SIS SBS Joint Injection Compositions for Concrete of Road Having Stylene Isoprene Stylene Stylene Butadien Stylene and Petroleum Resin Added Hydrogen and Constructing Methods Using Thereof
The present invention provides a joint injection material composition for a concrete road. With reference to 100 parts by weight of asphalt, the composition comprises: 5 to 50 parts by weight of styrene isoprene styrene; 1 to 20 parts by weight of styrene butadiene styrene; 5 to 30 parts by weight of hydrogenated petroleum resin; 3 to 10 parts by weight of low density polyethylene; 2 to 8 parts by weight of vegetable oil; 5 to 15 parts by weight of waste tire powder; 1 to 5 parts by weight of a mesophilic additive; 1 to 3 parts by weight of a rubber anti-aging agent; 0.1 to 2 parts by weight of slaked lime; and 0.1 to 2 parts by weight of a stabilizer. In a joint injection material composition for concrete roads according to the present invention, specifically, a joint injection material composition for concrete roads comprising SIS, SBS and hydrogenated petroleum resin, because the tensile strength and elongation are excellent, it is possible to prevent the concrete road from being stretched or contracted in length by heat, so that the length thereof is slightly changed according to changes in ambient temperature.
본 발명은 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 5 내지 50중량부; 스티렌부타디엔스티렌 1 내지 20중량부; 수소가 첨가된 석유수지 5 내지 30중량부; 저밀도 폴리에틸렌 3 내지 10중량부; 식물성 오일 2 내지 8중량부; 폐타이어 분말 5 내지 15중량부; 중온화 첨가제 1 내지 5중량부; 고무노화방지제 1 내지 3중량부; 소석회 0.1 내지 2중량부; 및 안정제 0.1 내지 2중량부를 포함하는 콘크리트 도로용 줄눈 주입재 조성물을 제공한다. 본 발명에 따른 콘크리트 도로용 줄눈 주입재 조성물, 특정적으로 SIS, SBS 및 수소가 첨가된 석유수지를 포함하는 콘크리트 도로용 줄눈 주입재 조성물은 인장강도 및 신률이 우수하여 콘크리트 도로가 열에 의해 길이가 신장 또는 수축됨으로써, 주위 기온의 변화에 따라 미세하게 그 길이가 변화되는 것을 방지할 수 있다.
SIS SBS Joint Injection Compositions for Concrete of Road Having Stylene Isoprene Stylene Stylene Butadien Stylene and Petroleum Resin Added Hydrogen and Constructing Methods Using Thereof
The present invention provides a joint injection material composition for a concrete road. With reference to 100 parts by weight of asphalt, the composition comprises: 5 to 50 parts by weight of styrene isoprene styrene; 1 to 20 parts by weight of styrene butadiene styrene; 5 to 30 parts by weight of hydrogenated petroleum resin; 3 to 10 parts by weight of low density polyethylene; 2 to 8 parts by weight of vegetable oil; 5 to 15 parts by weight of waste tire powder; 1 to 5 parts by weight of a mesophilic additive; 1 to 3 parts by weight of a rubber anti-aging agent; 0.1 to 2 parts by weight of slaked lime; and 0.1 to 2 parts by weight of a stabilizer. In a joint injection material composition for concrete roads according to the present invention, specifically, a joint injection material composition for concrete roads comprising SIS, SBS and hydrogenated petroleum resin, because the tensile strength and elongation are excellent, it is possible to prevent the concrete road from being stretched or contracted in length by heat, so that the length thereof is slightly changed according to changes in ambient temperature.
본 발명은 아스팔트 100중량부 기준으로, 스티렌이소프렌스티렌 5 내지 50중량부; 스티렌부타디엔스티렌 1 내지 20중량부; 수소가 첨가된 석유수지 5 내지 30중량부; 저밀도 폴리에틸렌 3 내지 10중량부; 식물성 오일 2 내지 8중량부; 폐타이어 분말 5 내지 15중량부; 중온화 첨가제 1 내지 5중량부; 고무노화방지제 1 내지 3중량부; 소석회 0.1 내지 2중량부; 및 안정제 0.1 내지 2중량부를 포함하는 콘크리트 도로용 줄눈 주입재 조성물을 제공한다. 본 발명에 따른 콘크리트 도로용 줄눈 주입재 조성물, 특정적으로 SIS, SBS 및 수소가 첨가된 석유수지를 포함하는 콘크리트 도로용 줄눈 주입재 조성물은 인장강도 및 신률이 우수하여 콘크리트 도로가 열에 의해 길이가 신장 또는 수축됨으로써, 주위 기온의 변화에 따라 미세하게 그 길이가 변화되는 것을 방지할 수 있다.
SIS SBS Joint Injection Compositions for Concrete of Road Having Stylene Isoprene Stylene Stylene Butadien Stylene and Petroleum Resin Added Hydrogen and Constructing Methods Using Thereof
SIS, SBS 및 수소가 첨가된 석유수지를 포함하는 콘크리트 도로용 줄눈 주입재 조성물 및 이를 이용한 시공방법
KIM MIN JUN (Autor:in)
01.06.2021
Patent
Elektronische Ressource
Koreanisch