Preparation method for submicron zirconia-toughened aluminium oxide powder and ceramic thereof
The invention discloses a preparation method for a submicron zirconia-toughened aluminium oxide powder and a ceramic thereof. The preparation method is characterized by comprising the following steps: (1) mixing industrial aluminium hydroxide, zirconium oxychloride, a composite mineralizer and a stabilizer for 1-2 hours; (2) heating to 1350-1500 DEG C at a heating speed of 3-5 DEG C and carrying out a calcining treatment for 2-8 hours to obtain ZTA powder; (3) mixing the ZTA powder, a dispersant and water and carrying out wet-method ball-milling, and carrying out spray-drying, thereby obtaining a submicron ZTA powder with the powder grain size D50 of 0.2-0.8mum. The obtained submicron ZTA powder is shaped into a ceramic biscuit, and the ceramic biscuit is sintered at a high temperature of 1500-1650 DEG C for 2-5 hours, so as to obtain a submicron ZTA ceramic with the relative density of 97-99%. The method is low in cost, simple in technique process, and convenient for realization of industrial production; the powder is small in raw crystalline grain size, narrow in distribution, and capable of being applied to the field of high-technology ceramics.
Preparation method for submicron zirconia-toughened aluminium oxide powder and ceramic thereof
The invention discloses a preparation method for a submicron zirconia-toughened aluminium oxide powder and a ceramic thereof. The preparation method is characterized by comprising the following steps: (1) mixing industrial aluminium hydroxide, zirconium oxychloride, a composite mineralizer and a stabilizer for 1-2 hours; (2) heating to 1350-1500 DEG C at a heating speed of 3-5 DEG C and carrying out a calcining treatment for 2-8 hours to obtain ZTA powder; (3) mixing the ZTA powder, a dispersant and water and carrying out wet-method ball-milling, and carrying out spray-drying, thereby obtaining a submicron ZTA powder with the powder grain size D50 of 0.2-0.8mum. The obtained submicron ZTA powder is shaped into a ceramic biscuit, and the ceramic biscuit is sintered at a high temperature of 1500-1650 DEG C for 2-5 hours, so as to obtain a submicron ZTA ceramic with the relative density of 97-99%. The method is low in cost, simple in technique process, and convenient for realization of industrial production; the powder is small in raw crystalline grain size, narrow in distribution, and capable of being applied to the field of high-technology ceramics.
Preparation method for submicron zirconia-toughened aluminium oxide powder and ceramic thereof
XU JIE (author) / CAO YULIANG (author) / XU HUA (author)
2015-09-16
Patent
Electronic Resource
English
IPC:
C04B
Kalk
,
LIME
European Patent Office | 2024
|TITANIUM NITRIDE-REINFORCED ZIRCONIA TOUGHENED ALUMINA CERAMIC POWDER AND PREPARATION METHOD THEREOF
European Patent Office | 2020
|Titanium nitride-reinforced zirconia toughened alumina ceramic powder and preparation method thereof
European Patent Office | 2022
|Whisker toughened zirconia ceramic and preparation method thereof
European Patent Office | 2021
|Submicron spherical zirconium oxide powder, preparation method thereof and zirconium oxide ceramic
European Patent Office | 2023
|