HIGH-ZIRCONIA ELECTRO-FUSED CAST REFRACTORY MATERIAL
Provided is a high-zirconia electro-fused cast refractory material which has a ZrO2 content of more than 95% by mass, rarely undergoes cracking during the production thereof, has excellent corrosion resistance to a molten glass, is less likely to produce zircon crystals even under heating of the refractory material alone or under heating of the refractory material while the refractory material being in contact with a molten glass, and can be produced in a large amount industrially. The high-zirconia electro-fused cast refractory material contains, as chemical components, ZrO2 in an amount of more than 95% by mass and 98% by mass or less, Al2O3 in an amount of 0.1 to 1.5% by mass, SiO2 in an amount of 1 to 2.5% by mass, K2O in an amount of 0 to 0.1% by mass, both of Na2O and K2O in a total amount of 0.01 to 0.3% by mass, B2O3 in an amount of 0.02 to 0.4% by mass, BaO in an amount of 0.01 to 0.6% by mass, SnO2 in an amount of 0.01 to 0.4% by mass, and both of Fe2O3 and TiO2 in a total amount of 0.3% by mass or less, in which the content of P2O5 is 0.04% by mass or less, and the contents of B2O3 and SnO2 satisfy the following formulae (1) and (2). 0.20≦(SnO2/B2O3)<6.5 ··· (1) 0.14% by mass ≦(CSnO2+CB2O3/2)≦0.55% by mass ··· (2) (In the formulae, CSnO2 represents the content of SnO2, and CB2O3 represents the content of B2O3, each of which is expressed in % by mass in the refractory material.)
L'invention concerne un matériau réfractaire coulé électrofondu à haute teneur en zircone qui a une teneur en ZrO2 supérieure à 95% en masse, qui subit rarement des fissures pendant sa production, qui a une excellente résistance à la corrosion par un verre fondu, qui est moins susceptible de produire des cristaux de zircon même en chauffant le matériau réfractaire seul ou en chauffant le matériau réfractaire alors que le matériau réfractaire est en contact avec un verre fondu, et qui peut être produit industriellement en grande quantité. Le matériau réfractaire coulé électrofondu à haute teneur en zircone contient, en tant que composants chimiques, du ZrO2 en une quantité supérieure à 95 % en masse et inférieure ou égale à 98 % en masse, de l'Al2O3 en une quantité allant de 0,1 à 1,5 % en masse, du SiO2 en une quantité allant de 1 à 2,5 % en masse, du K2O en une quantité allant de 0 à 0,1 % en masse, à la fois du Na2O et du K2O en une quantité totale allant de 0,01 à 0,3 % en masse, du B2O3 en une quantité allant de 0,02 à 0,4 % en masse, du BaO en une quantité allant de 0,01 à 0,6 % en masse, du SnO2 en une quantité allant de 0,01 à 0,4 % en masse, et à la fois du Fe2O3 et du TiO2 en une quantité totale de 0,3 % en masse ou moins, dans lequel la teneur en P2O5 est de 0,04 % en masse ou moins et les teneurs en B2O3 et SnO2 satisfont aux formules (1) et (2) suivantes. 0,20≦(SnO2/B2O3)<6,5 ··· (1) 0,14 % en masse ≦(CSnO2+CB2O3/2)≦0,55 % en masse ··· (2) (Dans les formules, CSnO2 représente la teneur en SnO2, et CB2O3 représente la teneur en B2O3, chacune d'entre elles étant exprimée en % en masse dans le matériau réfractaire.)
ＺｒＯ２が９５質量％を超える含有量であり、製造時の亀裂が少なく、溶融ガラスに対する耐食性に優れ、耐火物単体での加熱下又は溶融ガラスと接触した場合の加熱下でもジルコン結晶を生成しにくい、産業上量産が容易な高ジルコニア電気溶融鋳造耐火物を提供する。 化学成分として、ＺｒＯ２が９５質量％を超え９８質量％以下、Ａｌ２Ｏ３が０．１～１．５質量％、ＳｉＯ２が１～２．５質量％、Ｋ２Ｏが０～０．１質量％、且つ、Ｎａ２ＯとＫ２Ｏの合計が０．０１～０．３質量％、Ｂ２Ｏ３が０．０２～０．４質量％、ＢａＯが０．０１～０．６質量％、ＳｎＯ２が０．０１～０．４質量％、Ｆｅ２Ｏ３とＴｉＯ２の合計が０．３質量％以下、Ｐ２Ｏ５の含有量が０．０４質量％以下であり、Ｂ２Ｏ３及びＳｎＯ２の含有量が次の式（１）及び式（２）を満たす高ジルコニア電気溶融鋳造耐火物。 ０．２０≦（ＳｎＯ２／Ｂ２Ｏ３）＜６．５・・・（１） ０．１４質量％≦（ＣＳｎＯ２＋ＣＢ２Ｏ３／２）≦０．５５質量％ ・・・（２） （式中のＣＳｎＯ２はＳｎＯ２の含有量を、ＣＢ２Ｏ３はＢ２Ｏ３の含有量を示し、これらは耐火物中における質量％で表す。）
HIGH-ZIRCONIA ELECTRO-FUSED CAST REFRACTORY MATERIAL
Provided is a high-zirconia electro-fused cast refractory material which has a ZrO2 content of more than 95% by mass, rarely undergoes cracking during the production thereof, has excellent corrosion resistance to a molten glass, is less likely to produce zircon crystals even under heating of the refractory material alone or under heating of the refractory material while the refractory material being in contact with a molten glass, and can be produced in a large amount industrially. The high-zirconia electro-fused cast refractory material contains, as chemical components, ZrO2 in an amount of more than 95% by mass and 98% by mass or less, Al2O3 in an amount of 0.1 to 1.5% by mass, SiO2 in an amount of 1 to 2.5% by mass, K2O in an amount of 0 to 0.1% by mass, both of Na2O and K2O in a total amount of 0.01 to 0.3% by mass, B2O3 in an amount of 0.02 to 0.4% by mass, BaO in an amount of 0.01 to 0.6% by mass, SnO2 in an amount of 0.01 to 0.4% by mass, and both of Fe2O3 and TiO2 in a total amount of 0.3% by mass or less, in which the content of P2O5 is 0.04% by mass or less, and the contents of B2O3 and SnO2 satisfy the following formulae (1) and (2). 0.20≦(SnO2/B2O3)<6.5 ··· (1) 0.14% by mass ≦(CSnO2+CB2O3/2)≦0.55% by mass ··· (2) (In the formulae, CSnO2 represents the content of SnO2, and CB2O3 represents the content of B2O3, each of which is expressed in % by mass in the refractory material.)
