Fast Cementitious Cement Concrete Composition and Repair Method of Concrete Pavement Using the Same
The present invention relates to a method for preparing a rapid-curing ultra-high early strength concrete composition and to a method for repairing pavement by using the same which comprises: 5-40 wt% of a rapid-curing ultra-high early strength cement-based binder; 25-65 wt% of fine aggregates; 10-65 wt% of coarse aggregates; 2-25 wt% of water; and 0.1-5 wt% of an admixture, wherein the rapid-curing, ultra-high early strength cement-based binder is usually composed of 30-45 wt% of Portland cement clinker ground powder, 30-45 wt% of Wien-based rapid curing minerals, 10-20 wt% of rapid-curing cement, 0.1-2 wt% of gypsum, 2-10 wt% of slag powder, and 0.1-5 wt% of a latent heat material. According to the present invention, a problem of high costs of ultra-rapid-curing cement concrete can be addressed; a curing period thereof can be usually shortened compared to that of Portland cement concrete, early strength cement concrete and ultra-high early strength cement concrete; and durability will be enhanced to reduce costs for maintenance and improve constructability.
본 발명은, 속경성 초조강 시멘트계 결합재 5~40중량%, 잔골재 25~65중량%, 굵은골재 10~65중량%, 물 2~25중량%, 혼화제 0.1~5중량%를 포함하며, 상기 속경성 초조강 시멘트계 결합재는 보통 포틀랜드 시멘트 클링커 분쇄 분말 30~45중량%, 아윈계 속경성 광물 30~45중량%, 초속경 시멘트 10~20중량%, 석고 0.1~2중량%, 슬래그 미분말 2~10중량%, 잠열재 0.1~5중량%로 구성되는 속경성 초조강 콘크리트 조성물을 제조하는 방법과, 이를 이용한 포장 보수 공법에 관한 것이다. 본 발명에 의하면, 초속경 시멘트 콘크리트의 고비용을 해결하고 보통 포틀랜드 시멘트 콘크리트와 조강 시멘트 콘크리트, 초조강 시멘트 콘크리트보다 양생기간을 단축시키고, 내구성을 향상시켜 유지보수 비용 및 시공성 향상을 달성할 수 있다.
Fast Cementitious Cement Concrete Composition and Repair Method of Concrete Pavement Using the Same
The present invention relates to a method for preparing a rapid-curing ultra-high early strength concrete composition and to a method for repairing pavement by using the same which comprises: 5-40 wt% of a rapid-curing ultra-high early strength cement-based binder; 25-65 wt% of fine aggregates; 10-65 wt% of coarse aggregates; 2-25 wt% of water; and 0.1-5 wt% of an admixture, wherein the rapid-curing, ultra-high early strength cement-based binder is usually composed of 30-45 wt% of Portland cement clinker ground powder, 30-45 wt% of Wien-based rapid curing minerals, 10-20 wt% of rapid-curing cement, 0.1-2 wt% of gypsum, 2-10 wt% of slag powder, and 0.1-5 wt% of a latent heat material. According to the present invention, a problem of high costs of ultra-rapid-curing cement concrete can be addressed; a curing period thereof can be usually shortened compared to that of Portland cement concrete, early strength cement concrete and ultra-high early strength cement concrete; and durability will be enhanced to reduce costs for maintenance and improve constructability.
본 발명은, 속경성 초조강 시멘트계 결합재 5~40중량%, 잔골재 25~65중량%, 굵은골재 10~65중량%, 물 2~25중량%, 혼화제 0.1~5중량%를 포함하며, 상기 속경성 초조강 시멘트계 결합재는 보통 포틀랜드 시멘트 클링커 분쇄 분말 30~45중량%, 아윈계 속경성 광물 30~45중량%, 초속경 시멘트 10~20중량%, 석고 0.1~2중량%, 슬래그 미분말 2~10중량%, 잠열재 0.1~5중량%로 구성되는 속경성 초조강 콘크리트 조성물을 제조하는 방법과, 이를 이용한 포장 보수 공법에 관한 것이다. 본 발명에 의하면, 초속경 시멘트 콘크리트의 고비용을 해결하고 보통 포틀랜드 시멘트 콘크리트와 조강 시멘트 콘크리트, 초조강 시멘트 콘크리트보다 양생기간을 단축시키고, 내구성을 향상시켜 유지보수 비용 및 시공성 향상을 달성할 수 있다.
Fast Cementitious Cement Concrete Composition and Repair Method of Concrete Pavement Using the Same
속경성 초조강 시멘트 콘크리트 조성물 및 이를 이용한 콘크리트 포장 보수공법
WOO YANG YI (Autor:in) / PARK KEUN BAE (Autor:in) / KIM HYUN YU (Autor:in) / SHON YONG MIN (Autor:in)
09.11.2017
Patent
Elektronische Ressource
Koreanisch
| Europäisches Patentamt | 2015
| Europäisches Patentamt | 2018