LIGHTWEIGHT MICRO-CLOSED-PORE ALUMINA COMPOSITE REFRACTORY MATERIAL AND METHOD PREPARING SAME
A lightweight micro-closed-pore corundum composite refractory and a method preparing the same, wherein raw materials of the refractory comprise 95-99 parts by weight of α-Al2O3 micro-powder and 1-5 parts by weight of dolomite clinker; and additives of the refractory comprise 2-15 parts by weight of nano alumina sol, 5-15 parts by weight of a carbohydrate polymer, and 30-50 parts by weight of an organic alcohol. and the lightweight micro-closed-pore corundum composite refractory is prepared by: mixing and wet grinding the raw materials and the additives to obtain a slurry; placing the slurry in a mold, keeping the mold at 15-25° C. for 6-12 hours and then keeping the mold at 60-90° C. for 6-12 hours, then demolding; drying a demolded green body at 110-200° C. for 24-36 hours, and keeping the green body at 1800-2000° C. for 2-5 hours. A method preparing a lightweight micro-closed-pore corundum composite refractory is also provided. The lightweight micro-closed-pore corundum composite refractory of the present invention has characteristics of low bulk density, small average pore size, high closed porosity, low thermal conductivity, strong thermal shock resistance, abrasion resistance and slag resistance.
LIGHTWEIGHT MICRO-CLOSED-PORE ALUMINA COMPOSITE REFRACTORY MATERIAL AND METHOD PREPARING SAME
A lightweight micro-closed-pore corundum composite refractory and a method preparing the same, wherein raw materials of the refractory comprise 95-99 parts by weight of α-Al2O3 micro-powder and 1-5 parts by weight of dolomite clinker; and additives of the refractory comprise 2-15 parts by weight of nano alumina sol, 5-15 parts by weight of a carbohydrate polymer, and 30-50 parts by weight of an organic alcohol. and the lightweight micro-closed-pore corundum composite refractory is prepared by: mixing and wet grinding the raw materials and the additives to obtain a slurry; placing the slurry in a mold, keeping the mold at 15-25° C. for 6-12 hours and then keeping the mold at 60-90° C. for 6-12 hours, then demolding; drying a demolded green body at 110-200° C. for 24-36 hours, and keeping the green body at 1800-2000° C. for 2-5 hours. A method preparing a lightweight micro-closed-pore corundum composite refractory is also provided. The lightweight micro-closed-pore corundum composite refractory of the present invention has characteristics of low bulk density, small average pore size, high closed porosity, low thermal conductivity, strong thermal shock resistance, abrasion resistance and slag resistance.
LIGHTWEIGHT MICRO-CLOSED-PORE ALUMINA COMPOSITE REFRACTORY MATERIAL AND METHOD PREPARING SAME
GU HUAZHI (Autor:in) / HUANG AO (Autor:in) / FU LVPING (Autor:in) / ZHANG MEIJIE (Autor:in) / LI NAN (Autor:in)
08.11.2018
Patent
Elektronische Ressource
Englisch
IPC:
C04B
Kalk
,
LIME
Lightweight micro-closed-pore corundum composite refractory, method for preparing the same
Europäisches Patentamt | 2019
|Europäisches Patentamt | 2021
|Method for preparing closed-pore alumina-based ceramic with controllable pore size
Europäisches Patentamt | 2015
|Whisker-reinforced lightweight alumina-carbon refractory material and preparation method thereof
Europäisches Patentamt | 2021
|Europäisches Patentamt | 2022
|