HIGH-EARLY STRENGTH CEMENT CONCRETE COMPOSITION AND CONCRETE PAVEMENT REPAIR IT USING THE SAME METHOD USING SILICON SLUDGE
The present invention relates to a cement concrete composition using waste silicon sludge, a method of manufacturing the cement concrete composition, and a concrete pavement repairing method using the same. The cement concrete composition comprises: 3 to 40 wt% of a high-early strength cement binder; 20 to 75 wt% of a fine aggregate, 10 to 65 wt% of a coarse aggregate; 0.01 to 15 wt% of a performance improvement admixture; and 0.1 to 15 wt% of water, wherein the high-early strength cement binder includes: 20 to 90 wt% of ordinary Portland cement; 1 to 50 wt% of silicon waste sludge; 1 to 35 wt% of calcium alumina cement; 1 to 25 wt% of clinoptilolite; 1 to 15 wt% of anhydrous gypsum; 0.01 to 15 wt% of zinc sulfate; 0.01 to 15 wt% of magnesium sulfate; 0.01 to 10 wt% of lithium hydroxide; and 0.01 to 5 wt% of a water-reducing agent. According to the present invention, the cement concrete composition can improve strength and durability performance of concrete, and can be useful for recycling industrial waste by using the waste silicon sludge. Also, the cement concrete composition can be replaced with conventional high-early strength Portland cement, thereby reducing manufacturing costs thereof.
본 발명은 실리콘 폐슬러지를 이용한 시멘트 콘크리트 조성물과 이를 제조하는 방법 및 이를 이용한 콘크리트 포장 보수공법에 관한 것으로서, 조강형 시멘트 결합재 3~40중량%, 잔골재 20~75중량%, 굵은골재 10~65중량%, 성능 개선 혼화제 0.01~15 중량% 및 물 0.1~15중량%을 포함하여 이루어지고, 상기 조강형 시멘트 결합재는 보통 포틀랜드 시멘트 20∼90중량%, 실리콘 폐슬러지 1~50 중량%, 칼슘알루미나 시멘트 1~35 중량%, 클리노프틸로라이트(clinoptilolite) 1~25 중량%, 무수석고 1~15 중량%, 황산아연 0.01~15 중량%, 황산마그네슘 0.01~15 중량%, 리튬하이드록사이드 0.01~10 중량% 및 감수제 0.01~5중량%를 포함하여 이루어진다. 본 발명에 의하면, 콘크리트의 강도 및 내구성능을 개선할 수 있으며, 산업 폐기물인 재료를 사용함으로써 산업 폐기물의 재활용 측면에서 유용할 뿐만 아니라 기존 조강 포틀랜드 시멘트를 대체하여 사용할 수 있으므로 제조단가도 절감할 수 있는 효과가 있다.
HIGH-EARLY STRENGTH CEMENT CONCRETE COMPOSITION AND CONCRETE PAVEMENT REPAIR IT USING THE SAME METHOD USING SILICON SLUDGE
The present invention relates to a cement concrete composition using waste silicon sludge, a method of manufacturing the cement concrete composition, and a concrete pavement repairing method using the same. The cement concrete composition comprises: 3 to 40 wt% of a high-early strength cement binder; 20 to 75 wt% of a fine aggregate, 10 to 65 wt% of a coarse aggregate; 0.01 to 15 wt% of a performance improvement admixture; and 0.1 to 15 wt% of water, wherein the high-early strength cement binder includes: 20 to 90 wt% of ordinary Portland cement; 1 to 50 wt% of silicon waste sludge; 1 to 35 wt% of calcium alumina cement; 1 to 25 wt% of clinoptilolite; 1 to 15 wt% of anhydrous gypsum; 0.01 to 15 wt% of zinc sulfate; 0.01 to 15 wt% of magnesium sulfate; 0.01 to 10 wt% of lithium hydroxide; and 0.01 to 5 wt% of a water-reducing agent. According to the present invention, the cement concrete composition can improve strength and durability performance of concrete, and can be useful for recycling industrial waste by using the waste silicon sludge. Also, the cement concrete composition can be replaced with conventional high-early strength Portland cement, thereby reducing manufacturing costs thereof.
본 발명은 실리콘 폐슬러지를 이용한 시멘트 콘크리트 조성물과 이를 제조하는 방법 및 이를 이용한 콘크리트 포장 보수공법에 관한 것으로서, 조강형 시멘트 결합재 3~40중량%, 잔골재 20~75중량%, 굵은골재 10~65중량%, 성능 개선 혼화제 0.01~15 중량% 및 물 0.1~15중량%을 포함하여 이루어지고, 상기 조강형 시멘트 결합재는 보통 포틀랜드 시멘트 20∼90중량%, 실리콘 폐슬러지 1~50 중량%, 칼슘알루미나 시멘트 1~35 중량%, 클리노프틸로라이트(clinoptilolite) 1~25 중량%, 무수석고 1~15 중량%, 황산아연 0.01~15 중량%, 황산마그네슘 0.01~15 중량%, 리튬하이드록사이드 0.01~10 중량% 및 감수제 0.01~5중량%를 포함하여 이루어진다. 본 발명에 의하면, 콘크리트의 강도 및 내구성능을 개선할 수 있으며, 산업 폐기물인 재료를 사용함으로써 산업 폐기물의 재활용 측면에서 유용할 뿐만 아니라 기존 조강 포틀랜드 시멘트를 대체하여 사용할 수 있으므로 제조단가도 절감할 수 있는 효과가 있다.
HIGH-EARLY STRENGTH CEMENT CONCRETE COMPOSITION AND CONCRETE PAVEMENT REPAIR IT USING THE SAME METHOD USING SILICON SLUDGE
실리콘 폐슬러지를 이용한 시멘트 콘크리트 조성물 및 이를 이용한 콘크리트 포장 보수공법
PARK YOUNG JUN (Autor:in) / YEO WANG YEOP (Autor:in)
02.07.2015
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
Fast Cementitious Cement Concrete Composition and Repair Method of Concrete Pavement Using the Same
| Europäisches Patentamt | 2017
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2022