Strength development in magnesium oxysulfate cement
AbstractModulus of elasticity and microhardness measurements were made on magnesium oxysulfate systems (paste and compacted) having a wide range of porosity. Three sets of compacts were made; each set was made with particles having a different size range (5 to 150 μm; 150 to 300 μm; 300 to 600 μm). The log mechanical property versus porosity curves for paste samples were linear. The curves for compacted samples had a change in slope at 7.5 per cent porosity. At porosities less than 7.5 per cent, the data for paste and compacted samples were on the same curve. Tat higher porosities microhardness values for compacted samples were greater than those for paste samples; modulus of elasticity values were less. Compacted samples made with finest particles had higher values for mechanical properties at a given porosity. The mechanical behaviour of these systems was explained on the basis of the relative contribution of porosity, pore size distribution, interparticular bonds and strength of the solid phase.
RésuméDes mesures du module d'élasticité et de la microdureté ont été prises sur de l'oxysulfate de magnésium (en pâte et comprimé) ayant une porosité très variée. Trois ensembles de comprimés ont été fabriqués; chacun a été fait de trois séries de particules de grosseur différente (5 à 100 μm; 150 à 300 μm; 300 à 600 μm). Les courbes de propriété mécanique logarithmique et de porosité des échantillons en pâte étaient linéaires. Les courbes des échantillons comprimés avaient un changement d'inclinaison à 7.5 pour cent de porosité. A des porosités moindres que 7.5 pour cent les données des échantillons en pâte et comprimés se situaient sur la même courbe. Les valeurs de microdureté des échantillons comprimés à des porosités plus élevées étaient plus grandes que celles des échantillons en pâte; les valeurs du module d'élasticité étaient moindres. Les échantillons comprimés faits avec les particules les plus fines avaient des propriétés mécaniques de valeurs plus grandes à une porosité donnée. Le comportement mécanique de ces systémes a été expliqué en se fondant sur la contribution relative de la porosité, la distribution de la grosseur du pore, les liants entre les particule
Strength development in magnesium oxysulfate cement
AbstractModulus of elasticity and microhardness measurements were made on magnesium oxysulfate systems (paste and compacted) having a wide range of porosity. Three sets of compacts were made; each set was made with particles having a different size range (5 to 150 μm; 150 to 300 μm; 300 to 600 μm). The log mechanical property versus porosity curves for paste samples were linear. The curves for compacted samples had a change in slope at 7.5 per cent porosity. At porosities less than 7.5 per cent, the data for paste and compacted samples were on the same curve. Tat higher porosities microhardness values for compacted samples were greater than those for paste samples; modulus of elasticity values were less. Compacted samples made with finest particles had higher values for mechanical properties at a given porosity. The mechanical behaviour of these systems was explained on the basis of the relative contribution of porosity, pore size distribution, interparticular bonds and strength of the solid phase.
RésuméDes mesures du module d'élasticité et de la microdureté ont été prises sur de l'oxysulfate de magnésium (en pâte et comprimé) ayant une porosité très variée. Trois ensembles de comprimés ont été fabriqués; chacun a été fait de trois séries de particules de grosseur différente (5 à 100 μm; 150 à 300 μm; 300 à 600 μm). Les courbes de propriété mécanique logarithmique et de porosité des échantillons en pâte étaient linéaires. Les courbes des échantillons comprimés avaient un changement d'inclinaison à 7.5 pour cent de porosité. A des porosités moindres que 7.5 pour cent les données des échantillons en pâte et comprimés se situaient sur la même courbe. Les valeurs de microdureté des échantillons comprimés à des porosités plus élevées étaient plus grandes que celles des échantillons en pâte; les valeurs du module d'élasticité étaient moindres. Les échantillons comprimés faits avec les particules les plus fines avaient des propriétés mécaniques de valeurs plus grandes à une porosité donnée. Le comportement mécanique de ces systémes a été expliqué en se fondant sur la contribution relative de la porosité, la distribution de la grosseur du pore, les liants entre les particule
Strength development in magnesium oxysulfate cement
Beaudoin, J.J. (author) / Ramachandran, V.S. (author)
Cement and Concrete Research ; 8 ; 103-112
1977-11-02
10 pages
Article (Journal)
Electronic Resource
English
Preparation method of high-strength magnesium oxysulfate cement
| European Patent Office | 2023
Method for improving early strength of magnesium oxysulfate cement
European Patent Office | 2023