L'invention concerne un matériau réfractaire coulé électrofondu à haute teneur en zircone qui a une teneur en ZrO2 supérieure à 95% en masse, qui subit rarement des fissures pendant sa production, qui a une excellente résistance à la corrosion par un verre fondu, qui est moins susceptible de produire des cristaux de zircon même en chauffant le matériau réfractaire seul ou en chauffant le matériau réfractaire alors que le matériau réfractaire est en contact avec un verre fondu, et qui peut être produit industriellement en grande quantité. Le matériau réfractaire coulé électrofondu à haute teneur en zircone contient, en tant que composants chimiques, du ZrO2 en une quantité supérieure à 95 % en masse et inférieure ou égale à 98 % en masse, de l'Al2O3 en une quantité allant de 0,1 à 1,5 % en masse, du SiO2 en une quantité allant de 1 à 2,5 % en masse, du K2O en une quantité allant de 0 à 0,1 % en masse, à la fois du Na2O et du K2O en une quantité totale allant de 0,01 à 0,3 % en masse, du B2O3 en une quantité allant de 0,02 à 0,4 % en masse, du BaO en une quantité allant de 0,01 à 0,6 % en masse, du SnO2 en une quantité allant de 0,01 à 0,4 % en masse, et à la fois du Fe2O3 et du TiO2 en une quantité totale de 0,3 % en masse ou moins, dans lequel la teneur en P2O5 est de 0,04 % en masse ou moins et les teneurs en B2O3 et SnO2 satisfont aux formules (1) et (2) suivantes. 0,20≦(SnO2/B2O3)<6,5 ··· (1) 0,14 % en masse ≦(CSnO2+CB2O3/2)≦0,55 % en masse ··· (2) (Dans les formules, CSnO2 représente la teneur en SnO2, et CB2O3 représente la teneur en B2O3, chacune d'entre elles étant exprimée en % en masse dans le matériau réfractaire.)
ＺｒＯ２が９５質量％を超える含有量であり、製造時の亀裂が少なく、溶融ガラスに対する耐食性に優れ、耐火物単体での加熱下又は溶融ガラスと接触した場合の加熱下でもジルコン結晶を生成しにくい、産業上量産が容易な高ジルコニア電気溶融鋳造耐火物を提供する。 化学成分として、ＺｒＯ２が９５質量％を超え９８質量％以下、Ａｌ２Ｏ３が０．１～１．５質量％、ＳｉＯ２が１～２．５質量％、Ｋ２Ｏが０～０．１質量％、且つ、Ｎａ２ＯとＫ２Ｏの合計が０．０１～０．３質量％、Ｂ２Ｏ３が０．０２～０．４質量％、ＢａＯが０．０１～０．６質量％、ＳｎＯ２が０．０１～０．４質量％、Ｆｅ２Ｏ３とＴｉＯ２の合計が０．３質量％以下、Ｐ２Ｏ５の含有量が０．０４質量％以下であり、Ｂ２Ｏ３及びＳｎＯ２の含有量が次の式（１）及び式（２）を満たす高ジルコニア電気溶融鋳造耐火物。 ０．２０≦（ＳｎＯ２／Ｂ２Ｏ３）＜６．５・・・（１） ０．１４質量％≦（ＣＳｎＯ２＋ＣＢ２Ｏ３／２）≦０．５５質量％ ・・・（２） （式中のＣＳｎＯ２はＳｎＯ２の含有量を、ＣＢ２Ｏ３はＢ２Ｏ３の含有量を示し、これらは耐火物中における質量％で表す。）
HIGH-ZIRCONIA ELECTRO-FUSED CAST REFRACTORY MATERIAL
MATÉRIAU RÉFRACTAIRE COULÉ ÉLECTROFONDU À HAUTE TENEUR EN ZIRCONE
高ジルコニア電気溶融鋳造耐火物
SUGIYAMA HIROSHI (Autor:in) / MISU YASUO (Autor:in) / HASHIMOTO ITARU (Autor:in)
02.06.2022
Patent
Elektronische Ressource
Japanisch