CARBON BLOCK GRAPHITE BLOCK HAVING HIGH THERMAL CONDUCTIVITY MANUFACTURED THEREFROM AND MANUFACTURING METHODS FOR THE SAME
The present invention relates to a carbon block, a graphite block having high thermal conductivity manufactured therefrom, and a manufacturing method for the same. According to one embodiment, a manufacturing method of a carbon block can be provided, wherein the method comprises: a step a) of mixing graphite powders and a binder pitch, grinding and classifying the same to provide mixed powders; a step b) of putting the prepared mixed powders into a mold and pressurizing the same to provide a molded body; and a step c) of carbonizing the prepared molded body to provide a carbon block. A softening point of the binder pitch ranges from 80 ℃ to 150 ℃, and the mixing in the step a) is performed for 30 to 60 minutes at a temperature 60 ℃ to 120 ℃ higher than the softening point of the binder pitch. Accordingly, the present invention can prevent the deterioration of physical properties caused by volatile elements generated during the carbonization process.
본 발명은 탄소블록, 이로부터 제조되는 높은 열전도성을 갖는 흑연블록 및 그들의 제조방법에 관한 것으로서, 일 구현예에 따르면 a) 흑연 분말과 바인더 피치를 혼련하고, 분쇄 및 분급하여 혼련 분말을 마련하는 공정; b) 상기 마련된 혼련 분말을 금형에 넣고 가압하여 성형체를 마련하는 공정; 및 c) 상기 마련된 성형체를 탄화하여 탄소블록을 마련하는 공정;을 포함하며, 상기 바인더 피치의 연화점은 80 내지 150℃이며, 상기 a) 공정에서 혼련은, 상기 바인더 피치의 연화점 보다 60 내지 120℃ 높은 온도에서 30 내지 60분 동안 수행되는 것을 특징으로 하는, 탄소블록의 제조방법을 제공할 수 있다.
CARBON BLOCK GRAPHITE BLOCK HAVING HIGH THERMAL CONDUCTIVITY MANUFACTURED THEREFROM AND MANUFACTURING METHODS FOR THE SAME
The present invention relates to a carbon block, a graphite block having high thermal conductivity manufactured therefrom, and a manufacturing method for the same. According to one embodiment, a manufacturing method of a carbon block can be provided, wherein the method comprises: a step a) of mixing graphite powders and a binder pitch, grinding and classifying the same to provide mixed powders; a step b) of putting the prepared mixed powders into a mold and pressurizing the same to provide a molded body; and a step c) of carbonizing the prepared molded body to provide a carbon block. A softening point of the binder pitch ranges from 80 ℃ to 150 ℃, and the mixing in the step a) is performed for 30 to 60 minutes at a temperature 60 ℃ to 120 ℃ higher than the softening point of the binder pitch. Accordingly, the present invention can prevent the deterioration of physical properties caused by volatile elements generated during the carbonization process.
본 발명은 탄소블록, 이로부터 제조되는 높은 열전도성을 갖는 흑연블록 및 그들의 제조방법에 관한 것으로서, 일 구현예에 따르면 a) 흑연 분말과 바인더 피치를 혼련하고, 분쇄 및 분급하여 혼련 분말을 마련하는 공정; b) 상기 마련된 혼련 분말을 금형에 넣고 가압하여 성형체를 마련하는 공정; 및 c) 상기 마련된 성형체를 탄화하여 탄소블록을 마련하는 공정;을 포함하며, 상기 바인더 피치의 연화점은 80 내지 150℃이며, 상기 a) 공정에서 혼련은, 상기 바인더 피치의 연화점 보다 60 내지 120℃ 높은 온도에서 30 내지 60분 동안 수행되는 것을 특징으로 하는, 탄소블록의 제조방법을 제공할 수 있다.
CARBON BLOCK GRAPHITE BLOCK HAVING HIGH THERMAL CONDUCTIVITY MANUFACTURED THEREFROM AND MANUFACTURING METHODS FOR THE SAME
탄소블록, 이로부터 제조되는 높은 열전도성을 갖는 흑연블록 및 그들의 제조방법
LEE YOUNG SEAK (Autor:in) / LIM CHAEHUN (Autor:in) / KWAK CHEOL HWAN (Autor:in) / AN DONGHAE (Autor:in)
08.01.2024
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2019
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2025