ECO-FRIENDLY FINISHING COMPOSITION FOR PROTECTING SURFACE OF CONCRETE STRUCTURE AND FINISHING METHOD FOR SURFACE OF CONCRETE STRUCTURE USING THE SAME
The present invention relates to an eco-friendly surface finishing material composition for surface protection of a concrete structure. The eco-friendly surface finishing material composition for surface protection of a structure contains 35 to 85 wt% of a lithium-potassium silicate aqueous solution, 5 to 35 wt% of a sodium-magnesium silicate aqueous solution, 1 to 30 wt% of N-(aminoethyl-3-aminopropyl)trimethoxysilane, 1 to 30% by weight of hydrophobic silica sol, 0.01 to 10% by weight of hollow magnesium fluoride particles, 0.01 to 10% by weight of polypropyl acrylate, and 0.01 to 10% by weight of polyethyl methacrylate. The present invention can improve the strength and durability of a concrete structure.
본 발명은 콘크리트 구조물의 표면보호용 친환경 표면마감재 조성물에 관한 것으로서, 리튬-포타슘 실리케이트 수용액 35 내지 85 중량%, 소듐-마그네슘 실리케이트 수용액 5 내지 35 중량%, N-(아미노에틸-3-아미노프로필)트리메톡시실란 1 내지 30 중량%, 소수성 실리카졸 1 내지 30 중량%, 중공형 불화마그네슘 입자 0.01 내지 10 중량%, 폴리프로필아크릴레이트 0.01 내지 10 중량% 및 폴리에틸메타크릴레이트 0.01 내지 10 중량%를 포함하는 것이고; 상기 소수성 실리카졸은 규산염 100 중량부에 대하여, 증류수 80 내지 150 중량부, 황산마그네슘 1 내지 15 중량부 및 황산용액 0.5 내지 5 중량부를 고속 회전반응기에 투입하고 혼합하는 단계; 이와는 별도로, 헥사메틸디실라잔, 수화된 헥사메틸디실라잔, 테트라메틸디실라잔 및 이들의 혼합물로 이루어진 군에서 선택되는 1종 이상의 소수성 개질제 0.5 내지 10 중량부, 및 에탄올, 이소프로필알코올, 메탄올, 부탄올 및 이들의 혼합물로 이루어진 군에서 선택되는 1종 이상의 알코올계 용매 70 내지 80 중량부를 포함하는 소수성 개질 혼합물을 제조하는 단계; 및 상기 고속 회전반응기에 소수성 개질 혼합물을 추가하는 단계를 포함하는 방법으로 준비되는 것을 사용하여; 큰 침투깊이로 열화인자를 효과적으로 차단할 수 있고; 콘크리트 구조물의 강도와, 내구성을 향상시킬 수 있으며; 인체에 유해한 유기용매 및 중금속의 용출이 없어 개선된 시공환경 및 친환경성을 제공할 수 있는 콘크리트 구조물의 표면보호용 친환경 표면마감재 조성물 및 이를 이용한 콘크리트 구조물의 표면마감 시공방법에 관한 것이다.
ECO-FRIENDLY FINISHING COMPOSITION FOR PROTECTING SURFACE OF CONCRETE STRUCTURE AND FINISHING METHOD FOR SURFACE OF CONCRETE STRUCTURE USING THE SAME
The present invention relates to an eco-friendly surface finishing material composition for surface protection of a concrete structure. The eco-friendly surface finishing material composition for surface protection of a structure contains 35 to 85 wt% of a lithium-potassium silicate aqueous solution, 5 to 35 wt% of a sodium-magnesium silicate aqueous solution, 1 to 30 wt% of N-(aminoethyl-3-aminopropyl)trimethoxysilane, 1 to 30% by weight of hydrophobic silica sol, 0.01 to 10% by weight of hollow magnesium fluoride particles, 0.01 to 10% by weight of polypropyl acrylate, and 0.01 to 10% by weight of polyethyl methacrylate. The present invention can improve the strength and durability of a concrete structure.
본 발명은 콘크리트 구조물의 표면보호용 친환경 표면마감재 조성물에 관한 것으로서, 리튬-포타슘 실리케이트 수용액 35 내지 85 중량%, 소듐-마그네슘 실리케이트 수용액 5 내지 35 중량%, N-(아미노에틸-3-아미노프로필)트리메톡시실란 1 내지 30 중량%, 소수성 실리카졸 1 내지 30 중량%, 중공형 불화마그네슘 입자 0.01 내지 10 중량%, 폴리프로필아크릴레이트 0.01 내지 10 중량% 및 폴리에틸메타크릴레이트 0.01 내지 10 중량%를 포함하는 것이고; 상기 소수성 실리카졸은 규산염 100 중량부에 대하여, 증류수 80 내지 150 중량부, 황산마그네슘 1 내지 15 중량부 및 황산용액 0.5 내지 5 중량부를 고속 회전반응기에 투입하고 혼합하는 단계; 이와는 별도로, 헥사메틸디실라잔, 수화된 헥사메틸디실라잔, 테트라메틸디실라잔 및 이들의 혼합물로 이루어진 군에서 선택되는 1종 이상의 소수성 개질제 0.5 내지 10 중량부, 및 에탄올, 이소프로필알코올, 메탄올, 부탄올 및 이들의 혼합물로 이루어진 군에서 선택되는 1종 이상의 알코올계 용매 70 내지 80 중량부를 포함하는 소수성 개질 혼합물을 제조하는 단계; 및 상기 고속 회전반응기에 소수성 개질 혼합물을 추가하는 단계를 포함하는 방법으로 준비되는 것을 사용하여; 큰 침투깊이로 열화인자를 효과적으로 차단할 수 있고; 콘크리트 구조물의 강도와, 내구성을 향상시킬 수 있으며; 인체에 유해한 유기용매 및 중금속의 용출이 없어 개선된 시공환경 및 친환경성을 제공할 수 있는 콘크리트 구조물의 표면보호용 친환경 표면마감재 조성물 및 이를 이용한 콘크리트 구조물의 표면마감 시공방법에 관한 것이다.
ECO-FRIENDLY FINISHING COMPOSITION FOR PROTECTING SURFACE OF CONCRETE STRUCTURE AND FINISHING METHOD FOR SURFACE OF CONCRETE STRUCTURE USING THE SAME
콘크리트 구조물의 표면보호용 친환경 표면마감재 조성물 및 이를 이용한 콘크리트 구조물의 표면마감 시공방법
KIM YOUNG WOON (Autor:in)
20.05.2021
Patent
Elektronische Ressource
Koreanisch
| Europäisches Patentamt | 2017
| Europäisches Patentamt | 2019
| Europäisches Patentamt | 2017
| Europäisches Patentamt | 2018