METHOD OF PRODUCING CORUNDUM CERAMICS
FIELD: chemistry.SUBSTANCE: invention relates to chemical engineering, particularly to methods of producing corundum ceramics, and can be used in radioelectronic and electrovacuum equipment, as well as in medicine for making prostheses and implants. Preparation of aqueous suspension from layered double hydroxide of magnesium and aluminum Mg4Al2(OH)12CO3⋅3H2O and hydrated aluminum oxide Al2O3⋅nH2O, where n>3, with additional introduction of ammonium carbonate in amount of 3–8 mol per 1 mol of Al2O3. Layered double hydroxide of magnesium and aluminum Mg4Al2(OH)12CO3⋅3H2O is obtained by mixing crystalline hydrate of chloride or nitrate of magnesium and aluminum with ammonium carbonate. Suspension is stirred at temperature 70–120 °C and L:S=10–18 for 2–6 hours to form aluminum and ammonium hydroxocarbonate precipitate, which contains finely dispersed powder layered double magnesium and aluminum hydroxide. Precipitate is separated and dried at 100–120 °C to ensure constant weight, after which heated to temperature of 1,100–1,200 °C and held for 1.0–1.5 hours to obtain a ceramic-forming mixture which is subjected to molding and annealing.EFFECT: claimed method allows to reduce the energy consumption and the number of transactions and to receive corundum ceramics 3_95–3_98 g/cm3density when using commonly available starting components.3 cl, 4 ex
Изобретение относится к области химической технологии, в частности к способам получения корундовой керамики, и может быть использовано в радиоэлектронной и электровакуумной технике, а также в медицине для изготовления протезов и имплантатов. Осуществляют приготовление водной суспензии из слоистого двойного гидроксида магния и алюминия Mg4Al2(OH)12CO3⋅3H2O и гидратированного оксида алюминия Al2O3⋅nH2O, где n>3, с дополнительным введением в нее карбоната аммония в количестве 3-8 моль на 1 моль Al2O3. Слоистый двойной гидроксид магния и алюминия Mg4Al2(OH)12CO3⋅3H2O получают смешением кристаллогидратов хлорида или нитрата магния и алюминия с карбонатом аммония. Суспензию перемешивают при температуре 70-120°С и Ж:Т=10-18 в течение 2-6 часов с образованием осадка гидроксокарбоната алюминия и аммония, который содержит тонкодисперсный порошок слоистого двойного гидроксида магния и алюминия. Осадок отделяют и сушат при 100-120°С до обеспечения постоянной массы, после чего нагревают до температуры 1100-1200°С и выдерживают в течение 1,0-1,5 часов с получением керамообразующей смеси, которую подвергают формовке и обжигу. Заявляемый способ позволяет снизить энергоемкость и число операций и получить корундовую керамику плотностью 3,95-3,98 г/см3при использовании широкодоступных исходных компонентов. 2 з.п. ф-лы, 4 пр.
METHOD OF PRODUCING CORUNDUM CERAMICS
FIELD: chemistry.SUBSTANCE: invention relates to chemical engineering, particularly to methods of producing corundum ceramics, and can be used in radioelectronic and electrovacuum equipment, as well as in medicine for making prostheses and implants. Preparation of aqueous suspension from layered double hydroxide of magnesium and aluminum Mg4Al2(OH)12CO3⋅3H2O and hydrated aluminum oxide Al2O3⋅nH2O, where n>3, with additional introduction of ammonium carbonate in amount of 3–8 mol per 1 mol of Al2O3. Layered double hydroxide of magnesium and aluminum Mg4Al2(OH)12CO3⋅3H2O is obtained by mixing crystalline hydrate of chloride or nitrate of magnesium and aluminum with ammonium carbonate. Suspension is stirred at temperature 70–120 °C and L:S=10–18 for 2–6 hours to form aluminum and ammonium hydroxocarbonate precipitate, which contains finely dispersed powder layered double magnesium and aluminum hydroxide. Precipitate is separated and dried at 100–120 °C to ensure constant weight, after which heated to temperature of 1,100–1,200 °C and held for 1.0–1.5 hours to obtain a ceramic-forming mixture which is subjected to molding and annealing.EFFECT: claimed method allows to reduce the energy consumption and the number of transactions and to receive corundum ceramics 3_95–3_98 g/cm3density when using commonly available starting components.3 cl, 4 ex
Изобретение относится к области химической технологии, в частности к способам получения корундовой керамики, и может быть использовано в радиоэлектронной и электровакуумной технике, а также в медицине для изготовления протезов и имплантатов. Осуществляют приготовление водной суспензии из слоистого двойного гидроксида магния и алюминия Mg4Al2(OH)12CO3⋅3H2O и гидратированного оксида алюминия Al2O3⋅nH2O, где n>3, с дополнительным введением в нее карбоната аммония в количестве 3-8 моль на 1 моль Al2O3. Слоистый двойной гидроксид магния и алюминия Mg4Al2(OH)12CO3⋅3H2O получают смешением кристаллогидратов хлорида или нитрата магния и алюминия с карбонатом аммония. Суспензию перемешивают при температуре 70-120°С и Ж:Т=10-18 в течение 2-6 часов с образованием осадка гидроксокарбоната алюминия и аммония, который содержит тонкодисперсный порошок слоистого двойного гидроксида магния и алюминия. Осадок отделяют и сушат при 100-120°С до обеспечения постоянной массы, после чего нагревают до температуры 1100-1200°С и выдерживают в течение 1,0-1,5 часов с получением керамообразующей смеси, которую подвергают формовке и обжигу. Заявляемый способ позволяет снизить энергоемкость и число операций и получить корундовую керамику плотностью 3,95-3,98 г/см3при использовании широкодоступных исходных компонентов. 2 з.п. ф-лы, 4 пр.
METHOD OF PRODUCING CORUNDUM CERAMICS
Способ получения корундовой керамики
MATVEEV VIKTOR ALEKSEEVICH (Autor:in) / YAKOVLEV KIRILL ANDREEVICH (Autor:in)
25.11.2020
Patent
Elektronische Ressource
Russisch
IPC:
C04B
Kalk
,
LIME
/
B82Y
Bestimmter Gebrauch oder bestimmte Anwendung von Nanostrukturen
,
SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES
/
C01F
COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
,
Verbindungen der Metalle Beryllium, Magnesium, Aluminium, Calcium, Strontium, Barium, Radium, Thorium oder der Seltenen Erden
METHOD FOR PRODUCING CHARGE FOR CORUNDUM CERAMICS (VERSIONS)
| Europäisches Patentamt | 2017
METHOD OF PRODUCING REFRACTORY PRODUCTS FROM CORUNDUM CERAMICS
| Europäisches Patentamt | 2017
METHOD OF PRODUCING CORUNDUM CERAMICS CONTAINING METALLIC NICKEL
| Europäisches Patentamt | 2017
METHOD OF PRODUCING ARTICLES FROM CORUNDUM ARMOR CERAMICS
| Europäisches Patentamt | 2020