LIGHTWEIGHT REPAIR AGENT COMPOSITION FOR REPAIRING THE CONCRETE STRUCTURE AND REPAIRING METHOD OF THE CONCRETE STRUCTURE THEREWITH
The present invention relates to a lightweight mortar repair material composition for repairing a concrete structure and a repairing method of the concrete structure using the same. The lightweight mortar repair material composition for repairing a concrete structure includes: 5-75 wt% of a lightweight inorganic binder; 10-80 wt% of fine aggregate; 0.01-20 wt% of functional improvement agent; and 0.01-25 wt% of water. The lightweight inorganic binder includes: 10-85 wt% of crude Portland cement; 5-55 wt% of blast furnace slag powder; 5-30 wt% of hollow silica; 1-20 wt% of anhydrous gypsum; 0.1-20 wt% of volcanic ash; 0.1-15 wt% of tricalcium aluminate; 0.01-10 wt% of magnesite; 0.01-10 wt% of peat; 0.001-10 wt% of fibroferrite; and 0.001-10 wt% of retarder. The present invention has an effect of remarkably reducing maintenance costs by preventing concrete corrosion caused by chemical erosion in facilities such as an underground structure, a marine structure, a marine concrete structure, an underground concrete structure, a concrete structure in poor environment, and a sewer pipe by having excellent strength and durability, especially acid and salt resistance, by using an environmentally friendly lightweight inorganic binder having excellent acid and salt resistance and a functional improvement agent having excellent fluidity, toughness, adhesion, acid resistance, water resistance, and durability. The present invention provides excellent light weight, insulation, and strength and also provides excellent acid and salt resistance by using fine aggregate mixed with mica and silica having light weight, pozzolan characteristics, and far infrared effects.
본 발명은, 경량 무기계 결합재 5∼75중량%, 잔골재 10∼80중량%, 기능성 개선제 0.01∼20중량% 및 물 0.01∼25중량%를 포함하며, 경량 무기계 결합재는, 조강 포틀랜드 시멘트 10∼85중량%, 고로슬래그 분말 5∼55중량%, 중공형 실리카 5∼30중량%, 무수석고 1∼20중량%, 화산재 0.1∼20중량%, 트리칼슘알루미네이트 0.1∼15중량%, 마그네사이트 0.01∼10중량%, 이탄 또는 토탄(peat) 0.01∼10중량%, 피브로퍼라이트(Fibroferrite) 0.001~10중량% 및 지연제 0.001∼10중량%를 포함하는 것을 특징으로 하는 콘크리트 구조물 보수용 경량 모르타르 보수재 조성물 및 이를 이용한 콘크리트 구조물의 보수방법에 관한 것이다. 본 발명에 의하면, 내산 및 내염해성이 우수한 환경친화형 경량 무기계 결합재와 유동성, 인성, 접착력, 내산성, 내수성 및 내구성이 우수한 기능성 개선제 등을 사용함으로써 강도 및 내구성, 특히 내산 및 내염해성이 우수하여 지중구조물, 지수구조물, 해양콘크리트 구조물, 수중콘크리트 구조물, 열악한 환경하의 콘크리트 구조물, 하수관거 등의 화학적 침식으로 인한 콘크리트 부식을 방지할 수 있어 이에 사용되는 유지관리 비용을 현저히 절감할 수 있는 효과를 얻을 수 있다. 또한, 원적외선 효과, 포졸란 특성 및 경량인 실리카질 규사 및 운모가 혼입된 잔골재를 사용함으로써, 경량, 단열성 및 강도가 우수하고, 산성 및 염해 등에 대한 내구성이 우수하다.
