Frost resistance of cement mortars with different lime contents
Tests for the frost resistance were made on laboratory cements containing different amounts of belite activated by rapid clinker cooling. If freezing begins after the hydration of the belite these cements will offer better frost resistance than cements rich in alite. This is due to the lower portlandite content and the more dense microstructure of the cements containing a high amount of belite.
Frost resistance of cement mortars with different lime contents
Tests for the frost resistance were made on laboratory cements containing different amounts of belite activated by rapid clinker cooling. If freezing begins after the hydration of the belite these cements will offer better frost resistance than cements rich in alite. This is due to the lower portlandite content and the more dense microstructure of the cements containing a high amount of belite.
Frost resistance of cement mortars with different lime contents
Frostbeständigkeit von unterschiedlich kalkhaltigen Zementmörteln
Müller, A. (Autor:in) / Fuhr, C. (Autor:in) / Knöfel, D. (Autor:in)
Cement and Concrete Research ; 25 ; 809-818
1995
10 Seiten, 11 Bilder, 1 Tabelle, 5 Quellen
Aufsatz (Zeitschrift)
Englisch
Mörtel , Kalk , Wasser , Gehalt (Zusammensetzung) , chemische Reaktion , Porosität , mechanische Festigkeit , Aluminat , Ferrit (Oxidkeramik) , Berechnung , chemische Zusammensetzung , Mikrogefüge , Hydratisieren , Ferrit (Alpha-Mischkristall) , Berechnungsmethode , Alit , Belit , Silicat , Zementklinker , Frostbeständigkeit , Theorie-Experiment-Vergleich
Frost Resistance of Cement Mortars with Different Lime Contents
| Online Contents | 1995
Frost Resistance of Cement Mortars with Different Lime Contents
| British Library Online Contents | 1995
| NTIS | 1964
| Engineering Index Backfile | 1926
Hydrated lime and cement mortars
| Engineering Index Backfile | 1908