AbstractSulfate resistance of Portland-pozzolanic cements, prepared by gradual replacement of Portland cement by pozzolana, were studied in relation to their transverse strengths. Common clay and China clay, after calcination, were used as two different pozzolana. Strengths of samples, after curing separately in water and in 5% MgSO4 solution, were measured. On sulfate-curing the strength increased remarkably upto a maximum value beyond which it decreased. This was thought to be dependent on the mode of formation of ettringite in the set cement. Strength on water-curing was not much improved. This was due to the non-availability of lime by the reacting pozzolana because of slower rate of diffusion of lime from the hydrating cement.
ZusammenfassungDie Sulfat-Widerstandfähigkeit von Portland-Puzzolan Zementen (mit kalziniertem Ton und Kaolin) wurde hinsichtlich der Biegefestigkeit untersucht. Die Festigkeiten wurden nach getrennter Lagerung in Wasser und in 5%-iger MgSO4-Lösung gemessen. Nach der Sulfat-Lagerung nahm die Festigkeit bis zu einem Maximalwert zu, um dann wieder abzunehmen. Dieses Verhalten wird mit der Bildung von Ettringit im gebundenen Zement in Zusammenhang gebracht. Die Wasserlagerung verursachte keine wesentliche Verbesserung der Festigkeit. Dies wurde auf das Fehlen von Kalk infolge seiner langsameren Diffusionsgeschwindigkeit aus dem hydratierenden Zement zurückgeführt.
Sulfate resistance of portland-pozzolanic cements in relation to strength
AbstractSulfate resistance of Portland-pozzolanic cements, prepared by gradual replacement of Portland cement by pozzolana, were studied in relation to their transverse strengths. Common clay and China clay, after calcination, were used as two different pozzolana. Strengths of samples, after curing separately in water and in 5% MgSO4 solution, were measured. On sulfate-curing the strength increased remarkably upto a maximum value beyond which it decreased. This was thought to be dependent on the mode of formation of ettringite in the set cement. Strength on water-curing was not much improved. This was due to the non-availability of lime by the reacting pozzolana because of slower rate of diffusion of lime from the hydrating cement.
ZusammenfassungDie Sulfat-Widerstandfähigkeit von Portland-Puzzolan Zementen (mit kalziniertem Ton und Kaolin) wurde hinsichtlich der Biegefestigkeit untersucht. Die Festigkeiten wurden nach getrennter Lagerung in Wasser und in 5%-iger MgSO4-Lösung gemessen. Nach der Sulfat-Lagerung nahm die Festigkeit bis zu einem Maximalwert zu, um dann wieder abzunehmen. Dieses Verhalten wird mit der Bildung von Ettringit im gebundenen Zement in Zusammenhang gebracht. Die Wasserlagerung verursachte keine wesentliche Verbesserung der Festigkeit. Dies wurde auf das Fehlen von Kalk infolge seiner langsameren Diffusionsgeschwindigkeit aus dem hydratierenden Zement zurückgeführt.
Sulfate resistance of portland-pozzolanic cements in relation to strength
Samanta, C. (author) / Chatterjee, M.K. (author)
Cement and Concrete Research ; 12 ; 726-734
1982-05-03
9 pages
Article (Journal)
Electronic Resource
English
| Elsevier | 1994
Studies of sulfate resistance of Portland cements
| Engineering Index Backfile | 1941
| British Library Conference Proceedings | 1998
Sulfate resistance of calcined clay – Limestone – Portland cements
| Elsevier | 2018
Sulfate resistance of Portland cements, concretes and mortars
| Engineering Index Backfile | 1952