Method for manufacturing atomized flow guide pipe
The invention provides a method for manufacturing an atomized flow guide pipe. The method includes the following steps that 1, zirconcia and cerium oxide are added to a ball mill to be fully and evenly mixed and are screened, then, a binding agent is added, and the mixture is added into a mixer to be evenly mixed; 2, powder mixed in the step 1 is pressed into blocks through a hydraulic machine, placed into an oven to be dried and then placed in a high-temperature kiln to be baked to 800 DEG C to 1,000 DEG C, the temperature is kept for 1.5 hours to 3 hours, the kiln is stopped, and the powder is delivered out of the kiln after being naturally cooled to the normal temperature; and 3, after the products delivered out of the kiln are subjected to breaking and iron removing, mixed powder with the grain diameter being 100 nm to 200 nm is obtained through screening, the binding agent is added and mixed, the powder is dry-pressed through an upper pressing machine after being placed for 6 hours to 8 hours, water is removed, the powder is placed in an electric kiln to be baked to 1,600 DEG C to 1,700 DEG C, heat is preserved for 5 hours to 8 hours, the powder is delivered out of the electric kiln after being naturally cooled, and the flow guide pipe is obtained. The funnel-shaped flow guide pipe made of zirconium oxide and used for an atomizer is produced through a hydraulic dry-pressing method, and production efficiency is improved while raw materials are saved.
Method for manufacturing atomized flow guide pipe
The invention provides a method for manufacturing an atomized flow guide pipe. The method includes the following steps that 1, zirconcia and cerium oxide are added to a ball mill to be fully and evenly mixed and are screened, then, a binding agent is added, and the mixture is added into a mixer to be evenly mixed; 2, powder mixed in the step 1 is pressed into blocks through a hydraulic machine, placed into an oven to be dried and then placed in a high-temperature kiln to be baked to 800 DEG C to 1,000 DEG C, the temperature is kept for 1.5 hours to 3 hours, the kiln is stopped, and the powder is delivered out of the kiln after being naturally cooled to the normal temperature; and 3, after the products delivered out of the kiln are subjected to breaking and iron removing, mixed powder with the grain diameter being 100 nm to 200 nm is obtained through screening, the binding agent is added and mixed, the powder is dry-pressed through an upper pressing machine after being placed for 6 hours to 8 hours, water is removed, the powder is placed in an electric kiln to be baked to 1,600 DEG C to 1,700 DEG C, heat is preserved for 5 hours to 8 hours, the powder is delivered out of the electric kiln after being naturally cooled, and the flow guide pipe is obtained. The funnel-shaped flow guide pipe made of zirconium oxide and used for an atomizer is produced through a hydraulic dry-pressing method, and production efficiency is improved while raw materials are saved.
Method for manufacturing atomized flow guide pipe
WU GUOQING (author)
2015-11-18
Patent
Electronic Resource
English
| European Patent Office | 2023
Simulation of the Atomized Flow in Hydroelectric Engineering
| British Library Conference Proceedings | 2001
Flow guide pipe for vacuum ingot casting and preparation method of flow guide pipe
| European Patent Office | 2023
Liquid-liquid Atomized Jet-flow Characteristics and Particle Diameter Distribution
| British Library Online Contents | 2007
| European Patent Office | 2024