Causes of certain defects in cold rolling rolls
It is noted that rapid development of internal fatigue cracks originating in region of cold rolling work roll bore through action of alternating loads in presence of defects upon its surface, particularly longitudinal ones, leads to increased deformability of roll itself under load, to transformation of cross section into ellipse, to loss of capacity to reduce metal, etc; importance of checking condition of bore by ultrasonic or optical methods is indicated. (See also Stal n 5 May 1963 p 438-40)
Causes of certain defects in cold rolling rolls
It is noted that rapid development of internal fatigue cracks originating in region of cold rolling work roll bore through action of alternating loads in presence of defects upon its surface, particularly longitudinal ones, leads to increased deformability of roll itself under load, to transformation of cross section into ellipse, to loss of capacity to reduce metal, etc; importance of checking condition of bore by ultrasonic or optical methods is indicated. (See also Stal n 5 May 1963 p 438-40)
Causes of certain defects in cold rolling rolls
Prichiny nekotorykh defektov valkov kholodnoi prokatki
Gur'Ev, A.V. (author) / Gedberg, M.G. (author) / Terent'Ev, S.G. (author) / Shepel, L.T. (author)
1963
3 pages
Article (Journal)
English
© Metadata Copyright Elsevier B. V. All rights reserved.
Causes of certain defects in cold rolling rolls
| Engineering Index Backfile | 1963
Wear in cold rolling milling rolls: A methodological approach
| British Library Online Contents | 2019
Increasing strength of working rolls in cold rolling mill
| Engineering Index Backfile | 1967
| Engineering Index Backfile | 1958
Failure analysis of rolls of cold rolling mill in steel plant
| British Library Conference Proceedings | 1997