CEMENT MORTAR COMPOSITION FOR REPAIRING CONCRETE STRUCTURE WITH IMPROVED DURABILITY AND REPAIRING METHOD OF CONCRETE STRUCTURE THEREWITH
The present invention relates to a cement mortar composition for repairing a concrete structure with enhanced durability, and a method of repairing a concrete structure using the same. The cement mortar composition for repairing a concrete structure with enhanced durability comprises: 3-75 wt% of a rapid hardening inorganic binder; 20-70 wt% of a fine aggregate; 1-35 wt% of a performance modifier; and 4-30 wt% of water. The rapid hardening inorganic binder comprises: 20-93 wt% of early strength type Portland cement; 1-20 wt% of tricalcium aluminate; 1-20 wt% of blast furnace slag fine powder having a powder degree of 3,000 to 8,500 cm^2/g; 1-20 wt% of magnesite; 1-10 wt% of hydroxycarbonate; 1-10 wt% of gypsum; and 1-10 wt% of aluminum powder. According to the present invention, a cement mortar composition is a rapid hardening type and exhibits high strength and excellent durability, thereby reducing a construction period, increasing the use period of a construction, and reducing costs on maintenance and repair work.
본 발명은, 속경형 무기 결합재 3∼75중량%, 잔골재 20∼70중량%, 성능 개질제 1∼35중량% 및 물 4~30중량%를 포함하며, 상기 속경형 무기 결합재는 조강 포틀랜드 시멘트 20∼93중량%, 트리칼슘알루미네이트 1∼20중량%, 분말도가 3,000~8,500 cm/g인 고로슬래그 미분말 1∼20중량%, 마그네사이트 1~20중량%, 하이드록시탄산마그네슘 1∼10중량%, 석고 1∼10중량%, 및 알루미늄 분말 1~10중량%를 포함하는 것을 특징으로 하는 내구성능이 개선된 콘크리트 구조물 보수용 시멘트 모르타르 조성물 및 이를 이용한 콘크리트 구조물 유지 보수 방법에 관한 것이다. 본 발명에 의하면, 속경형이고 높은 강도 및 우수한 내구성을 나타냄으로써, 시공기간을 단축하고, 구조물의 사용기간을 증가시킬 수 있을 뿐만 아니라 유지보수에 소요되는 비용을 절감할 수 있다.
CEMENT MORTAR COMPOSITION FOR REPAIRING CONCRETE STRUCTURE WITH IMPROVED DURABILITY AND REPAIRING METHOD OF CONCRETE STRUCTURE THEREWITH
The present invention relates to a cement mortar composition for repairing a concrete structure with enhanced durability, and a method of repairing a concrete structure using the same. The cement mortar composition for repairing a concrete structure with enhanced durability comprises: 3-75 wt% of a rapid hardening inorganic binder; 20-70 wt% of a fine aggregate; 1-35 wt% of a performance modifier; and 4-30 wt% of water. The rapid hardening inorganic binder comprises: 20-93 wt% of early strength type Portland cement; 1-20 wt% of tricalcium aluminate; 1-20 wt% of blast furnace slag fine powder having a powder degree of 3,000 to 8,500 cm^2/g; 1-20 wt% of magnesite; 1-10 wt% of hydroxycarbonate; 1-10 wt% of gypsum; and 1-10 wt% of aluminum powder. According to the present invention, a cement mortar composition is a rapid hardening type and exhibits high strength and excellent durability, thereby reducing a construction period, increasing the use period of a construction, and reducing costs on maintenance and repair work.
본 발명은, 속경형 무기 결합재 3∼75중량%, 잔골재 20∼70중량%, 성능 개질제 1∼35중량% 및 물 4~30중량%를 포함하며, 상기 속경형 무기 결합재는 조강 포틀랜드 시멘트 20∼93중량%, 트리칼슘알루미네이트 1∼20중량%, 분말도가 3,000~8,500 cm/g인 고로슬래그 미분말 1∼20중량%, 마그네사이트 1~20중량%, 하이드록시탄산마그네슘 1∼10중량%, 석고 1∼10중량%, 및 알루미늄 분말 1~10중량%를 포함하는 것을 특징으로 하는 내구성능이 개선된 콘크리트 구조물 보수용 시멘트 모르타르 조성물 및 이를 이용한 콘크리트 구조물 유지 보수 방법에 관한 것이다. 본 발명에 의하면, 속경형이고 높은 강도 및 우수한 내구성을 나타냄으로써, 시공기간을 단축하고, 구조물의 사용기간을 증가시킬 수 있을 뿐만 아니라 유지보수에 소요되는 비용을 절감할 수 있다.
CEMENT MORTAR COMPOSITION FOR REPAIRING CONCRETE STRUCTURE WITH IMPROVED DURABILITY AND REPAIRING METHOD OF CONCRETE STRUCTURE THEREWITH
내구성능이 개선된 콘크리트 구조물 보수용 시멘트 모르타르 조성물 및 이를 이용한 콘크리트 구조물 유지 보수 방법
WON YONG DAE (Autor:in)
03.07.2018
Patent
Elektronische Ressource
Koreanisch
| Europäisches Patentamt | 2018
| Europäisches Patentamt | 2018
| Europäisches Patentamt | 2018
| Europäisches Patentamt | 2018
| Europäisches Patentamt | 2017