TWO-PHASE MIXTURE BASED ON CEMENT FOR COMPOSITES IN CONSTRUCTION 3D PRINTING TECHNOLOGY
FIELD: construction.SUBSTANCE: invention relates to construction materials which are adapted to 3D construction printing modes. Invention includes a two-phase mixture based on cement for composites in construction 3D printing technology. Two-phase mixture contains two phases: solid (phase 1) - mixture of dry components and liquid (phase 2) - aqueous solution. Ratio of the two phases is 4.8–5:1. Phase 1 contains components, wt. %: portlandcement CEM I 42.5 H - 48.3–49.8, limestone flour with content of CaCO3 of not less than 95 % - 49.8–51.1, xanthan gum with content (C35H49O29) n is not less than 91 % - 0.1–0.15, tetrapotassium pyrophosphate with K4P2O5 content of not less than 98 % - 0.1–0.15, polypropylene fiber with length of 12 mm - 0.2–0.3. Phase 2 contains water and superplasticizer based on polycarboxylate esters. Weight ratio of components: water - 96.2–97.8 %, superplasticizer - 2.2–3.8 %.EFFECT: technical result is increased plasticity, shape stability, compression strength, bending tensile strength, adhesion strength of composite layers.1 cl, 1 tbl
Изобретение относится к строительным материалам, которые адаптированы к режимам строительной 3D-печати. Изобретение содержит двухфазную смесь на основе цемента для композитов в технологии строительной 3D-печати. Двухфазная смесь содержит две фазы: твердую (фаза 1) - смесь из сухих компонентов и жидкую (фаза 2) - водный раствор. Соотношение двух фаз равно 4,8-5:1. Фаза 1 включает компоненты, % масс.: портландцемент ЦЕМ I 42,5 Н - 48,3-49,8, известняковую муку с содержанием СаСО3 не менее 95% - 49,8-51,1, камедь ксантановую с содержанием (С35H49О29)n не менее 91% - 0,1-0,15, тетракалий пирофосфат технический с содержанием K4Р2О5 не менее 98% - 0,1-0,15, полипропиленовую фибру длиной 12 мм - 0,2-0,3. Фаза 2 содержит воду и суперпластификатор на основе поликарбоксилатных эфиров. Массовые соотношения компонентов: вода - 96,2-97,8%, суперпластификатор - 2,2-3,8%. Технический результат – повышаются пластичность, формоустойчивость, прочность на сжатие, прочность на растяжение при изгибе, прочность сцепления слоев композита. 1 табл.
TWO-PHASE MIXTURE BASED ON CEMENT FOR COMPOSITES IN CONSTRUCTION 3D PRINTING TECHNOLOGY
FIELD: construction.SUBSTANCE: invention relates to construction materials which are adapted to 3D construction printing modes. Invention includes a two-phase mixture based on cement for composites in construction 3D printing technology. Two-phase mixture contains two phases: solid (phase 1) - mixture of dry components and liquid (phase 2) - aqueous solution. Ratio of the two phases is 4.8–5:1. Phase 1 contains components, wt. %: portlandcement CEM I 42.5 H - 48.3–49.8, limestone flour with content of CaCO3 of not less than 95 % - 49.8–51.1, xanthan gum with content (C35H49O29) n is not less than 91 % - 0.1–0.15, tetrapotassium pyrophosphate with K4P2O5 content of not less than 98 % - 0.1–0.15, polypropylene fiber with length of 12 mm - 0.2–0.3. Phase 2 contains water and superplasticizer based on polycarboxylate esters. Weight ratio of components: water - 96.2–97.8 %, superplasticizer - 2.2–3.8 %.EFFECT: technical result is increased plasticity, shape stability, compression strength, bending tensile strength, adhesion strength of composite layers.1 cl, 1 tbl
Изобретение относится к строительным материалам, которые адаптированы к режимам строительной 3D-печати. Изобретение содержит двухфазную смесь на основе цемента для композитов в технологии строительной 3D-печати. Двухфазная смесь содержит две фазы: твердую (фаза 1) - смесь из сухих компонентов и жидкую (фаза 2) - водный раствор. Соотношение двух фаз равно 4,8-5:1. Фаза 1 включает компоненты, % масс.: портландцемент ЦЕМ I 42,5 Н - 48,3-49,8, известняковую муку с содержанием СаСО3 не менее 95% - 49,8-51,1, камедь ксантановую с содержанием (С35H49О29)n не менее 91% - 0,1-0,15, тетракалий пирофосфат технический с содержанием K4Р2О5 не менее 98% - 0,1-0,15, полипропиленовую фибру длиной 12 мм - 0,2-0,3. Фаза 2 содержит воду и суперпластификатор на основе поликарбоксилатных эфиров. Массовые соотношения компонентов: вода - 96,2-97,8%, суперпластификатор - 2,2-3,8%. Технический результат – повышаются пластичность, формоустойчивость, прочность на сжатие, прочность на растяжение при изгибе, прочность сцепления слоев композита. 1 табл.
TWO-PHASE MIXTURE BASED ON CEMENT FOR COMPOSITES IN CONSTRUCTION 3D PRINTING TECHNOLOGY
Двухфазная смесь на основе цемента для композитов в технологии строительной 3D-печати
SLAVCHEVA GALINA STANISLAVOVNA (Autor:in) / ARTAMONOVA OLGA VLADIMIROVNA (Autor:in) / SHVEDOVA MARIYA ALEKSANDROVNA (Autor:in) / BRITVINA EKATERINA ALEKSEEVNA (Autor:in)
05.08.2020
Patent
Elektronische Ressource
Russisch
IPC:
C04B
Kalk
,
LIME
/
B33Y
ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
,
Additive (generative) Fertigung, d. h. die Herstellung von dreidimensionalen [3D] Bauteilen durch additive Abscheidung, additive Agglomeration oder additive Schichtung, z. B. durch 3D- Drucken, Stereolithografie oder selektives Lasersintern
TWO-PHASE MIXTURE BASED ON CEMENT FOR COMPOSITES IN CONSTRUCTION 3D PRINTING TECHNOLOGY
| Europäisches Patentamt | 2020
TWO-PHASE MIXTURE BASED ON CEMENT FOR COMPOSITES IN CONSTRUCTION 3D PRINTING TECHNOLOGY
| Europäisches Patentamt | 2020
TWO-PHASE MIXTURE BASED ON CEMENT FOR COMPOSITES IN CONSTRUCTION 3D PRINTING TECHNOLOGY
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2022
POLYMER-CEMENT DRY CONSTRUCTION MIXTURE FOR 3D PRINTING
| Europäisches Patentamt | 2020