Kinetics of chalcopyrite galvanic leaching using sulfate media at the low temperature in the GalvanoxTM process
In this research work, the dissolution of chalcopyrite was investigated under atmospheric pressure, with sulfate media at low temperatures, in 30°C to 50°C. In the galvanic interaction between chalcopyrite and pyrite, pyrite is used as a leaching catalyst. Effects of different parameters such as temperature, stirring speed, pyrite to chalcopyrite ratio, particle size, and solution potential were examined. Results showed that maximum copper recovery in low temperature was achieved after 24 hours, under the following condition: stirring speed of 800 rpm, pyrite to chalcopyrite ratio 4, solution potential 440 mV, temperature 50°C, and particle size of -38 microns. In addition, kinetic studies indicated that chalcopyrite dissolution with pyrite followed the shrinking core model, and the reaction was controlled by the surface reaction. Activation energy (Ea) was calculated as 88 kJ/mol.
Kinetics of chalcopyrite galvanic leaching using sulfate media at the low temperature in the GalvanoxTM process
In this research work, the dissolution of chalcopyrite was investigated under atmospheric pressure, with sulfate media at low temperatures, in 30°C to 50°C. In the galvanic interaction between chalcopyrite and pyrite, pyrite is used as a leaching catalyst. Effects of different parameters such as temperature, stirring speed, pyrite to chalcopyrite ratio, particle size, and solution potential were examined. Results showed that maximum copper recovery in low temperature was achieved after 24 hours, under the following condition: stirring speed of 800 rpm, pyrite to chalcopyrite ratio 4, solution potential 440 mV, temperature 50°C, and particle size of -38 microns. In addition, kinetic studies indicated that chalcopyrite dissolution with pyrite followed the shrinking core model, and the reaction was controlled by the surface reaction. Activation energy (Ea) was calculated as 88 kJ/mol.
Kinetics of chalcopyrite galvanic leaching using sulfate media at the low temperature in the GalvanoxTM process
Soghra Salehi (author) / Mohammad Noaparast (author) / Seyed Ziaodin Shafaie (author)
2016
Article (Journal)
Electronic Resource
Unknown
Metadata by DOAJ is licensed under CC BY-SA 1.0
Leaching process and kinetics analysis for sulfidation roasted chalcopyrite
| British Library Online Contents | 2006
Kinetics of sulfuric acid leaching chalcopyrite by microwave heating
| British Library Online Contents | 2000
| Taylor & Francis Verlag | 2024
Chalcopyrite leaching at ambient temperature with oxidants and mechanism investigation
| British Library Online Contents | 2008