- Manufacturing method of the zirconia-alumina composite

CHOI WOO HYUK / SON JAE YONG / KANG SOK WON / JUNG SUNG MO

The present invention relates to a preparation method of zirconia-alumina composite, which comprises the steps of: introducing raw materials including zirconia powder and alumina powder and balls into a reaction container; injecting nitrogen gas into the reaction container and sealing the container; loading the reaction container containing the raw materials and the balls into a high-energy mill and performing high-energy milling to obtain a nitrogen-doped mixed powder; molding the nitrogen-doped mixed powder; and sintering the molded product. According to the present invention, sintering can be performed at low temperatures and specific resistance can be lowered. In addition, the zirconia-alumina composite of the present invention has excellent mechanical properties such as strength, hardness, toughness, and wear resistance.

본 발명은, 지르코니아 분말과 알루미나 분말을 포함하는 원료와 볼(ball)을 반응용기에 투입하는 단계와, 상기 반응용기에 질소 가스를 주입하고 밀봉하는 단계와, 상기 원료와 상기 볼이 담긴 반응용기를 고에너지 밀링기에 장입하고 고에너지 밀링하여 질소가 도핑된 혼합분말을 수득하는 단계와, 상기 질소가 도핑된 혼합분말을 성형하는 단계 및 성형된 결과물을 소결하는 단계를 포함하는 지르코니아-알루미나 복합체의 제조방법에 관한 것이다. 본 발명에 의하면, 저온에서 소결이 가능하고, 비저항을 낮출 수 있으며, 강도, 경도, 인성, 내마모성 등의 기계적 특성이 우수하다.

Zugriff

Download

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren