METHOD OF MAKING CERAMICS BASED ON SILICON NITRIDE - TITANIUM NITRIDE COMPOSITE
FIELD: manufacturing technology.SUBSTANCE: invention relates to a method of producing a ceramic composite from silicon nitride, hardened with titanium nitride, having a combination of physical and mechanical properties, such as high strength and hardness, low coefficient of thermal expansion, wear resistance and electrical conductivity. This type of ceramics is designed for operation in acidic and aggressive media, in conditions of high temperatures and prolonged mechanical action. Proposed method comprises mixing silicon nitride powder with sintering additive and titanium metal produced by plasma chemical method, grinding in medium of isopropanol in planetary mill, drying, addition of 3 wt% aqueous 10 % solution of polyvinylpyrrolidone, cold uniaxial pressing of blanks. Subsequent sintering and nitriding of workpieces is carried out in one step by hot pressing in graphite mold at 1,650 °C with maximum specific pressure of 30 MPa for 60 minutes in nitrogen atmosphere.EFFECT: method enables to obtain in one stage dense ceramic materials having strength of up to 565 MPa, density higher than 3_14 g/cmand conducting electric current.1 cl, 1 dwg, 1 tbl, 2 ex
Изобретение относится к способу получения керамического композита из нитрида кремния, упрочненного нитридом титана, обладающего совокупностью физико-механических свойств, таких как высокая прочность и твердость, низкий коэффициент термического расширения, износостойкость и электрическая проводимость. Данный вид керамики предназначен для работы в кислых и агрессивных средах, в условиях высоких температур и длительного механического воздействия. Предложенный способ включает смешение порошка нитрида кремния со спекающей добавкой и металлическим титаном, полученным плазмохимическим методом, помол в среде изопропанола в планетарной мельнице, сушку, добавление 3 мас.% водного 10%-ного раствора поливинилпирролидона, холодное одноосное прессование заготовок. Последующее спекание и азотирование заготовок проводят в одну стадию методом горячего прессования в графитовой пресс-форме при температуре 1650°С с максимальным удельным давлением 30 МПа в течение 60 мин в атмосфере азота. Способ позволяет получать в одну стадию плотноспеченные керамические материалы, обладающие прочностью до 565 МПа, с плотностью выше 3,14 г/сми проводящие электрический ток. 1 ил., 1 табл., 2 пр.
METHOD OF MAKING CERAMICS BASED ON SILICON NITRIDE - TITANIUM NITRIDE COMPOSITE
FIELD: manufacturing technology.SUBSTANCE: invention relates to a method of producing a ceramic composite from silicon nitride, hardened with titanium nitride, having a combination of physical and mechanical properties, such as high strength and hardness, low coefficient of thermal expansion, wear resistance and electrical conductivity. This type of ceramics is designed for operation in acidic and aggressive media, in conditions of high temperatures and prolonged mechanical action. Proposed method comprises mixing silicon nitride powder with sintering additive and titanium metal produced by plasma chemical method, grinding in medium of isopropanol in planetary mill, drying, addition of 3 wt% aqueous 10 % solution of polyvinylpyrrolidone, cold uniaxial pressing of blanks. Subsequent sintering and nitriding of workpieces is carried out in one step by hot pressing in graphite mold at 1,650 °C with maximum specific pressure of 30 MPa for 60 minutes in nitrogen atmosphere.EFFECT: method enables to obtain in one stage dense ceramic materials having strength of up to 565 MPa, density higher than 3_14 g/cmand conducting electric current.1 cl, 1 dwg, 1 tbl, 2 ex
Изобретение относится к способу получения керамического композита из нитрида кремния, упрочненного нитридом титана, обладающего совокупностью физико-механических свойств, таких как высокая прочность и твердость, низкий коэффициент термического расширения, износостойкость и электрическая проводимость. Данный вид керамики предназначен для работы в кислых и агрессивных средах, в условиях высоких температур и длительного механического воздействия. Предложенный способ включает смешение порошка нитрида кремния со спекающей добавкой и металлическим титаном, полученным плазмохимическим методом, помол в среде изопропанола в планетарной мельнице, сушку, добавление 3 мас.% водного 10%-ного раствора поливинилпирролидона, холодное одноосное прессование заготовок. Последующее спекание и азотирование заготовок проводят в одну стадию методом горячего прессования в графитовой пресс-форме при температуре 1650°С с максимальным удельным давлением 30 МПа в течение 60 мин в атмосфере азота. Способ позволяет получать в одну стадию плотноспеченные керамические материалы, обладающие прочностью до 565 МПа, с плотностью выше 3,14 г/сми проводящие электрический ток. 1 ил., 1 табл., 2 пр.
METHOD OF MAKING CERAMICS BASED ON SILICON NITRIDE - TITANIUM NITRIDE COMPOSITE
Способ изготовления керамики на основе композита нитрид кремния - нитрид титана
TITOV DMITRIJ DMITRIEVICH (Autor:in) / LYSENKOV ANTON SERGEEVICH (Autor:in) / FROLOVA MARIANNA GENNADEVNA (Autor:in) / KARGIN YURIJ FEDOROVICH (Autor:in) / KIM KONSTANTIN ALEKSANDROVICH (Autor:in) / IVICHEVA SVETLANA NIKOLAEVNA (Autor:in)
21.08.2019
Patent
Elektronische Ressource
Russisch
IPC:
C04B
Kalk
,
LIME
Microstructures and properties in aluminum nitride-titanium nitride composite ceramics
| British Library Online Contents | 1999
| British Library Online Contents | 1994
| British Library Online Contents | 2009
METHOD FOR OBTAINING COMPOSITE CERAMICS BASED ON SILICON NITRIDE
| Europäisches Patentamt | 2018
Titanium Nitride - Silicon Nitride Composite Coatings Deposited by Reactive Magnetron Sputtering
| British Library Online Contents | 1998