LIGHT-WEIGHTED MORTAR COMPOSITIONS FOR REPAIRING AND REPAIRING METHOD OF CONCRETE STRUCTURE THEREWITH
The present invention relates to lightweight mortar and a concrete repair method using the same. The object of the present invention is to provide lightweight mortar having rapid hardening, salt-resistance, and durability by mixing high-belite cement with attapulgite without addition of a methylcellulose thickener and a concrete repair method using the same. The lightweight mortar comprises: 30-40 wt% of high-belite cement; 1-5 wt% of attapulgite; 20-40 wt% of silica sand having a particle size of 2-1 mm; 10-30 wt% of silica sand having a particle size of 1-0.5 mm; 1-5 wt% of re-emulsification type powder resin; 0.1-1.0 wt% of defoamer; 1-5 wt% of siloxane-based rust inhibitor; and 0.1-1.0 wt% of polypropylene fiber. The high-belite cement (high belite sulphur aluminate cement, HB-SCA) is obtained by mixing and crushing bauxite, limestone, fly ash, and blast furnace slag in clinker fired at the temperature of 1,500-1,600 deg. C with phosphoric acid refinement type III beta-anhydrous gypsum. The lightweight mortar is used to repair concrete.
본 발명은 경량 모르타르와 이를 이용한 콘크리트 보수공법에 관한 것으로, 그 목적은 메틸셀룰로우스계 증점제의 첨가없이도 하이벨라이트 시멘트와 아타플자이트의 혼합에 의해 속경성, 내염성 및 내구성을 구비한 경량 모르타르와 이를 이용한 콘크리트 보수공법을 제공하는 것이다. 본 발명은 하이벨라이트 시멘트 30∼40wt%, 아타플자이트 1∼5wt%, 입경 2∼1㎜의 규사 20∼40wt%, 입경 1∼0.5㎜의 규사 10∼30wt%, 재유화형 분말수지 1∼5wt%, 소포제 0.1∼1.0wt%, 실록산계 방청제 1∼5wt%, 폴리프로필렌 파이버 0.1∼1.0wt% 를 포함하되, 상기 하이벨라이트 시멘트(High Belite Sulphur Aluminate Cement, HB-SCA)는 보오크사이트, 석회석, 플라이애쉬, 고로수쇄슬래그를 1,500∼1,600℃에서 소성한 클린커에, 인산정제 Ⅲ형 β무수석고가 혼합 분쇄된 경량 모르타르에 의해 콘크리트를 보수하도록 되어 있다.
LIGHT-WEIGHTED MORTAR COMPOSITIONS FOR REPAIRING AND REPAIRING METHOD OF CONCRETE STRUCTURE THEREWITH
The present invention relates to lightweight mortar and a concrete repair method using the same. The object of the present invention is to provide lightweight mortar having rapid hardening, salt-resistance, and durability by mixing high-belite cement with attapulgite without addition of a methylcellulose thickener and a concrete repair method using the same. The lightweight mortar comprises: 30-40 wt% of high-belite cement; 1-5 wt% of attapulgite; 20-40 wt% of silica sand having a particle size of 2-1 mm; 10-30 wt% of silica sand having a particle size of 1-0.5 mm; 1-5 wt% of re-emulsification type powder resin; 0.1-1.0 wt% of defoamer; 1-5 wt% of siloxane-based rust inhibitor; and 0.1-1.0 wt% of polypropylene fiber. The high-belite cement (high belite sulphur aluminate cement, HB-SCA) is obtained by mixing and crushing bauxite, limestone, fly ash, and blast furnace slag in clinker fired at the temperature of 1,500-1,600 deg. C with phosphoric acid refinement type III beta-anhydrous gypsum. The lightweight mortar is used to repair concrete.
본 발명은 경량 모르타르와 이를 이용한 콘크리트 보수공법에 관한 것으로, 그 목적은 메틸셀룰로우스계 증점제의 첨가없이도 하이벨라이트 시멘트와 아타플자이트의 혼합에 의해 속경성, 내염성 및 내구성을 구비한 경량 모르타르와 이를 이용한 콘크리트 보수공법을 제공하는 것이다. 본 발명은 하이벨라이트 시멘트 30∼40wt%, 아타플자이트 1∼5wt%, 입경 2∼1㎜의 규사 20∼40wt%, 입경 1∼0.5㎜의 규사 10∼30wt%, 재유화형 분말수지 1∼5wt%, 소포제 0.1∼1.0wt%, 실록산계 방청제 1∼5wt%, 폴리프로필렌 파이버 0.1∼1.0wt% 를 포함하되, 상기 하이벨라이트 시멘트(High Belite Sulphur Aluminate Cement, HB-SCA)는 보오크사이트, 석회석, 플라이애쉬, 고로수쇄슬래그를 1,500∼1,600℃에서 소성한 클린커에, 인산정제 Ⅲ형 β무수석고가 혼합 분쇄된 경량 모르타르에 의해 콘크리트를 보수하도록 되어 있다.
LIGHT-WEIGHTED MORTAR COMPOSITIONS FOR REPAIRING AND REPAIRING METHOD OF CONCRETE STRUCTURE THEREWITH
경량 모르타르와 이를 이용한 콘크리트 보수공법
KANG HO MAN (Autor:in) / KIM JUNG RAE (Autor:in) / KWON HYUN O (Autor:in)
23.05.2018
Patent
Elektronische Ressource
Koreanisch
| Europäisches Patentamt | 2016
| Europäisches Patentamt | 2018
| Europäisches Patentamt | 2017
| Europäisches Patentamt | 2018
Concrete structure repairing mortar and repairing method
| Europäisches Patentamt | 2018