Utilization of Iron Tailings for High Strength Fired Brick
his paper studies the feasibility of preparation high strength fired bricks from iron tailings with addition of clay and coal gangue. The results indicated that the optimum conditions were found to be that the hematite tailings content were 35%–50%; the firing temperature was 1000 °C. Under these conditions, the mechanical strength, the water absorption and the bulk density of the fired bricks were 21.17–26.14 MPa, 14.55–15.47% and 1.648–1.629g/cm3, respectively, these were well conformed to standards MU20 of Chinese Fired Common Bricks Standard (GB/T5101-2003).The phase composition and microstructure of the fired specimen were characterized by XRD and SEM. The results showed that the major crystalline phases present in fired brick were quartz, albite, amphibole, hematite and muscovite, and glass phase encapsulated and cement the crystalline phases forming strong entirety which promoted the strength of bricks.
Utilization of Iron Tailings for High Strength Fired Brick
his paper studies the feasibility of preparation high strength fired bricks from iron tailings with addition of clay and coal gangue. The results indicated that the optimum conditions were found to be that the hematite tailings content were 35%–50%; the firing temperature was 1000 °C. Under these conditions, the mechanical strength, the water absorption and the bulk density of the fired bricks were 21.17–26.14 MPa, 14.55–15.47% and 1.648–1.629g/cm3, respectively, these were well conformed to standards MU20 of Chinese Fired Common Bricks Standard (GB/T5101-2003).The phase composition and microstructure of the fired specimen were characterized by XRD and SEM. The results showed that the major crystalline phases present in fired brick were quartz, albite, amphibole, hematite and muscovite, and glass phase encapsulated and cement the crystalline phases forming strong entirety which promoted the strength of bricks.
Utilization of Iron Tailings for High Strength Fired Brick
Advanced Materials Research ; 550-553 ; 2373-2377
26.07.2012
5 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Utilization of Iron Tailings for High Strength Fired Brick
| Tema Archiv | 2012
Environment-friendly high-parameter tailings non-fired and non-steamed brick
| Europäisches Patentamt | 2015
Process for producing high-strength sintered hollow brick by utilizing tailings
| Europäisches Patentamt | 2020
The Utilization of Coconut Fibre into Fired Clay Brick
| British Library Online Contents | 2016