether, and 0.01 to 10 wt% of polymethacrylic acid aminoalkyl ester. The high early strength cement concrete composition according to the present invention is capable of improving concrete workability, improving the strength of the concrete, its tensile strength and adhesive strength in particular, significantly improving durability, and preventing expansion breakdown and surface cracking of the concrete.
본 발명은 내구성능이 개선된 초속경 시멘트 콘크리트 조성물 및 이를 이용한 도로 유지 보수 공법에 관한 것으로, 초속경 시멘트 결합재 5∼40중량%, 잔골재 15∼75중량%, 굵은골재 15∼70중량%, 물 0.1∼20중량% 및 폴리머 개질제 0.01∼20중량% 포함하며, 상기 초속경 시멘트 결합재는 조강 포틀랜드 시멘트 15∼75중량%, 칼슘설포알루미네이트 3∼45중량%, 알루미나 시멘트 1∼35중량%, 규산 백토 1∼30중량%, 분말도가 3,500∼8,000㎠/g인 고로슬래그 분말 1∼40중량%, 석고 1∼20중량%, 산화칼슘 0.01∼15중량%, 니켈알루미네이트 0.01∼10중량% 및 지르코늄 0.01∼10중량%를 포함하고, 상기 폴리머 개질제는 스티렌-부타디엔 고무 40∼99중량%, 우레탄 에멀젼 0.1∼30중량%, 폴리파라페닐렌 비닐렌 0.01∼15중량%, 폴리페닐에테르 0.01∼15중량% 및 폴리메타크릴산아미노알킬에스테르 0.01∼10중량%를 포함하는 것을 특징으로 하는 것이다. 본 발명에 따른 초속경 시멘트 콘크리트 조성물은 콘크리트의 작업성을 향상시킬 수 있고, 콘크리트의 강도, 특히 인장강도 및 부착강도를 개선하며 내구성을 크게 향상시킬 수 있고, 콘크리트의 표면균열 및 팽창파괴현상을 방지하는 효과를 발휘할 수 있다.
A HIGH EARLY STRENGTH CEMENT CONCRETE COMPOSITION HAVING THE IMPROVED DURABILITY FOR ROAD PAVEMENT AND A REPAIRING METHOD OF ROAD PAVEMENT USING THE SAME
내구성능이 개선된 초속경 시멘트 콘크리트 조성물 및 이를 이용한 도로 유지 보수 공법
SHIN MIN JI (Autor:in) / KIM YOUNG NAM (Autor:in) / PARK JEONG YEON (Autor:in)
28.03.2017
Patent
Elektronische Ressource
Koreanisch
| Europäisches Patentamt | 2016
| Europäisches Patentamt | 2017
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2017
| Europäisches Patentamt | 2016