High-temperature, non-destructive evaluation of calcium aluminate-cement castables
Calcium aluminate castables made of Secar 71 or of synthetic CA mixed with submicrometer alumina and containing tabular alumina were investigated using non-destructive measurement of Young's modulus and synchrotron radiation-energy dispersive diffraction in the temperature range from 20 deg C to 1600 deg C. Both techniques appear to complement each other to follow and understand conversion and decomposition of hydrates, sintering phenomena, and high-temperature reactions.
High-temperature, non-destructive evaluation of calcium aluminate-cement castables
Calcium aluminate castables made of Secar 71 or of synthetic CA mixed with submicrometer alumina and containing tabular alumina were investigated using non-destructive measurement of Young's modulus and synchrotron radiation-energy dispersive diffraction in the temperature range from 20 deg C to 1600 deg C. Both techniques appear to complement each other to follow and understand conversion and decomposition of hydrates, sintering phenomena, and high-temperature reactions.
High-temperature, non-destructive evaluation of calcium aluminate-cement castables
Zerstörungsfreie Hochtemperaturauswertung von gießbarem Kalzium-Aluminat-Zement
Nonnet, E. (Autor:in) / Lequeux, N. (Autor:in) / Boch, P. (Autor:in)
2001
13 Seiten, 8 Bilder, 2 Tabellen, 29 Quellen
Aufsatz (Konferenz)
Englisch
High-Temperature, Non-Destructive Evaluation of Calcium Aluminate-Cement Castables
| British Library Conference Proceedings | 2001
Application of Calcium Aluminate Cement in Alumina-Spinel Castables
| British Library Conference Proceedings | 2001