LIGHTWEIGHT REPAIR AGENT COMPOSITION FOR REPAIRING THE CONCRETE STRUCTURE AND REPAIRING METHOD OF THE CONCRETE STRUCTURE THEREWITH
The present invention relates to a lightweight mortar repair material composition for repairing a concrete structure and a repairing method of the concrete structure using the same. The lightweight mortar repair material composition for repairing a concrete structure includes: 5-75 wt% of a lightweight inorganic binder; 10-80 wt% of fine aggregate; 0.01-20 wt% of functional improvement agent; and 0.01-25 wt% of water. The lightweight inorganic binder includes: 10-85 wt% of crude Portland cement; 5-55 wt% of blast furnace slag powder; 5-30 wt% of hollow silica; 1-20 wt% of anhydrous gypsum; 0.1-20 wt% of volcanic ash; 0.1-15 wt% of tricalcium aluminate; 0.01-10 wt% of magnesite; 0.01-10 wt% of peat; 0.001-10 wt% of fibroferrite; and 0.001-10 wt% of retarder. The present invention has an effect of remarkably reducing maintenance costs by preventing concrete corrosion caused by chemical erosion in facilities such as an underground structure, a marine structure, a marine concrete structure, an underground concrete structure, a concrete structure in poor environment, and a sewer pipe by having excellent strength and durability, especially acid and salt resistance, by using an environmentally friendly lightweight inorganic binder having excellent acid and salt resistance and a functional improvement agent having excellent fluidity, toughness, adhesion, acid resistance, water resistance, and durability. The present invention provides excellent light weight, insulation, and strength and also provides excellent acid and salt resistance by using fine aggregate mixed with mica and silica having light weight, pozzolan characteristics, and far infrared effects.
본 발명은, 경량 무기계 결합재 5∼75중량%, 잔골재 10∼80중량%, 기능성 개선제 0.01∼20중량% 및 물 0.01∼25중량%를 포함하며, 경량 무기계 결합재는, 조강 포틀랜드 시멘트 10∼85중량%, 고로슬래그 분말 5∼55중량%, 중공형 실리카 5∼30중량%, 무수석고 1∼20중량%, 화산재 0.1∼20중량%, 트리칼슘알루미네이트 0.1∼15중량%, 마그네사이트 0.01∼10중량%, 이탄 또는 토탄(peat) 0.01∼10중량%, 피브로퍼라이트(Fibroferrite) 0.001~10중량% 및 지연제 0.001∼10중량%를 포함하는 것을 특징으로 하는 콘크리트 구조물 보수용 경량 모르타르 보수재 조성물 및 이를 이용한 콘크리트 구조물의 보수방법에 관한 것이다. 본 발명에 의하면, 내산 및 내염해성이 우수한 환경친화형 경량 무기계 결합재와 유동성, 인성, 접착력, 내산성, 내수성 및 내구성이 우수한 기능성 개선제 등을 사용함으로써 강도 및 내구성, 특히 내산 및 내염해성이 우수하여 지중구조물, 지수구조물, 해양콘크리트 구조물, 수중콘크리트 구조물, 열악한 환경하의 콘크리트 구조물, 하수관거 등의 화학적 침식으로 인한 콘크리트 부식을 방지할 수 있어 이에 사용되는 유지관리 비용을 현저히 절감할 수 있는 효과를 얻을 수 있다. 또한, 원적외선 효과, 포졸란 특성 및 경량인 실리카질 규사 및 운모가 혼입된 잔골재를 사용함으로써, 경량, 단열성 및 강도가 우수하고, 산성 및 염해 등에 대한 내구성이 우수하다.
LIGHTWEIGHT REPAIR AGENT COMPOSITION FOR REPAIRING THE CONCRETE STRUCTURE AND REPAIRING METHOD OF THE CONCRETE STRUCTURE THEREWITH
콘크리트 구조물 보수용 경량 모르타르 보수재 조성물 및 이를 이용한 콘크리트 구조물의 보수방법
KANG IN DONG (Autor:in)
23.02.2018
Patent
Elektronische Ressource
Koreanisch
| Europäisches Patentamt | 2018
| Europäisches Patentamt | 2019
| Europäisches Patentamt | 2017
| Europäisches Patentamt | 2018
| Europäisches Patentamt | 2018