Characteristics of bricks made from waste steel slag
The characteristics of bricks made from steel slag were investigated in this research. Slag addition was shown to reduce the required firing temperature. When the firing temperature was greater than 1050 degree C and the slag addition less than 10%, the bricks met ROC national standard CNS 3319 third-class brick for builders. The percentage of slag increased as the quartz and kaolin decreased in the sintered samples while the magnesium aluminum silicate and calcium silicate increased. There were no new crystal phases observed in these samples.
Characteristics of bricks made from waste steel slag
The characteristics of bricks made from steel slag were investigated in this research. Slag addition was shown to reduce the required firing temperature. When the firing temperature was greater than 1050 degree C and the slag addition less than 10%, the bricks met ROC national standard CNS 3319 third-class brick for builders. The percentage of slag increased as the quartz and kaolin decreased in the sintered samples while the magnesium aluminum silicate and calcium silicate increased. There were no new crystal phases observed in these samples.
Characteristics of bricks made from waste steel slag
Charaktereistische Merkmale von Ziegeln aus Stahlwerksschlacke
Shih, Pai-Haung (Autor:in) / Wu, Zong-Zheng (Autor:in) / Chiang, Hung-Lung (Autor:in)
Waste Management ; 24 ; 1043-1047
2004
5 Seiten, 10 Quellen
Aufsatz (Zeitschrift)
Englisch
Characteristics of acid resisting bricks made from quarry residues and waste steel slag
| British Library Online Contents | 2008
Characteristics of acid resisting bricks made from quarry residues and waste steel slag
| Online Contents | 2008