ANNEALING OF LARGE-SIZE BLANKS OF FINE-GRAIN GRAPHITE BY ISOSTATIC PRESSING
FIELD: process engineering.SUBSTANCE: claimed invention relates to production of large-size articles from fine-grain graphite, over 800 mm in length and over 300 mm in diameter. Every said blank is arranged in annealing furnace chamber cartridge at loading thereto. It is arranged vertically in a special individual shell with wall depth making at least 10 mm to allow uniform temperature field over the blank entire surface. Aforesaid shell is made of metal (steel or aluminium) or ceramic material with high heat conductivity and capacity comparable with those of metals. Sizes of shell inside sizes allow a uniform gap between blank side surface and shell wall of at least 25 mm. Said gap is filled with heat insulating disperse hydrocarbon material or the other one that features heat conductivity factor smaller than that of the other filling used in loading of annealing furnace. Annealing is executed on schedule for at least 320 hours to maximum temperature of 1100-1500°C.EFFECT: higher yield owing to decreased amount of rejects at annealing stage in multichamber furnace of industrial furnaces.1 tbl, 1 ex
Предлагаемое изобретение относится к производству крупногабаритных изделий из мелкозернистого графита с длиной более 800 мм и диаметром более 300 мм. Технический результат изобретения - повышение выхода годных крупногабаритных изделий мелкозернистого графита изостатического прессования за счет снижения брака по трещинам на стадии обжига в многокамерных промышленных печах. Каждую крупногабаритную заготовку мелкозернистого графита изостатического прессования при загрузке в печь обжига размещают в кассете камеры печи, устанавливая ее вертикально в специальную индивидуальную оболочку с толщиной стенки не менее 10 мм с целью получения равномерного температурного поля по всей поверхности заготовки. Оболочку выполняют из металла (стали или алюминия) или керамического материала, имеющего высокую теплопроводность и теплоемкость, соизмеримые с теми же свойствами у металлов. Размеры внутренней полости оболочки обеспечивают равномерный зазор между боковой поверхностью заготовки и стенкой оболочки не менее 25 мм, который заполняется теплоизоляционным дисперсным углеродным или иным материалом с коэффициентом теплопроводности меньшим, чем у остальной пересыпки, используемой при загрузке печи обжига. Обжиг проводят по графику не менее 320 часов до максимальной температуры 1100-1500°С. 1 табл., 1 пр.
ANNEALING OF LARGE-SIZE BLANKS OF FINE-GRAIN GRAPHITE BY ISOSTATIC PRESSING
FIELD: process engineering.SUBSTANCE: claimed invention relates to production of large-size articles from fine-grain graphite, over 800 mm in length and over 300 mm in diameter. Every said blank is arranged in annealing furnace chamber cartridge at loading thereto. It is arranged vertically in a special individual shell with wall depth making at least 10 mm to allow uniform temperature field over the blank entire surface. Aforesaid shell is made of metal (steel or aluminium) or ceramic material with high heat conductivity and capacity comparable with those of metals. Sizes of shell inside sizes allow a uniform gap between blank side surface and shell wall of at least 25 mm. Said gap is filled with heat insulating disperse hydrocarbon material or the other one that features heat conductivity factor smaller than that of the other filling used in loading of annealing furnace. Annealing is executed on schedule for at least 320 hours to maximum temperature of 1100-1500°C.EFFECT: higher yield owing to decreased amount of rejects at annealing stage in multichamber furnace of industrial furnaces.1 tbl, 1 ex
Предлагаемое изобретение относится к производству крупногабаритных изделий из мелкозернистого графита с длиной более 800 мм и диаметром более 300 мм. Технический результат изобретения - повышение выхода годных крупногабаритных изделий мелкозернистого графита изостатического прессования за счет снижения брака по трещинам на стадии обжига в многокамерных промышленных печах. Каждую крупногабаритную заготовку мелкозернистого графита изостатического прессования при загрузке в печь обжига размещают в кассете камеры печи, устанавливая ее вертикально в специальную индивидуальную оболочку с толщиной стенки не менее 10 мм с целью получения равномерного температурного поля по всей поверхности заготовки. Оболочку выполняют из металла (стали или алюминия) или керамического материала, имеющего высокую теплопроводность и теплоемкость, соизмеримые с теми же свойствами у металлов. Размеры внутренней полости оболочки обеспечивают равномерный зазор между боковой поверхностью заготовки и стенкой оболочки не менее 25 мм, который заполняется теплоизоляционным дисперсным углеродным или иным материалом с коэффициентом теплопроводности меньшим, чем у остальной пересыпки, используемой при загрузке печи обжига. Обжиг проводят по графику не менее 320 часов до максимальной температуры 1100-1500°С. 1 табл., 1 пр.
ANNEALING OF LARGE-SIZE BLANKS OF FINE-GRAIN GRAPHITE BY ISOSTATIC PRESSING
СПОСОБ ОБЖИГА КРУПНОГАБАРИТНЫХ ЗАГОТОВОК МЕЛКОЗЕРНИСТОГО ГРАФИТА ИЗОСТАТИЧЕСКОГО ПРЕССОВАНИЯ
PEREVEZENTSEV VALENTIN PETROVICH (Autor:in) / BEJLINA NATALIJA JUR EVNA (Autor:in) / RUBINCHIK OL GA VASIL EVNA (Autor:in)
20.08.2015
Patent
Elektronische Ressource
Russisch
IPC:
C04B
Kalk
,
LIME
Method for preparing large-size isostatic pressing graphite product
| Europäisches Patentamt | 2024
Isostatic pressing graphite for semiconductor and preparation method of isostatic pressing graphite
| Europäisches Patentamt | 2024
Preparation method of fine-structure isotropic isostatic pressing graphite
| Europäisches Patentamt | 2022
Preparation method of isostatic pressing fine structure graphite sagger
| Europäisches Patentamt | 2024
Large-size isostatic pressing graphite cylinder material and preparation method thereof
| Europäisches Patentamt | 2023