SBS Middle Temperature Modified-Asphalt Concrete Compositions Using Stylene Butadien Stylene and Constructing Methods Using Thereof
The present invention relates to a medium temperature modified asphalt concrete composition and a constructing method thereof, wherein the medium temperature modified asphalt concrete composition comprises, based on 100 parts by weight of asphalt, 1 to 30 parts by weight of styrene butadiene styrene; 1 to 30 parts by weight of petroleum resin; 800 to 1,500 parts by weight of aggregate; 0.1 to 10 parts by weight of performance improver; 0.1 to 5 parts by weight of nanoceramic particles; 0.1 to 2 parts by weight of cellulose fiber; 0.5 to 5 parts by weight of mesophilic additive; 0.1 to 5 parts by weight of commercial agent; and 0.1 to 2 parts by weight of antioxidant. The medium temperature modified asphalt concrete composition according to the present invention, and more particularly the medium temperature modified asphalt concrete composition comprises SBS, is durable, not prone to plastic deformation, aging and/or delamination, and facilitates the pouring process at a low cost, as well as allowing for pouring and/or placing at medium temperatures, which are lower temperatures than conventional asphalt concrete compositions.
본 발명은 아스팔트 100중량부 기준으로, 스티렌부타디엔스티렌 1 내지 30중량부; 석유수지 1 내지 30중량부; 골재 800 내지 1,500중량부; 성능개선제 0.1 내지 10중량부; 나노세라믹 입자 0.1 내지 5중량부; 셀룰로오스 섬유 0.1 내지 2중량부; 중온 첨가제 0.5 내지 5중량부; 상용화제 0.1 내지 5중량부; 및 산화방지제 0.1 내지 2중량부를 포함하는 중온 개질아스팔트 콘크리트 조성물 및 이의 시공방법에 관한 것이다. 본 발명에 따른 중온 개질아스팔트 콘크리트 조성물, 특정적으로 SBS를 포함하는 중온 개질아스팔트 콘크리트 조성물은 내구성이 좋고, 소성변형, 노화 및/또는 박리가 쉽게 발생하지 않으면서도, 저비용으로 타설공정을 용이하게 수행할 수 있을 뿐만 아니라, 일반 아스팔트 콘크리트 조성물 보다 낮은 온도인 중온에서 타설 및/또는 포설이 가능하도록 하는 등의 효과가 있다.
SBS Middle Temperature Modified-Asphalt Concrete Compositions Using Stylene Butadien Stylene and Constructing Methods Using Thereof
The present invention relates to a medium temperature modified asphalt concrete composition and a constructing method thereof, wherein the medium temperature modified asphalt concrete composition comprises, based on 100 parts by weight of asphalt, 1 to 30 parts by weight of styrene butadiene styrene; 1 to 30 parts by weight of petroleum resin; 800 to 1,500 parts by weight of aggregate; 0.1 to 10 parts by weight of performance improver; 0.1 to 5 parts by weight of nanoceramic particles; 0.1 to 2 parts by weight of cellulose fiber; 0.5 to 5 parts by weight of mesophilic additive; 0.1 to 5 parts by weight of commercial agent; and 0.1 to 2 parts by weight of antioxidant. The medium temperature modified asphalt concrete composition according to the present invention, and more particularly the medium temperature modified asphalt concrete composition comprises SBS, is durable, not prone to plastic deformation, aging and/or delamination, and facilitates the pouring process at a low cost, as well as allowing for pouring and/or placing at medium temperatures, which are lower temperatures than conventional asphalt concrete compositions.
본 발명은 아스팔트 100중량부 기준으로, 스티렌부타디엔스티렌 1 내지 30중량부; 석유수지 1 내지 30중량부; 골재 800 내지 1,500중량부; 성능개선제 0.1 내지 10중량부; 나노세라믹 입자 0.1 내지 5중량부; 셀룰로오스 섬유 0.1 내지 2중량부; 중온 첨가제 0.5 내지 5중량부; 상용화제 0.1 내지 5중량부; 및 산화방지제 0.1 내지 2중량부를 포함하는 중온 개질아스팔트 콘크리트 조성물 및 이의 시공방법에 관한 것이다. 본 발명에 따른 중온 개질아스팔트 콘크리트 조성물, 특정적으로 SBS를 포함하는 중온 개질아스팔트 콘크리트 조성물은 내구성이 좋고, 소성변형, 노화 및/또는 박리가 쉽게 발생하지 않으면서도, 저비용으로 타설공정을 용이하게 수행할 수 있을 뿐만 아니라, 일반 아스팔트 콘크리트 조성물 보다 낮은 온도인 중온에서 타설 및/또는 포설이 가능하도록 하는 등의 효과가 있다.
SBS Middle Temperature Modified-Asphalt Concrete Compositions Using Stylene Butadien Stylene and Constructing Methods Using Thereof
SBS를 포함하는 중온 개질아스팔트 콘크리트 조성물및 이를 이용한 시공방법
KIM DONG JIN (Autor:in)
08.01.2024
Patent
Elektronische Ressource
Koreanisch