PENAMBAHAN ABU DAUN BAMBU SEBAGAI SUBSTITUSI MATERIAL SEMEN TERHADAP KINERJA BETON
Bamboo leaf ash has reactive properties that can react to hard and stiff materials. Based on research, through burning for 2 hours bamboo leaf ash has 75.9% silica. Based on the background, the purpose of this study is to determine the effect of bamboo ash as a mixture of cement on the performance of concrete. The method used in this research is the experimental method. Experiments were carried out on normal concrete with K 240 concrete quality which the variation of bamboo leaf ash is 0%, 3%, 5%, and 7% from the cement mixture and compressive strength test with a sample of 3 cube-shaped specimens measuring 15 x 15 x 15 cm at the age of 14 days. The data analysis technique used is linear regression using SPSS software. The results show the compressive strength value which is influenced by the variation of the mixture of bamboo leaf ash is Y = 13.871 + 0.419 X where x is the variation of the mixture and y is the compressive strength value of concrete. The value of t-test = 2.504 > t-table = 1.812 indicates a significant influence between the addition of variations in the mixture of bamboo leaf ash to compressive strength. The optimum variation was found in the proportion of bamboo ash mixture of 5% and 7%. ; Abu daun bambu mempunyai sifat reaktif yang dapat bereaksi menjadi bahan keras dan kaku. Berdasarkan penelitian, melalui pembakaran selama 2 jam abu daun bambu memiliki silika 75.9 %. Berdasarkan latar belakang, tujuan penelitian ini yaitu mengetahui pengaruh abu daun bambu sebagai campuran semen terhadap kinerja beton. Metode yang digunakan dalam penelitian ini adalah metode eksperimen. Eksperiman dilakukan terhadap beton normal dengan mutu beton K 240 yang diberi abu daun bambu dengan variasi 0%, 3%, 5%, dan 7% dari campuran semen serta di uji kuat tekan dengan sampel 3 benda uji berbentuk kubus ukuran 15 x 15 x 15 cm pada umur 14 hari. Teknik analisa data yang digunakan adalah regresi linier dengan menggunakan software SPSS. Hasil menunjukkan nilai kuat tekan yang dipengaruhi oleh variasi campuran abu daun bambu adalah Y = 13.871 + 0.419 X dimana x adalah variasi campuran dan y adalah nilai kuat tekan beton. Nilai t-hitung = 2.504 > t-tabel = 1.812 mengindikasikan ada pengaruh yang signifikan antara penambahan variasi campuran abu daun bambu terhadap kuat tekan. Variasi optimum terdapat pada proporsi campuran abu daun bambu 5% dan 7%.
PENAMBAHAN ABU DAUN BAMBU SEBAGAI SUBSTITUSI MATERIAL SEMEN TERHADAP KINERJA BETON
Bamboo leaf ash has reactive properties that can react to hard and stiff materials. Based on research, through burning for 2 hours bamboo leaf ash has 75.9% silica. Based on the background, the purpose of this study is to determine the effect of bamboo ash as a mixture of cement on the performance of concrete. The method used in this research is the experimental method. Experiments were carried out on normal concrete with K 240 concrete quality which the variation of bamboo leaf ash is 0%, 3%, 5%, and 7% from the cement mixture and compressive strength test with a sample of 3 cube-shaped specimens measuring 15 x 15 x 15 cm at the age of 14 days. The data analysis technique used is linear regression using SPSS software. The results show the compressive strength value which is influenced by the variation of the mixture of bamboo leaf ash is Y = 13.871 + 0.419 X where x is the variation of the mixture and y is the compressive strength value of concrete. The value of t-test = 2.504 > t-table = 1.812 indicates a significant influence between the addition of variations in the mixture of bamboo leaf ash to compressive strength. The optimum variation was found in the proportion of bamboo ash mixture of 5% and 7%. ; Abu daun bambu mempunyai sifat reaktif yang dapat bereaksi menjadi bahan keras dan kaku. Berdasarkan penelitian, melalui pembakaran selama 2 jam abu daun bambu memiliki silika 75.9 %. Berdasarkan latar belakang, tujuan penelitian ini yaitu mengetahui pengaruh abu daun bambu sebagai campuran semen terhadap kinerja beton. Metode yang digunakan dalam penelitian ini adalah metode eksperimen. Eksperiman dilakukan terhadap beton normal dengan mutu beton K 240 yang diberi abu daun bambu dengan variasi 0%, 3%, 5%, dan 7% dari campuran semen serta di uji kuat tekan dengan sampel 3 benda uji berbentuk kubus ukuran 15 x 15 x 15 cm pada umur 14 hari. Teknik analisa data yang digunakan adalah regresi linier dengan menggunakan software SPSS. Hasil menunjukkan nilai kuat tekan yang dipengaruhi oleh variasi campuran abu daun bambu adalah Y = 13.871 + 0.419 X dimana x adalah variasi campuran dan y adalah nilai kuat tekan beton. Nilai t-hitung = 2.504 > t-tabel = 1.812 mengindikasikan ada pengaruh yang signifikan antara penambahan variasi campuran abu daun bambu terhadap kuat tekan. Variasi optimum terdapat pada proporsi campuran abu daun bambu 5% dan 7%.
PENAMBAHAN ABU DAUN BAMBU SEBAGAI SUBSTITUSI MATERIAL SEMEN TERHADAP KINERJA BETON
Nura Diana, Anita Intan (author) / Fansuri, Subaidillah (author) / Deshariyanto, Dwi (author)
2020-10-27
doi:10.22225/pd.9.2.1788.172-182
PADURAKSA: Jurnal Teknik Sipil Universitas Warmadewa; Vol. 9 No. 2 (2020); 172-182 ; 2581-2939 ; 2303-2693 ; 10.22225/pd.9.2
Article (Journal)
Electronic Resource
English
DDC:
690
ANALISIS KINERJA BETON NORMAL DAN BETON DENGAN SEMEN SUBSTITUSI BLAST FURNACE SLAG
| BASE | 2019