METHOD OF MAKING LARGE-SIZED GLASS CERAMIC FOAM BLOCKS
FIELD: construction; technological processes.SUBSTANCE: invention relates to a method of producing block glass-ceramic foamed ceramics. Method involves preparation of a floured glass-ceramic phase with particle size 1-50 mcm, containing production wastes with silicon carbide content of not less than 10 wt%. Method then includes preparation of a floured mixture for making foam blocks with particle size 1-50 mcm and containing a floured glass-ceramic phase in amount of 5-95 wt% and a binding component - balance. Mixture is then used to mould a workpiece with thickness of 15-60 mm in form of large-size tiles, drying to residual moisture content of 0.5 %. Method then includes plastering with double-layer engobe lower and two side surfaces thereof, parallel to movement of roller conveyor. Tiles are dried on roller conveyor without use of moulds and trays are fed into a furnace. In furnace at end of tile sintering zone roller conveyor speed is less by 10-25% compared to it. After foaming at end of furnace bar is subjected to abrupt cooling, an incision is made and after bar exits furnace, said bar is divided into blocks along incision lines with further annealing and mechanical treatment.EFFECT: production of ceramic foam materials with thickness of up to 200 mm with uniformly closed small-pore structure throughout volume of material and improved physical and chemical properties.24 cl, 2 tbl
Изобретение относится к способу получения блочной стеклокристаллической пенокерамики. Техническим результатом изобретения является изготовление пенокерамических материалов толщиной до 200 мм с равномерно замкнутой мелкопористой структурой по всему объему материала и высокими физико-химическими свойствами. Способ включает подготовку тонкомолотой стеклокристаллической фазы с размером частиц 1-50 мкм, содержащей отходы производства с содержанием не менее 10 мас.% карбида кремния. Затем проводят подготовку тонкомолотой шихты для изготовления пеноблоков, имеющей размер частиц 1-50 мкм и содержащей тонкомолотую стеклокристаллическую фазу в количестве 5-95 мас.% и связующий компонент - остальное. Из шихты прессуют заготовки толщиной 15-60 мм в виде крупноразмерных плиток, сушат их до остаточной влажности 0,5%. Далее осуществляют обмазку двухслойным ангобом их нижних и двух боковых поверхностей, параллельных движению роликового транспортера. Высушенные плитки по роликовому транспортеру без применения форм и поддонов поступают в печь обжига. В печи обжига в конце зоны спекания плиток скорость роликового транспортера меньше на 10-25%, чем до нее. После вспенивания в конце печи обжига брус подвергают резкому охлаждению, наносят надрез и после выхода бруса из печи обжига осуществляют его разделение на блоки по линиям надреза с последующим их отжигом и механической обработкой. 23 з.п. ф-лы, 2 табл.
METHOD OF MAKING LARGE-SIZED GLASS CERAMIC FOAM BLOCKS
FIELD: construction; technological processes.SUBSTANCE: invention relates to a method of producing block glass-ceramic foamed ceramics. Method involves preparation of a floured glass-ceramic phase with particle size 1-50 mcm, containing production wastes with silicon carbide content of not less than 10 wt%. Method then includes preparation of a floured mixture for making foam blocks with particle size 1-50 mcm and containing a floured glass-ceramic phase in amount of 5-95 wt% and a binding component - balance. Mixture is then used to mould a workpiece with thickness of 15-60 mm in form of large-size tiles, drying to residual moisture content of 0.5 %. Method then includes plastering with double-layer engobe lower and two side surfaces thereof, parallel to movement of roller conveyor. Tiles are dried on roller conveyor without use of moulds and trays are fed into a furnace. In furnace at end of tile sintering zone roller conveyor speed is less by 10-25% compared to it. After foaming at end of furnace bar is subjected to abrupt cooling, an incision is made and after bar exits furnace, said bar is divided into blocks along incision lines with further annealing and mechanical treatment.EFFECT: production of ceramic foam materials with thickness of up to 200 mm with uniformly closed small-pore structure throughout volume of material and improved physical and chemical properties.24 cl, 2 tbl
Изобретение относится к способу получения блочной стеклокристаллической пенокерамики. Техническим результатом изобретения является изготовление пенокерамических материалов толщиной до 200 мм с равномерно замкнутой мелкопористой структурой по всему объему материала и высокими физико-химическими свойствами. Способ включает подготовку тонкомолотой стеклокристаллической фазы с размером частиц 1-50 мкм, содержащей отходы производства с содержанием не менее 10 мас.% карбида кремния. Затем проводят подготовку тонкомолотой шихты для изготовления пеноблоков, имеющей размер частиц 1-50 мкм и содержащей тонкомолотую стеклокристаллическую фазу в количестве 5-95 мас.% и связующий компонент - остальное. Из шихты прессуют заготовки толщиной 15-60 мм в виде крупноразмерных плиток, сушат их до остаточной влажности 0,5%. Далее осуществляют обмазку двухслойным ангобом их нижних и двух боковых поверхностей, параллельных движению роликового транспортера. Высушенные плитки по роликовому транспортеру без применения форм и поддонов поступают в печь обжига. В печи обжига в конце зоны спекания плиток скорость роликового транспортера меньше на 10-25%, чем до нее. После вспенивания в конце печи обжига брус подвергают резкому охлаждению, наносят надрез и после выхода бруса из печи обжига осуществляют его разделение на блоки по линиям надреза с последующим их отжигом и механической обработкой. 23 з.п. ф-лы, 2 табл.
METHOD OF MAKING LARGE-SIZED GLASS CERAMIC FOAM BLOCKS
СПОСОБ ИЗГОТОВЛЕНИЯ КРУПНОРАЗМЕРНЫХ СТЕКЛОКРИСТАЛЛИЧЕСКИХ ПЕНОБЛОКОВ
CHEREPANOV BORIS STEPANOVICH (Autor:in) / CHEREPANOV ANDREJ BORISOVICH (Autor:in) / DOLMANOV IGOR NIKOLAEVICH (Autor:in)
20.10.2016
Patent
Elektronische Ressource
Russisch
IPC:
C04B
Kalk
,
LIME
METHOD FOR PRODUCING LARGE-SIZED FOAMED GLASS-CERAMIC BLOCKS
| Europäisches Patentamt | 2024
METHOD FOR PRODUCING LARGE-SIZED FOAMED GLASS-CRYSTALLINE BLOCKS
| Europäisches Patentamt | 2016
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2023