POLYMER-CEMENT DRY CONSTRUCTION MIXTURE FOR 3D PRINTING
FIELD: technological processes.SUBSTANCE: present invention relates to a polymer-cement dry construction mixture for 3D printing, comprising portland cement, polymer binder, sand, fiber glass and modifier, wherein polymer binder used is redispersible polymer powder of polyvinyl acetate or copolymers of polyvinyl acetate, sand is used with grain diameter up to 5 mm, fibrous fiber is used as fibrous fiber with dimensions l×d = 6 ÷ 12 × 0.005÷0.05 mm, modifier is a powdered floroglyucinfurfural modifier in the following ratio, wt% portland cement - 27.45-32.55, redispersible polymer powder - 1.63-2.75, sand - 65.10-68.60, fiber glass - 0.65-1.12, powder modifier - 0.07-0.15. Invention is developed in dependent claims.EFFECT: providing high thixotropic properties, fast structure formation and high plastic strength at rest, high adhesion between layers, low loss of water from exposed surfaces of hardening material and low shrinkage deformations.5 cl, 2 tbl
Настоящее изобретение относится к полимерцементной сухой строительной смеси для 3D-печати, включающей портландцемент, полимерное связующее, песок, фиброволокно и модификатор, причем в качестве полимерного связующего используют редиспергируемый полимерный порошок поливинилацетата или сополимеров поливинилацетата, песок используют с диаметром зерен до 5 мм, в качестве фиброволокна используют фиброволокно с размерами l×d = 6 ÷ 12 × 0,005÷0,05 мм, в качестве модификатора - порошковый флороглюцинфурфурольный модификатор в следующем соотношении, мас.% портландцемент - 27,45-32,55, редиспергируемый полимерный порошок - 1,63-2,75, песок - 65,10-68,60, фиброволокно - 0,65-1,12, порошковый модификатор - 0,07-0,15. Изобретение развито в зависимых пунктах формулы изобретения. Технический результат - обеспечение высоких тиксотропных свойств, быстрого структурообразования и высокой пластической прочности в состоянии покоя, высокой адгезии между слоями, низкой потери воды с открытых поверхностей твердеющего материала и низких усадочных деформаций. 4 з.п. ф-лы, 2 табл.
POLYMER-CEMENT DRY CONSTRUCTION MIXTURE FOR 3D PRINTING
FIELD: technological processes.SUBSTANCE: present invention relates to a polymer-cement dry construction mixture for 3D printing, comprising portland cement, polymer binder, sand, fiber glass and modifier, wherein polymer binder used is redispersible polymer powder of polyvinyl acetate or copolymers of polyvinyl acetate, sand is used with grain diameter up to 5 mm, fibrous fiber is used as fibrous fiber with dimensions l×d = 6 ÷ 12 × 0.005÷0.05 mm, modifier is a powdered floroglyucinfurfural modifier in the following ratio, wt% portland cement - 27.45-32.55, redispersible polymer powder - 1.63-2.75, sand - 65.10-68.60, fiber glass - 0.65-1.12, powder modifier - 0.07-0.15. Invention is developed in dependent claims.EFFECT: providing high thixotropic properties, fast structure formation and high plastic strength at rest, high adhesion between layers, low loss of water from exposed surfaces of hardening material and low shrinkage deformations.5 cl, 2 tbl
Настоящее изобретение относится к полимерцементной сухой строительной смеси для 3D-печати, включающей портландцемент, полимерное связующее, песок, фиброволокно и модификатор, причем в качестве полимерного связующего используют редиспергируемый полимерный порошок поливинилацетата или сополимеров поливинилацетата, песок используют с диаметром зерен до 5 мм, в качестве фиброволокна используют фиброволокно с размерами l×d = 6 ÷ 12 × 0,005÷0,05 мм, в качестве модификатора - порошковый флороглюцинфурфурольный модификатор в следующем соотношении, мас.% портландцемент - 27,45-32,55, редиспергируемый полимерный порошок - 1,63-2,75, песок - 65,10-68,60, фиброволокно - 0,65-1,12, порошковый модификатор - 0,07-0,15. Изобретение развито в зависимых пунктах формулы изобретения. Технический результат - обеспечение высоких тиксотропных свойств, быстрого структурообразования и высокой пластической прочности в состоянии покоя, высокой адгезии между слоями, низкой потери воды с открытых поверхностей твердеющего материала и низких усадочных деформаций. 4 з.п. ф-лы, 2 табл.
POLYMER-CEMENT DRY CONSTRUCTION MIXTURE FOR 3D PRINTING
ПОЛИМЕРЦЕМЕНТНАЯ СУХАЯ СТРОИТЕЛЬНАЯ СМЕСЬ ДЛЯ 3D-ПЕЧАТИ
POLUEKTOVA VALENTINA ANATOLEVNA (Autor:in) / SHAPOVALOV NIKOLAI AFANASEVICH (Autor:in)
29.12.2020
Patent
Elektronische Ressource
Russisch
IPC:
C04B
Kalk
,
LIME
TWO-PHASE MIXTURE BASED ON CEMENT FOR COMPOSITES IN CONSTRUCTION 3D PRINTING TECHNOLOGY
| Europäisches Patentamt | 2020
TWO-PHASE MIXTURE BASED ON CEMENT FOR COMPOSITES IN CONSTRUCTION 3D PRINTING TECHNOLOGY
| Europäisches Patentamt | 2020
TWO-PHASE MIXTURE BASED ON CEMENT FOR COMPOSITES IN CONSTRUCTION 3D PRINTING TECHNOLOGY
| Europäisches Patentamt | 2020
TWO-PHASE MIXTURE BASED ON CEMENT FOR COMPOSITES IN CONSTRUCTION 3D PRINTING TECHNOLOGY
| Europäisches Patentamt | 2020