The present invention relates to a method for manufacturing a building material using food waste to increase safety in case of fire. According to the present invention, the method comprises the following steps: a) putting collected food waste and water into a storage tank and washing the food waste; b) putting the washed food waste in a box-type dryer and primarily drying the same at a temperature of 100 to 200°C for 0.5 to 1.5 hours; c) pulverizing the primarily dried food waste at a grinding speed of 100 to 300 rpm for 20 to 40 minutes; d) mixing the pulverized food waste with 1 to 3 kg of cement powder, 50 to 150 kg of red clay powder, 0.5 to 1.5 kg of a woodworking adhesive with respect to 500 kg of the pulverized food waste; e) putting the mixture into a compression means and molding the same into a predetermined shape; f) secondarily drying the molded product outdoors for 8 to 12 hours through natural drying; g) drying the secondarily dried molded product for the third time in a conveyor dryer at a temperature of 100 to 200°C for 0.5 to 1.5 hours; and h) drying the dried molded product for the fourth time in a conveyor dryer at a temperature of 300 to 400°C for 20 to 60 minutes.
본 발명은 음식물 쓰레기를 이용한 건축자재 제조방법에 관한 것이다.본 발명에 따른 음식물 쓰레기를 이용한 건축자재 제조방법은, a) 수거된 음식물 쓰레기를 저장조에 넣고, 이 저장조에 물을 투입하여 세척하는 단계; b) 세척된 음식물 쓰레기를 박스형 건조기에 넣고 100~200℃ 온도에서 30분~1시간 30분 동안 1차 건조시키는 단계; c) 1차 건조된 음식물 쓰레기를 분당 100~300 rpm의 분쇄속도로서, 20분~40분 동안 분쇄하는 단계; d) 분쇄된 음식물 쓰레기 500 ㎏을 기준으로 하여 부재료인 시멘트 가루 : 1~3 ㎏, 황토가루 : 50~150 ㎏, 목공용 접착제 : 0.5~1.5 ㎏을 분쇄된 음식물 쓰레기에 혼합하는 단계; e) 혼합물을 압축수단에 넣고 일정한 형태로 성형하는 단계; f) 성형품을 야외에서 8~12시간 동안 자연건조를 통해 2차 건조시키는 단계; g) 2차 건조된 성형품을 컨베이어(conveyor)건조기에서 100~200℃ 온도에서 30 ~ 1시간 30분 동안 3차 건조시키는 단계; h) 3차 건조된 성형품을 컨베이어 건조기에서 300~400℃ 온도에서 20 ~ 60분 동안 4차 건조시키는 단계로 이루어지는 것을 특징으로 한다.
The present invention relates to a method for manufacturing a building material using food waste to increase safety in case of fire. According to the present invention, the method comprises the following steps: a) putting collected food waste and water into a storage tank and washing the food waste; b) putting the washed food waste in a box-type dryer and primarily drying the same at a temperature of 100 to 200°C for 0.5 to 1.5 hours; c) pulverizing the primarily dried food waste at a grinding speed of 100 to 300 rpm for 20 to 40 minutes; d) mixing the pulverized food waste with 1 to 3 kg of cement powder, 50 to 150 kg of red clay powder, 0.5 to 1.5 kg of a woodworking adhesive with respect to 500 kg of the pulverized food waste; e) putting the mixture into a compression means and molding the same into a predetermined shape; f) secondarily drying the molded product outdoors for 8 to 12 hours through natural drying; g) drying the secondarily dried molded product for the third time in a conveyor dryer at a temperature of 100 to 200°C for 0.5 to 1.5 hours; and h) drying the dried molded product for the fourth time in a conveyor dryer at a temperature of 300 to 400°C for 20 to 60 minutes.
본 발명은 음식물 쓰레기를 이용한 건축자재 제조방법에 관한 것이다.본 발명에 따른 음식물 쓰레기를 이용한 건축자재 제조방법은, a) 수거된 음식물 쓰레기를 저장조에 넣고, 이 저장조에 물을 투입하여 세척하는 단계; b) 세척된 음식물 쓰레기를 박스형 건조기에 넣고 100~200℃ 온도에서 30분~1시간 30분 동안 1차 건조시키는 단계; c) 1차 건조된 음식물 쓰레기를 분당 100~300 rpm의 분쇄속도로서, 20분~40분 동안 분쇄하는 단계; d) 분쇄된 음식물 쓰레기 500 ㎏을 기준으로 하여 부재료인 시멘트 가루 : 1~3 ㎏, 황토가루 : 50~150 ㎏, 목공용 접착제 : 0.5~1.5 ㎏을 분쇄된 음식물 쓰레기에 혼합하는 단계; e) 혼합물을 압축수단에 넣고 일정한 형태로 성형하는 단계; f) 성형품을 야외에서 8~12시간 동안 자연건조를 통해 2차 건조시키는 단계; g) 2차 건조된 성형품을 컨베이어(conveyor)건조기에서 100~200℃ 온도에서 30 ~ 1시간 30분 동안 3차 건조시키는 단계; h) 3차 건조된 성형품을 컨베이어 건조기에서 300~400℃ 온도에서 20 ~ 60분 동안 4차 건조시키는 단계로 이루어지는 것을 특징으로 한다.
Manufacturing method of building material by using food waste
음식물 쓰레기를 이용한 건축자재 제조방법
NA JIN OK (Autor:in)
29.03.2021
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
/
B09B
DISPOSAL OF SOLID WASTE
,
Beseitigung von festem Abfall
/
B28B
Formgeben von Ton oder anderen keramischen Stoffzusammensetzungen, Schlacke oder von Mischungen, die zementartiges Material enthalten, z.B. Putzmörtel
,
SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS, SLAG OR MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
METHOD FOR MANUFACTURING BUILDING MATERIAL USING FOOD WASTE
| Europäisches Patentamt | 2021
Method for manufacturing building material by using building solid waste
| Europäisches Patentamt | 2021
Manufacturing method of building material using stone waste
| Europäisches Patentamt | 2018
Manufacturing method of building material using stone waste
| Europäisches Patentamt | 2018
Europäisches Patentamt | 2021