Temperature-stable low-dielectric-constant microwave dielectric ceramic CaLi3Nd3W2O13
The invention discloses a high-quality-factor temperature-stable low-dielectric-constant microwave dielectric ceramic CaLi3Nd3W2O13 and a preparation method thereof. The method comprises the following steps: (1) CaCO3, Li2CO3, Nd2O3 and WO3 original powders with purities higher than 99.9% (weight percentage) are weighed and blended according to the composition of CaLi3Nd3W2O13; (2) the raw material obtained in the step (1) is subjected to wet ball milling for 12h, wherein a ball milling medium is distilled water; after drying, the material is pre-sintered for 6h under a temperature of 720 DEG C in an air atmosphere; and (3) a binding agent is added to the powder obtained in the step (2), granulation and compression molding are carried out; and sintering is carried out for 4h under a temperature of 770-820 DEG C in an air atmosphere. The binding agent is a polyvinyl alcohol solution with a mass concentration of 5%, wherein the addition amount of polyvinyl alcohol accounts for 3% of the total mass of the powder. The ceramic provided by the invention can be well sintered under a temperature below 820 DEG C. The dielectric constant of the ceramic reaches 23.1-23.8, and the quality factor Qf of the ceramic reaches 123000-161000GHz. The ceramic has a low resonance frequency temperature coefficient, and has high application value in industrial application.
Temperature-stable low-dielectric-constant microwave dielectric ceramic CaLi3Nd3W2O13
The invention discloses a high-quality-factor temperature-stable low-dielectric-constant microwave dielectric ceramic CaLi3Nd3W2O13 and a preparation method thereof. The method comprises the following steps: (1) CaCO3, Li2CO3, Nd2O3 and WO3 original powders with purities higher than 99.9% (weight percentage) are weighed and blended according to the composition of CaLi3Nd3W2O13; (2) the raw material obtained in the step (1) is subjected to wet ball milling for 12h, wherein a ball milling medium is distilled water; after drying, the material is pre-sintered for 6h under a temperature of 720 DEG C in an air atmosphere; and (3) a binding agent is added to the powder obtained in the step (2), granulation and compression molding are carried out; and sintering is carried out for 4h under a temperature of 770-820 DEG C in an air atmosphere. The binding agent is a polyvinyl alcohol solution with a mass concentration of 5%, wherein the addition amount of polyvinyl alcohol accounts for 3% of the total mass of the powder. The ceramic provided by the invention can be well sintered under a temperature below 820 DEG C. The dielectric constant of the ceramic reaches 23.1-23.8, and the quality factor Qf of the ceramic reaches 123000-161000GHz. The ceramic has a low resonance frequency temperature coefficient, and has high application value in industrial application.
Temperature-stable low-dielectric-constant microwave dielectric ceramic CaLi3Nd3W2O13
LI CHUNCHUN (author) / TANG YING (author) / WANG DAN (author)
2015-09-16
Patent
Electronic Resource
English
IPC:
C04B
Kalk
,
LIME
Temperature-stable low-dielectric constant microwave dielectric ceramic CaLaV3O10
| European Patent Office | 2015
Temperature-stable medium-dielectric-constant microwave dielectric ceramic BaLi2LaVO6
| European Patent Office | 2016
Temperature-stable low-dielectric-constant microwave dielectric ceramic Bi3Nb9WO30
| European Patent Office | 2015
Temperature stable low dielectric constant microwave dielectric ceramic LiBaLa2V3O12
| European Patent Office | 2016
Temperature stable ultralow dielectric constant microwave dielectric ceramic LiZnYbV2O8
| European Patent Office | 2016