METHOD FOR PRODUCING POROUS BIOCERAMIC WOLLASTONITE
FIELD: medicine.SUBSTANCE: invention can be used in implant surgery, in traumatology, orthopedics, dentistry and other fields of medicine for the restoration, replacement and reconstruction of damaged hard tissues in a living organism. The proposed method includes the preparation of an amorphous composite material containing an amorphous mixture of dispersed hydrated calcium silicate and hydroxyapatite from calcium- and silicon-containing solutions by a sol-gel method using a latex template, the resulting material is washed, pressed and sintered. Pressing at a pressure of 24-25 MPa is carried out in a vacuum simultaneously with sintering, while sintering is carried out using electric pulse heating at a rate of 160-170°C / min to a temperature of 800-900°C with exposure at the reached temperature for 4.5-5,0 min. Electric pulse heating is provided in the mode of low-voltage pulses at a current strength of 470-500 A and a voltage of 1.9-2.0 V. The sintered ceramic material is allowed to cool, and then it is heated in an air atmosphere at a rate of 4.5-5.0°C / min. up to 800-850°С and kept at the reached temperature for 4.5-5.0 minutes.EFFECT: increase in the strength properties of calcium phosphate bioceramics based on wollastonite by increasing the homogeneity of its porous structure, enhancing its biologically active properties by lowering the temperature and reducing the time of thermal action on the processed material while reducing the time and labor costs for the method.2 cl, 2 ex, 5 dwg
Изобретение относится к области биологически активных керамических медицинских материалов и может быть использовано в имплантационной хирургии, в травматологии, ортопедии, стоматологии и других областях медицины для восстановления, замещения и реконструкции поврежденных твердых тканей в живом организме. Предлагаемый способ включает приготовление аморфного композитного материала, содержащего аморфную смесь дисперсного гидратированного силиката кальция и гидроксиапатита, из кальций- и кремнийсодержащих растворов золь-гель методом с применением латексного темплата, полученный материал промывают, прессуют и спекают. Прессование при давлении 24-25 МПа проводят в вакууме одновременно со спеканием, при этом спекание осуществляют при помощи электроимпульсного разогрева со скоростью 160-170°С/мин до температуры 800-900°С с выдержкой при достигнутой температуре в течение 4,5-5,0 мин. Электроимпульсный разогрев обеспечивают в режиме низковольтных импульсов при силе тока 470-500 А и напряжении 1,9-2,0 В. Спеченному керамическому материалу дают остыть, затем нагревают его в атмосфере воздуха со скоростью 4,5-5,0°С/мин до 800-850°С и выдерживают при достигнутой температуре в течение 4,5-5,0 мин. Технический результат - повышение прочностных качеств кальцийфосфатной биокерамики на основе волластонита за счет увеличения гомогенности ее пористой структуры, усиление ее биологически активных свойств за счет снижения температуры и сокращения времени термического воздействия на обрабатываемый материал при одновременном уменьшении затрат времени и трудозатрат на осуществление способа. 1 з.п. ф-лы, 2 пр., 5 ил.
METHOD FOR PRODUCING POROUS BIOCERAMIC WOLLASTONITE
FIELD: medicine.SUBSTANCE: invention can be used in implant surgery, in traumatology, orthopedics, dentistry and other fields of medicine for the restoration, replacement and reconstruction of damaged hard tissues in a living organism. The proposed method includes the preparation of an amorphous composite material containing an amorphous mixture of dispersed hydrated calcium silicate and hydroxyapatite from calcium- and silicon-containing solutions by a sol-gel method using a latex template, the resulting material is washed, pressed and sintered. Pressing at a pressure of 24-25 MPa is carried out in a vacuum simultaneously with sintering, while sintering is carried out using electric pulse heating at a rate of 160-170°C / min to a temperature of 800-900°C with exposure at the reached temperature for 4.5-5,0 min. Electric pulse heating is provided in the mode of low-voltage pulses at a current strength of 470-500 A and a voltage of 1.9-2.0 V. The sintered ceramic material is allowed to cool, and then it is heated in an air atmosphere at a rate of 4.5-5.0°C / min. up to 800-850°С and kept at the reached temperature for 4.5-5.0 minutes.EFFECT: increase in the strength properties of calcium phosphate bioceramics based on wollastonite by increasing the homogeneity of its porous structure, enhancing its biologically active properties by lowering the temperature and reducing the time of thermal action on the processed material while reducing the time and labor costs for the method.2 cl, 2 ex, 5 dwg
Изобретение относится к области биологически активных керамических медицинских материалов и может быть использовано в имплантационной хирургии, в травматологии, ортопедии, стоматологии и других областях медицины для восстановления, замещения и реконструкции поврежденных твердых тканей в живом организме. Предлагаемый способ включает приготовление аморфного композитного материала, содержащего аморфную смесь дисперсного гидратированного силиката кальция и гидроксиапатита, из кальций- и кремнийсодержащих растворов золь-гель методом с применением латексного темплата, полученный материал промывают, прессуют и спекают. Прессование при давлении 24-25 МПа проводят в вакууме одновременно со спеканием, при этом спекание осуществляют при помощи электроимпульсного разогрева со скоростью 160-170°С/мин до температуры 800-900°С с выдержкой при достигнутой температуре в течение 4,5-5,0 мин. Электроимпульсный разогрев обеспечивают в режиме низковольтных импульсов при силе тока 470-500 А и напряжении 1,9-2,0 В. Спеченному керамическому материалу дают остыть, затем нагревают его в атмосфере воздуха со скоростью 4,5-5,0°С/мин до 800-850°С и выдерживают при достигнутой температуре в течение 4,5-5,0 мин. Технический результат - повышение прочностных качеств кальцийфосфатной биокерамики на основе волластонита за счет увеличения гомогенности ее пористой структуры, усиление ее биологически активных свойств за счет снижения температуры и сокращения времени термического воздействия на обрабатываемый материал при одновременном уменьшении затрат времени и трудозатрат на осуществление способа. 1 з.п. ф-лы, 2 пр., 5 ил.
METHOD FOR PRODUCING POROUS BIOCERAMIC WOLLASTONITE
Способ получения пористого биокерамического волластонита
PAPYNOV EVGENIJ KONSTANTINOVICH (Autor:in) / SHICHALIN OLEG OLEGOVICH (Autor:in) / APANASEVICH VLADIMIR IOSIFOVICH (Autor:in) / AFONIN IGOR SERGEEVICH (Autor:in) / EVDOKIMOV IVAN OLEGOVICH (Autor:in)
26.02.2021
Patent
Elektronische Ressource
Russisch
Preparation of Porous Wollastonite Microspheres
| British Library Online Contents | 2012
METHOD OF PRODUCING WOLLASTONITE-CONTAINING FIRED PRODUCT
| Europäisches Patentamt | 2024
Preparation of Porous Wollastonite Ceramics for Filtration
| British Library Online Contents | 2007
Porous calc silicate bioceramic material, preparation method and application
| Europäisches Patentamt | 2015