SIS SEBS Asphalt Waterproofing Agent Composition Comprising Styrene Isoprene Styrene Styrene Ethylene Butylene Styrene and Aggregate-powder of Improved Grain Size and Constructing Methods Using Thereof
The present invention relates to an asphalt waterproofing agent composition containing, based on 100 parts by weight of asphalt: 1 to 25 parts by weight of styrene isoprene styrene; 1 to 25 parts by weight of a styrene ethylene butylene styrene copolymer; 1 to 25 parts by weight of a petroleum resin; 500 to 2,000 parts by weight of aggregate; 30 to 150 parts by weight of aggregate powder; 0.1 to 2 parts by weight of cellulose fiber; 0.1 to 2 parts by weight of wax; and 0.1 to 2 parts by weight of an antioxidant. The asphalt waterproofing agent composition according to the present invention, the asphalt waterproofing agent composition comprising SIS, SEBS, and aggregate powder of improved grain size to be specific, is highly permeable in relation to, for example, micro-cracks and capillary pores in surfaces where a waterproofing agent is to be applied, examples of which include roads, bridges, bridge surfaces, and asphalt concrete structures. As a result, it is possible to form an additional protective film by applying the waterproofing agent composition. In addition, firm bonding can be performed on the interface between a waterproofing agent and an asphalt concrete bridge surface prone to be damaged by external load, impact, or the like, resistance to infiltrating water can be improved, and the durability of the asphalt concrete bridge surface can be significantly improved as a result.
본 발명은 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 1 내지 25중량부; 스티렌에틸렌부틸렌스티렌 공중합체 1 내지 25중량부; 석유수지 1 내지 25중량부; 골재 500 내지 2,000중량부; 미분말 골재 30 내지 150중량부; 셀룰로오스 섬유 0.1 내지 2중량부; 왁스 0.1 내지 2중량부; 및 산화방지제 0.1 내지 2중량부를 포함하는 아스팔트 도막 방수제 조성물에 관한 것이다. 본 발명에 따른 아스팔트 도막 방수제 조성물, 특정적으로 SIS, SEBS 및 개선된 골재 입도의 미분말 골재를 포함하는 아스팔트 도막 방수제 조성물은 도막 방수제를 적용하고자 하는 표면, 예를 들면 도로, 교량, 교면, 아스팔트 콘크리트 구조물의 미세균열 및 모세관 공극 등에의 침투성능이 우수한 도막 방수제 조성물을 적용함으로써, 추가적 보호막을 형성할 수 있고, 외부하중이나 충격 등으로 손상받기 쉬운 아스팔트 콘크리트 교면과 방수제 계면의 결합을 공고히 할 수 있을 뿐만 아니라 내투수 저항성을 향상시킬 수 있어 아스팔트 콘크리트 교면의 내구성을 대폭 향상시킬 수 있다.
SIS SEBS Asphalt Waterproofing Agent Composition Comprising Styrene Isoprene Styrene Styrene Ethylene Butylene Styrene and Aggregate-powder of Improved Grain Size and Constructing Methods Using Thereof
The present invention relates to an asphalt waterproofing agent composition containing, based on 100 parts by weight of asphalt: 1 to 25 parts by weight of styrene isoprene styrene; 1 to 25 parts by weight of a styrene ethylene butylene styrene copolymer; 1 to 25 parts by weight of a petroleum resin; 500 to 2,000 parts by weight of aggregate; 30 to 150 parts by weight of aggregate powder; 0.1 to 2 parts by weight of cellulose fiber; 0.1 to 2 parts by weight of wax; and 0.1 to 2 parts by weight of an antioxidant. The asphalt waterproofing agent composition according to the present invention, the asphalt waterproofing agent composition comprising SIS, SEBS, and aggregate powder of improved grain size to be specific, is highly permeable in relation to, for example, micro-cracks and capillary pores in surfaces where a waterproofing agent is to be applied, examples of which include roads, bridges, bridge surfaces, and asphalt concrete structures. As a result, it is possible to form an additional protective film by applying the waterproofing agent composition. In addition, firm bonding can be performed on the interface between a waterproofing agent and an asphalt concrete bridge surface prone to be damaged by external load, impact, or the like, resistance to infiltrating water can be improved, and the durability of the asphalt concrete bridge surface can be significantly improved as a result.
본 발명은 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 1 내지 25중량부; 스티렌에틸렌부틸렌스티렌 공중합체 1 내지 25중량부; 석유수지 1 내지 25중량부; 골재 500 내지 2,000중량부; 미분말 골재 30 내지 150중량부; 셀룰로오스 섬유 0.1 내지 2중량부; 왁스 0.1 내지 2중량부; 및 산화방지제 0.1 내지 2중량부를 포함하는 아스팔트 도막 방수제 조성물에 관한 것이다. 본 발명에 따른 아스팔트 도막 방수제 조성물, 특정적으로 SIS, SEBS 및 개선된 골재 입도의 미분말 골재를 포함하는 아스팔트 도막 방수제 조성물은 도막 방수제를 적용하고자 하는 표면, 예를 들면 도로, 교량, 교면, 아스팔트 콘크리트 구조물의 미세균열 및 모세관 공극 등에의 침투성능이 우수한 도막 방수제 조성물을 적용함으로써, 추가적 보호막을 형성할 수 있고, 외부하중이나 충격 등으로 손상받기 쉬운 아스팔트 콘크리트 교면과 방수제 계면의 결합을 공고히 할 수 있을 뿐만 아니라 내투수 저항성을 향상시킬 수 있어 아스팔트 콘크리트 교면의 내구성을 대폭 향상시킬 수 있다.
SIS SEBS Asphalt Waterproofing Agent Composition Comprising Styrene Isoprene Styrene Styrene Ethylene Butylene Styrene and Aggregate-powder of Improved Grain Size and Constructing Methods Using Thereof
SIS, SEBS 및 개선된 골재 입도의 미분말 골재를 포함하는 아스팔트 도막 방수제 조성물 및 이의 시공방법