Development of silica fume-based geopolymer foams
Highlights Pastes of silica fume and sodium hydroxide expand with thermal treatment. Sodium hydroxide solution concentration and oven temperatures affect porosity. Pore formation is due to silanol condensation and subsequent water vapor loss. Foams with ~85 kg/m3 bulk density and 0.04 W/mK thermal conductivity can be made.
Abstract Thermal insulation materials are critical for reducing the energy consumption and carbon emissions associated with buildings. A good insulation material must not only have low density and sufficient mechanical properties but also resist high temperatures and fires. In addition, its production process must be simple and inexpensive. This study describes the production of very low density (>85 kg/m3) inorganic foams with high porosity (<94%). Silica fume and NaOH solutions are mixed to prepare a geopolymer paste that is cured in a laboratory oven at 60–100 °C, and expanded in a furnace at ~ 200–500 °C. The expansion mechanism and pore structures of the foams, as well as their physical, mechanical, and thermal properties were investigated with microscopy, spectroscopy, and measurement of compressive strength and thermal conductivity. Foaming of cured geopolymer pastes is due to loss of water vapor resulting from the condensation of silanol groups. Porosity increases and bulk density decreases with increasing NaOH concentration and higher furnace temperatures. The foams have 0.15–0.75 MPa compressive strength, and 0.04–0.10 W/mK thermal conductivity. Addition of 1–2% chopped basalt fibers increases strength of the low-density foams ~ 3–6 times while only doubling their densities. Microscopy reveals that the foams are made of irregular-shaped, fragmented cells, µm to mm in size.
Development of silica fume-based geopolymer foams
Highlights Pastes of silica fume and sodium hydroxide expand with thermal treatment. Sodium hydroxide solution concentration and oven temperatures affect porosity. Pore formation is due to silanol condensation and subsequent water vapor loss. Foams with ~85 kg/m3 bulk density and 0.04 W/mK thermal conductivity can be made.
Abstract Thermal insulation materials are critical for reducing the energy consumption and carbon emissions associated with buildings. A good insulation material must not only have low density and sufficient mechanical properties but also resist high temperatures and fires. In addition, its production process must be simple and inexpensive. This study describes the production of very low density (>85 kg/m3) inorganic foams with high porosity (<94%). Silica fume and NaOH solutions are mixed to prepare a geopolymer paste that is cured in a laboratory oven at 60–100 °C, and expanded in a furnace at ~ 200–500 °C. The expansion mechanism and pore structures of the foams, as well as their physical, mechanical, and thermal properties were investigated with microscopy, spectroscopy, and measurement of compressive strength and thermal conductivity. Foaming of cured geopolymer pastes is due to loss of water vapor resulting from the condensation of silanol groups. Porosity increases and bulk density decreases with increasing NaOH concentration and higher furnace temperatures. The foams have 0.15–0.75 MPa compressive strength, and 0.04–0.10 W/mK thermal conductivity. Addition of 1–2% chopped basalt fibers increases strength of the low-density foams ~ 3–6 times while only doubling their densities. Microscopy reveals that the foams are made of irregular-shaped, fragmented cells, µm to mm in size.
Development of silica fume-based geopolymer foams
Shakouri, Sahra (author) / Bayer, Özgür (author) / Erdoğan, Sinan T. (author)
2020-07-31
Article (Journal)
Electronic Resource
English
| European Patent Office | 2021
Geopolymer synthesis using silica fume and sodium aluminate
| British Library Online Contents | 2007
Method for manufacturing coal-based geopolymer foam including silica fume
| European Patent Office | 2024
METHOD FOR MANUFACTURING COAL-BASED GEOPOLYMER FOAM INCLUDING SILICA FUME
| European Patent Office | 2023
Method for manufacturing coal-based geopolymer foam including silica fume
| European Patent Office | 2024